Preparation method of soft line-suction microfiber leather without thickness loss

A microfiber leather and soft technology, applied in the field of leather, can solve the problems of poor softness of the finished product, superfiber absorbing pattern, hard hand feeling, stiff hand feeling, etc., and achieve the effect of fast texture change, soft hand feeling and short development cycle

CN110130118APending Publication Date: 2019-08-16ZHEJIANG HEXIN NEW MATERIAL CO LTD
12 Cites 2 Cited by

Patent Information

Authority / Receiving Office
CN · China
Patent Type
Applications(China)
Current Assignee / Owner
Publication Date
2019-08-16
Patent Text Reader

Abstract

The invention discloses a preparation method of soft line-suction microfiber leather without thickness loss. The preparation method comprises following steps: S1, base fabric is subjected to softeningtreatment; S2, dry surface making is performed, and microfiber leather is obtained; S3, printing treatment is performed, and a printing layer is obtained; S4, a line-suction process is adopted, a vacuum line suction machine is utilized for sucking lines, a heating hood passes through two heating areas, the first heating area is used for heating a main body, the second heating area is used for supplementing heat, and cooling is performed; the soft line-suction microfiber leather without thickness loss is obtained. The thickness of the line-suction microfiber leather prepared with the method ofthe soft line-suction microfiber leather without thickness loss is increased by about 0.05 mm; the product which is 1.0 mm-1.5 mm touches soft and full; the lines are natural and are copied from genuine leather directly, a line-suction roller is made, the lines are transferred to the surface of the product by the line-suction roller, and the lines have a short development cycle and change fast compared with release paper.
Need to check novelty before this filing date? Find Prior Art

Description

technical field

[0001] The invention relates to the field of leather, in particular to a method for preparing thick and soft microfiber leather with absorbing patterns. Background technique

[0002] There are different definitions of microfiber, also known as microfiber, fine denier fiber, ultrafine fiber, and the English name microfiber. Generally, fibers with a denier of 0.3 denier (5 microns in diameter) are called superfine fibers. Due to the extremely fineness of ultra-fine fibers, the stiffness of the silk is greatly reduced, and the fabric feels extremely soft. The fine fibers can also increase the layered structure of the silk, increase the specific surface area and capillary effect, and make the internal reflection of the fiber more delicate on the surface. , so that it has a silky elegant luster, and has good moisture absorption and moisture dissipation. Microfibers are a class of high-tech new fibers developed in modern times, among which sea-island microfibers ...

Examples

Embodiment 1

[0061] A kind of preparation method of thick and soft absorb grain microfiber leather comprises the following steps:

[0062] S1. Softening of base fabric

[0063] S11. Send the superfine fiber nonwoven fabric (microfiber BASE, also known as superfiber base cloth) into the impregnation tank, and impregnate it with the impregnation slurry;

[0064] S12, then carry out cold rolling by rolling mill, during cold rolling, the roll pressure of this rolling mill is 2~8 Kg / cm , and roll speed is 8~15m / min;

[0065] S13, then perform infrared pre-drying, then dry and cool to obtain the base cloth;

[0066] S2. Dry noodles

[0067] S21. Prepare the surface layer slurry, and coat the prepared surface layer slurry on the release paper, the coating thickness is 0.2-0.3mm, and then control the temperature of the oven to dry at 60-150°C, and cool. form a surface layer;

[0068] S22. Prepare the middle layer slurry, apply the prepared middle layer slurry on the surface layer, the coating ...

Embodiment 2

[0091] A kind of preparation method of thick and soft absorb grain microfiber leather comprises the following steps:

[0092] S1. Softening of base fabric

[0093] S11. Send the superfine fiber nonwoven fabric (microfiber BASE, also known as superfiber base cloth) into the impregnation tank, and impregnate it with the impregnation slurry;

[0094] S12, carry out cold rolling by rolling mill then, during cold rolling, the roll pressure of this rolling mill is 2Kg / cm , and roll speed is 15m / min;

[0095] S13, then perform infrared pre-drying, then dry and cool to obtain the base cloth;

[0096] S2. Dry noodles

[0097] S21. Prepare the surface layer slurry, and coat the prepared surface layer slurry on the release paper with a coating thickness of 0.3mm, then control the temperature of the oven to dry at 60-150°C, and cool to form the surface Floor;

[0098]S22. Prepare the middle layer slurry, apply the prepared middle layer slurry on the surface layer, the coating thicknes...

Embodiment 3

[0122] A kind of preparation method of thick and soft absorb grain microfiber leather comprises the following steps:

[0123] S1. Softening of base fabric

[0124] S11. Send the superfine fiber nonwoven fabric (microfiber BASE, also known as superfiber base cloth) into the impregnation tank, and impregnate it with the impregnation slurry;

[0125] S12, carry out cold rolling by rolling mill then, during cold rolling, the roll pressure of this rolling mill is 8 Kg / cm , and roll speed is 8m / min;

[0126] S13, then perform infrared pre-drying, then dry and cool to obtain the base cloth;

[0127] S2. Dry noodles

[0128] S21. Prepare the surface layer slurry, and coat the prepared surface layer slurry on the release paper with a coating thickness of 0.2mm, then control the temperature of the oven to dry at 60-150°C, and cool to form the surface Floor;

[0129] S22. Prepare the middle layer slurry, apply the prepared middle layer slurry on the surface layer, the coating thickne...