Prediction method of incubation period for centrally cracked tensile specimens considering the effects of thickness and crack depth

A technology of central crack and tensile specimen, which is applied in the direction of measuring device, strength characteristics, testing material strength by applying stable tension/compression, etc., to achieve the effect of simplifying the incubation period prediction step

Active Publication Date: 2021-05-18
TIANJIN UNIV
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the application of this prediction model involves a large number of complex calculation processes and has a certain degree of conservatism, and there are certain limitations for the application of actual components.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Prediction method of incubation period for centrally cracked tensile specimens considering the effects of thickness and crack depth
  • Prediction method of incubation period for centrally cracked tensile specimens considering the effects of thickness and crack depth
  • Prediction method of incubation period for centrally cracked tensile specimens considering the effects of thickness and crack depth

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0019] The present invention will be described in further detail below in conjunction with the accompanying drawings and specific embodiments. It should be understood that the specific embodiments described here are only used to explain the present invention, not to limit the present invention. In this embodiment, P92 high-temperature heat-resistant steel is selected.

[0020] The incubation period prediction method of the central crack tensile specimen considering thickness and crack depth influence of the present invention comprises the following steps:

[0021] S1: Establish a creep incubation period prediction model for a central crack tensile specimen, the model includes a central crack tensile specimen body 1 with a cuboid structure, and upper and lower holes 2 and lower holes are symmetrically arranged at the upper and lower ends of the specimen body. Hole 3; insert a prefabricated crack 4 in the middle of the symmetrical plane of the sample body, and apply a constant ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for predicting the incubation period of a central crack tensile specimen considering the influence of thickness and depth. The central crack tensile specimen model is used to calculate and extract the incubation period, and a large amount of simulated data is used to fit the formula to propose a central Prediction of incubation period in cracked tensile specimens. The invention has the beneficial effects of simplifying the steps of predicting the incubation period of a central crack tensile sample.

Description

technical field [0001] The present invention relates to the evaluation of the incubation period prediction engineering criticality of the central crack tensile specimen (MT) considering the influence of thickness and crack depth. Incubation period of tensile specimens. Background technique [0002] Components and equipment serving in high-temperature environments will inevitably have various defects during production and service. The initiation and propagation of creep cracks is a major failure mechanism of high-temperature components containing defects and leads to failure before the design life. The incubation period of creep cracks occupies a large proportion in the service life of high-temperature components. In order to ensure the reliability of components serving in high-temperature environments, the research on the incubation period of creep cracks becomes more and more important. Creep initiation is defined as the time when microcracks (or pores) first connect to f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information