Black anti-aging glass fiber reinforced plastic composite material

A composite material and anti-aging technology, which is applied in the field of FRP materials, can solve problems such as affecting use, low surface strength, and accelerating aging speed, and achieve the effects of improving production efficiency, protecting polymers, and slowing down aging speed

Inactive Publication Date: 2020-03-24
河北华强科技开发有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] FRP is a composite material, which is composed of two or more materials to form another material that can meet people's requirements. It is widely used in engineering construction, automobiles a

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0014] Example 1

[0015] A black ageing resistant glass fiber reinforced plastic composite material, which is characterized in that it includes material components and parts by weight: 50 parts of polyester resin, 20 parts of glass fiber, 11 parts of filler, 5 parts of light stabilizer, 2 parts of accelerator, and curing 6 parts of agent and 22 parts of black color paste; The filler includes 3 parts of calcium powder, 5 parts of glass beads, and 3 parts of aluminum hydroxide; The accelerator is cyclohexanone peroxide; the curing agent is alicyclic amine The light stabilizer is a light shielding agent; the use temperature of the accelerator is 25-30°; the glass fiber is an alkali-free fiber, and the monofilament diameter of the alkali-free fiber is 13-20 microns.

Example Embodiment

[0016] Example 2

[0017] A black aging-resistant glass fiber reinforced plastic composite material, characterized in that: a black aging-resistant glass fiber reinforced plastic composite material, characterized in that it includes material components and parts by weight: 55 parts of polyester resin, 25 parts of glass fiber, and 16 parts of filler , 7 parts of light stabilizer, 4 parts of accelerator, 10 parts of curing agent and 30 parts of black color paste; The filler includes 5 parts of calcium powder, 7 parts of glass beads and 4 parts of aluminum hydroxide; The accelerator is over Cyclohexanone oxide; the curing agent is alicyclic amine; the light stabilizer is a light shielding agent; the use temperature of the accelerator is 25-30°; the glass fiber is an alkali-free fiber, the alkali-free fiber The monofilament diameter is 13-20 microns.

Example Embodiment

[0018] Example 3

[0019] A black aging-resistant glass fiber reinforced plastic composite material, characterized in that: a black aging-resistant glass fiber reinforced plastic composite material, characterized in that it includes material components and parts by weight: 60 parts of polyester resin, 27 parts of glass fiber, and 20 parts of filler , 8 parts of light stabilizer, 5 parts of accelerator, 11 parts of curing agent and 22 parts of black color paste; The filler includes 8 parts of calcium powder, 9 parts of glass beads and 3 parts of aluminum hydroxide; The accelerator is over Dibenzoyl oxide; the curing agent is an aromatic amine; the light stabilizer is a light shielding agent; the use temperature of the accelerator is 25-30°; the glass fiber is an alkali-free fiber, the alkali-free The fiber monofilament diameter is 13-20 microns.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Monofilament diameteraaaaaaaaaa
Diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of glass fiber reinforced plastic materials, in particular to a black anti-aging glass fiber reinforced plastic composite material. The material comprisesthe following components by weight: 50-60 parts of polyester resin, 20-30 parts of glass fiber, 10-23 parts of filler, 5-8 parts of a light stabilizer, 2-6 parts of an accelerant, 5-15 parts of a curing agent and 20-35 parts of a black color paste. The filler comprises 3-9 parts of calcium powder, 5-10 parts of glass beads and 3-4 parts of aluminum hydroxide; and the accelerant is any one of cyclohexanone peroxide, methyl ethyl ketone peroxide or dibenzoyl peroxide. The invention provides the black anti-aging glass fiber reinforced plastic composite material, under the condition of long-time illumination, the aging speed can be slowed down, the service life is prolonged, and meanwhile, through raw material collocation, the surface hardness is also greatly improved.

Description

technical field [0001] The invention relates to the technical field of FRP materials, in particular to a black aging-resistant FRP composite material. Background technique [0002] FRP is a composite material, which is composed of two or more materials to form another material that can meet people's requirements. It is widely used in engineering construction, automobiles and mechanical parts. However, the current FRP material After being exposed to light, the aging speed is accelerated, and the strength of the surface itself is low, which affects the use in actual life. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a black anti-aging FRP composite material for the above-mentioned technical deficiencies, which can slow down the aging speed and improve the service life under long-term light conditions. Hardness has also been greatly improved. [0004] In order to solve the above-mentioned technical problems, th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L67/00C08K13/04C08K7/14C08K3/26C08K7/20C08K3/22C08K3/04C08K5/14C08K5/17C08K5/18C08K5/00C08K3/014
CPCC08K3/04C08K3/22C08K3/26C08K5/005C08K5/14C08K5/17C08K5/18C08K7/14C08K7/20C08K13/04C08K2003/2227C08K2201/003C08L2201/08C08K3/014C08L67/00
Inventor 夏云广王洪君王帅王超郑春荣仉宁许博文仉媛媛仉儒张文宁
Owner 河北华强科技开发有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap