A pipeline steel with excellent toughness for extremely low temperature environment at -45°C and its manufacturing method
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A manufacturing method and pipeline steel technology, which is applied in the field of pipeline steel and its manufacturing, can solve the problems of high production cost and achieve the effects of alleviating stress concentration and excellent low-temperature toughness
Active Publication Date: 2021-03-12
BAOSHAN IRON & STEEL CO LTD
View PDF13 Cites 1 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0004] Chinese patent CN106480381A discloses a hot-rolled wide and thick plate with good plasticity and toughness for low-temperature pipelines. This patent adopts the composition design of low Ni (0.06-0.15%) and Mo-containing composition design, the production cost is high, and its DWTT performance is only Satisfy the requirement of -20℃
The technical solution disclosed in this patent is designed with low Ni (0.21-0.35%) and high Nb (0.05-0.08%) composition, the structure is quasi-polygonal ferrite + granular bainite, and its DWTT performance only meets the requirements of -25°C
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0047] In the following, the ultra-low temperature pipeline steel and its manufacturing method according to the present invention will be further explained and described in conjunction with the accompanying drawings and specific examples. However, such explanations and descriptions do not constitute undue limitations on the technical solution of the present invention.
[0048] Table 1 shows the mass percentages of chemical elements in the pipeline steels of the examples of the present invention, Table 2 shows the process parameters of the pipeline steels of the examples of the present invention, and Table 3 shows the properties of the pipeline steels of the examples of the present invention.
[0049] It can be seen from Table 3 that the yield strength Rt0.5≥450MPa, the tensile strength Rm≥535MPa, and the elongation A 50.8 ≥18%, -45°C Charpy impact energy AKV≥250J, -45°C DWTT fracture shear area ratio SA%≥85%, which can meet the toughness requirements of -45°C extremely low temp...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
particle size
aaaaa
aaaaa
yield strength
aaaaa
aaaaa
tensile strength
aaaaa
aaaaa
Login to view more
Abstract
The invention discloses pipeline steel with excellent toughness for a minus 45 DEG C extremely-low-temperature environment and a manufacturing method thereof. The steel comprises, in percentage by mass, the following chemical elements of 0.030%-0.060% of C, 0.10%-0.30% of Si, 1.30%-1.60% of Mn, less than or equal to 0.0100% of P, less than or equal to 0.0015% of S, 0.40%-0.55% of Ni, 0.05%-0.20% of Cr, 0.050%-0.075% of Nb, 0.008%-0.020% of Ti, 0.0010%-0.0040% of Ca, 0.010%-0.050% of Al, less than or equal to 0.005% of B, 0.0010%-0.0060% of N, less than or equal to 0.0050% of O, and the balanceFe and inevitable impurities, wherein the elements simultaneously meet the following relationship that the Ni is larger than or equal to 1.6*(C+Mn / 6), log (C*Nb) is less than or equal to minus 2.5, Cplus Mn / 6 plus Cr / 5 is larger than or equal to 0.28% and is less than or equal to 0.35%, and Ti / N is larger than or equal to 2.5 and is less than or equal to 5.0. The yield strength of the pipeline steel is larger than or equal to 450 MPa, the tensile strength is larger than or equal to 535 MPa, the elongation rate is larger than or equal to 18%, the Charpy impact power AKV at minus 45 DEG C is larger than or equal to 250J, and the shear area rate Sa% of a DWTT fracture at minus 45 DEG C is larger than or equal to 85%.
Description
technical field [0001] The invention relates to a pipeline steel and a manufacturing method thereof, in particular to a pipeline steel with excellent toughness for an extremely low temperature environment of -45°C and a manufacturing method thereof. Background technique [0002] Oil and natural gas will still account for the main part of the primary energy consumption in the future, and the demand will continue to rise, and the mining area will gradually expand. The service temperature can be as low as -45°C. Although modern controlled rolling and controlled cooling technology has been able to obtain pipeline steel with both strength and toughness, it is still difficult to meet the low temperature toughness requirements of -45°C. Therefore, pipeline steel with extremely low temperature toughness has considerable application prospects. [0003] The low-temperature toughness of pipeline steel usually refers to Charpy impact performance (CVN) and drop weight tear performance (...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.