Oil-soluble corrosion inhibitor for gas well tubing and preparation method thereof

An oil-soluble corrosion inhibitor and oil pipe technology, which is used in gas well oil pipe and equipment protection, petroleum and petrochemical fields, can solve the problems affecting the stability of corrosion inhibitor and anti-corrosion effect, etc., and achieves good flat spreadability, good compatibility, flat surface Good spreading effect

Active Publication Date: 2022-01-04
西安三维科技发展有限责任公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The invention provides an oil-soluble corrosion inhibitor for gas well tubing and its preparation method, which is used to solve the problem that the existing imidazoline corrosion inhibitors cause the ring opening of imidazolines under long-term storage, thereby affecting the stability and anticorrosion effect of the corrosion inhibitors. question

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Oil-soluble corrosion inhibitor for gas well tubing and preparation method thereof
  • Oil-soluble corrosion inhibitor for gas well tubing and preparation method thereof
  • Oil-soluble corrosion inhibitor for gas well tubing and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Embodiment 1 of the present invention provides an oil-soluble corrosion inhibitor for gas well tubing. According to the mass fraction, its raw material is composed of 25% of the main agent and 75% of the compound, wherein the main agent is imidazoline Schiff base, and the compound The compound is based on the total mass of the oil-soluble corrosion inhibitor for gas well tubing, and the compound is composed of 10% benzotriazole, 7% hydroxyethyl thiosuccinic acid, and 58% solvent naphtha 200#.

[0032] Specifically, the preparation method of an oil-soluble corrosion inhibitor for gas well tubing comprises the following steps:

[0033] (1) Aspartic acid and diethylenetriamine are added into the reaction kettle according to the molar ratio of 1:1.2 for reaction, and water-carrying agent xylene is added at the same time, wherein the xylene water-carrying agent is oil for gas well tubing 10% of the total mass of the soluble corrosion inhibitor, heating and stirring to 150-16...

Embodiment 2

[0045] Embodiment 2 of the present invention provides an oil-soluble corrosion inhibitor for gas well tubing. According to the mass fraction, its raw material is composed of 20% of the main agent and 80% of the compound, wherein the main agent is imidazoline Schiff base, and the compound The compound is based on the total mass of the oil-soluble corrosion inhibitor for gas well tubing, and the compound is composed of 15% aromatic azole, 10% hydroxyethyl thiosuccinic acid and 55% solvent.

[0046] Wherein, the aromatic azole is selected from mercaptobenzothiazole, and the solvent is selected from solvent naphtha 100#.

[0047] Specifically, the preparation method of an oil-soluble corrosion inhibitor for gas well tubing comprises the following steps:

[0048] (1) Aspartic acid and triethylenetetramine are added to the reaction kettle according to the molar ratio of 1:1.5 to react, and xylene water-carrying agent is added at the same time, wherein the water-carrying agent xylene...

Embodiment 3

[0060] Embodiment 3 of the present invention provides an oil-soluble corrosion inhibitor for gas well tubing. According to the mass fraction, its raw materials are composed of 20% of the main agent and 80% of the compound, wherein the main agent is imidazoline Schiff base, and the compound The compound is based on the total mass of the oil-soluble corrosion inhibitor for gas well tubing, and the compound is composed of 10% aromatic azole, 5% hydroxyethyl thiosuccinic acid and 65% solvent.

[0061] Wherein, the aromatic azole is selected to be methyl benzotriazole, and the solvent is selected mineral spirits 100#.

[0062] Specifically, the preparation method of an oil-soluble corrosion inhibitor for gas well tubing comprises the following steps:

[0063] (1) Aspartic acid and tetraethylenepentamine are added to the reaction kettle according to the molar ratio of 1:1.5 to react, and xylene water-carrying agent is added at the same time, wherein the water-carrying agent xylene i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an oil-soluble corrosion inhibitor for gas well tubing and a preparation method thereof, which is used to solve the problem that the existing imidazoline corrosion inhibitors cause imidazoline ring opening under long-term storage, thereby affecting the stability and anticorrosion effect of the corrosion inhibitors The problem. According to the mass fraction, its raw materials are composed of 20-30% main agent and 70-80% compound, wherein the main agent is imidazoline Schiff base, and the compound is the total mass of oil-soluble corrosion inhibitor for gas well tubing Calculated, the compound is composed of 10-15% aromatic azole, 5-10% hydroxyethyl thiosuccinic acid, and 45-65% solvent. The corrosion inhibitor obtained in the present invention is suitable for gas well tubing with low water content, can be quickly adsorbed on the inner wall of the pipeline, and can be adsorbed in the gas well tubing to form a dense corrosion inhibitor protective film. 2 Carbon steel pipelines and equipment in the gas well environment have a good protection effect. It has the characteristics of good planar spreadability and good compatibility with diesel oil, crude oil and condensate oil.

Description

technical field [0001] The invention relates to the technical field of gas well tubing and equipment protection in the petroleum and petrochemical field, and more specifically relates to an oil-soluble corrosion inhibitor for gas well tubing and a preparation method thereof. Background technique [0002] To effectively control corrosion in sulfur-containing environments, it is an economical and effective measure to apply corrosion inhibitor technology while making reasonable material selection. The use of corrosion inhibitors is an important method of corrosion protection at home and abroad, and the specific corrosion inhibition treatment process is determined according to the characteristics of the gathering and transportation system itself. [0003] At present, the industrial corrosion inhibitors used at home and abroad are basically adsorption corrosion inhibitors, such as Mannich bases, imidazoline derivatives, pyridine and quinoline quaternary ammonium salts, acetylenic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23F11/10C23F11/14
CPCC23F11/10C23F11/149C09K8/54C09K2208/32
Inventor 张磊贺华镭苟利鹏杨金峰张进科陈岑李欢吴阳李乐徐磊丁平平
Owner 西安三维科技发展有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com