Celadon-Jianzhan porcelain combined firing process for porcelain

A kind of celadon and craftsmanship technology, which is applied in the production of drinking vessels, clay products, ceramic materials, etc., can solve the problems of not finding porcelain, difficult to combine, etc., and achieve the effect of good flammability, stable color, and no impurities

Active Publication Date: 2020-02-21
南平市建阳区兰亭叙建盏陶瓷有限公司
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Porcelain is extremely difficult to combine due to the limitation of blank, glaze composition and firing process. At present, there is no porcelain made by combining celadon and Jianzhan process.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Celadon-Jianzhan porcelain combined firing process for porcelain
  • Celadon-Jianzhan porcelain combined firing process for porcelain
  • Celadon-Jianzhan porcelain combined firing process for porcelain

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] The porcelain firing process combining celadon and Jianzhan includes the following steps:

[0041] (1) Prepare green body raw materials, Jianzhan glaze slurry, celadon glaze slurry, wherein,

[0042] The green body raw material is prepared by the following method: mixing 7 parts by weight of kaolin, 1 part by weight of field mud and 3 parts by weight of red mud, crushing, elutriating, grinding, passing through a 90-mesh sieve, press filtration, mud refining, After aging for one year, the raw material of the green body is obtained;

[0043] The Jianzhan glaze slurry is prepared by the following method: mix 5 parts by weight of glaze ore, 3 parts by weight of plant ash, 2 parts by weight of field mud, and 0.3 parts by weight of iron red, add 3.5 times by weight of water and put it into a ball mill Grind and pass through a 90-mesh sieve to obtain Jianzhan glaze slurry;

[0044] The celadon glaze slurry is prepared by the following method: take 65 parts by weight of ridge...

Embodiment 2

[0062] The porcelain firing process combining celadon and Jianzhan includes the following steps:

[0063] (1) Prepare green body raw materials, Jianzhan glaze slurry, celadon glaze slurry, wherein,

[0064] The green body raw material is prepared by the following method: mixing 6 parts by weight of kaolin, 2 parts by weight of field mud and 4 parts by weight of red mud, crushing, elutriating, grinding, passing through a 80-mesh sieve, press filtration, mud refining, After aging for one year, the raw material of the green body is obtained;

[0065] The Jianzhan glaze slurry is prepared by the following method: mix 4 parts by weight of glaze ore, 3 parts by weight of plant ash, 2 parts by weight of field mud, and 0.3 parts by weight of iron red, add 3 times the weight of water and put it into a ball mill Grind and pass through an 80-mesh sieve to obtain Jianzhan glaze slurry;

[0066] The celadon glaze slurry is prepared by the following method: take 70 parts by weight of ridg...

Embodiment 3

[0082] The porcelain firing process combining celadon and Jianzhan includes the following steps:

[0083] (1) Prepare green body raw materials, Jianzhan glaze slurry, celadon glaze slurry, wherein,

[0084] The green body raw material is prepared by the following method: mixing 8 parts by weight of kaolin, 1 part by weight of field mud and 2 parts by weight of red mud, crushing, elutriating, grinding, passing through a 100-mesh sieve, pressure filtration, mud refining, After aging for one year, the raw material of the green body is obtained;

[0085] The Jianzhan glaze slurry is prepared by the following method: mix 6 parts by weight of glaze ore, 3.5 parts by weight of plant ash, 3 parts by weight of field mud, and 0.2 parts by weight of iron red, add 3 times by weight of water and put it into a ball mill Grind and pass through a 100-mesh sieve to obtain Jianzhan glaze slurry;

[0086] The celadon glaze slurry is prepared by the following method: take 60 parts by weight of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
depthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a celadon-Jianzhan porcelain combined firing process for porcelain. The process comprises the following steps: preparing a green body raw material, Jianzhan glaze slip and celadon glaze slip; subjecting the green body raw material to throwing so as to form a cup shape, conducting green body trimming, engraving a pattern outside a cup body, and carrying out biscuiting and cooling to obtain a green body; conducting glazing; and putting the glazed and air-dried green body into an electric kiln for roasting, stopping the electric kiln, carrying out natural cooling, and drawing a produced cup out of the electric kiln. According to the invention, Longquan celadon and Jianzhan porcelain firing processes are combined, the interior and the mouth edge of the fired porcelain cup are Jianzhan porcelain glaze surfaces, and the exterior of the cup is a celadon glaze surface with a carved pattern; and a combination of celadon and Jianzhan porcelain breaks the constraint of traditional porcelain types, presents strong visual impact and artistic aesthetic feeling, and is of milestone significance in the field of porcelain.

Description

technical field [0001] The invention relates to the technical field of porcelain, in particular to a porcelain firing process combining celadon and Jianzhan. Background technique [0002] Jianzhan is a representative of black porcelain, one of the eight famous porcelains in the Song Dynasty in China, and was used by the royal family in the Song Dynasty. In the middle and late Yuan Dynasty, with the chaos of war and changes in social fashion, Jianyao Jianzhan tended to decline, and in the following hundreds of years, the firing skills of Jianyao Jianzhan were on the verge of being lost. After the reform and opening up, the 800-year-old Jianzhan firing technique has been restored and developed. [0003] Celadon is a traditional porcelain treasure of the Han nationality in China, among which Longquan celadon is well-known. People describe Longquan celadon as "quality like jade, bright as mirror, and sound like chime". Longquan celadon has the advantages of fine and tough text...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/24C04B33/04C04B33/132C04B33/34C03C8/00A47G19/22
CPCC04B33/04C04B33/1321C04B33/1322C04B33/24C04B33/34C03C8/00A47G19/2205Y02P40/60
Inventor 李光熙
Owner 南平市建阳区兰亭叙建盏陶瓷有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com