Shielding type plastic film and composite belt prepared therefrom

A plastic film and shielding technology, which is applied in the fields of magnetic field/electric field shielding, synthetic resin layered products, electrical components, etc., can solve the problem of poor adhesion between plastic film and sheath or metal, inconsistent functions, and low electrical conductivity, etc. question

Pending Publication Date: 2020-05-15
JIANGSU KEMAITE TECH DEV CO LTD
View PDF10 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the film has a certain degree of adhesion to the aluminum layer and the outer layer is a semiconductive layer, the conductivity of the inner layer and the middle layer is not high, that is, the components and functions of the inner, middle and outer layers of the film are inconsiste

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Shielding type plastic film and composite belt prepared therefrom
  • Shielding type plastic film and composite belt prepared therefrom
  • Shielding type plastic film and composite belt prepared therefrom

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0066] Example 1

[0067] A composite tape is provided with a shielding type plastic film layer on one side of the metal layer, wherein the metal layer is an aluminum foil, and the preparation method of the composite tape comprises the following steps:

[0068] 1) Wet ball milling of metal oxides to remove Fe 2 O 3 The mass ratio of NiO and NiO is 1.08:2.35, the total mass of metal oxides and absolute ethanol is 2:1 by mass, and the total mass of grinding balls and metal oxides is weighed according to mass ratio of 13:1.1, and then the weighed grinding balls are weighed. Put into the grinding jar, then add Fe 2 O 3 , NiO and absolute ethanol, and finally ball milled at a speed of 200r / min for 10h.

[0069] 2) Screening the metal oxide, after drying the metal oxide obtained in step 1) in an oven at 110° C. for 4 hours, it is screened with a 250-mesh gauze.

[0070] 3) Surface treatment of hollow glass beads, the surface treatment liquid and hollow glass beads are weighed a...

Example Embodiment

[0081] Example 2

[0082] A composite tape is provided with a shielding type plastic film layer on one side of the metal layer, wherein the metal layer is an aluminum foil, and the preparation method of the composite tape comprises the following steps:

[0083] 1) Wet ball milling of metal oxides to remove Fe 2 O 3 The mass ratio of NiO and NiO is 1.08:2.35, the total mass of metal oxides and absolute ethanol is 2:1 by mass, and the total mass of grinding balls and metal oxides is weighed according to mass ratio of 13:1.1, and then the weighed grinding balls are weighed. Put into the grinding jar, then add Fe 2 O 3 , NiO and absolute ethanol, and finally ball milled at a speed of 200r / min for 10h.

[0084] 2) Screening the metal oxide, after drying the metal oxide obtained in step 1) in an oven at 110° C. for 4 hours, it is screened with a 250-mesh gauze.

[0085] 3) Surface treatment of hollow glass beads, the surface treatment liquid and hollow glass beads are weighed a...

Example Embodiment

[0096] Example 3

[0097] A composite tape is provided with a shielding type plastic film layer on one side of the metal layer, wherein the metal layer is an aluminum foil, and the preparation method of the composite tape comprises the following steps:

[0098] 1) Wet ball milling of metal oxides to remove Fe 2 O 3 The mass ratio of NiO and NiO is 1.08:2.35, the total mass of metal oxides and absolute ethanol is 2:1 by mass, and the total mass of grinding balls and metal oxides is weighed according to mass ratio of 13:1.1, and then the weighed grinding balls are weighed. Put into the grinding jar, then add Fe 2 O 3 , NiO and absolute ethanol, and finally ball milled at a speed of 200r / min for 10h.

[0099] 2) Screening the metal oxide, after drying the metal oxide obtained in step 1) in an oven at 110° C. for 4 hours, it is screened with a 250-mesh gauze.

[0100] 3) Surface treatment of hollow glass beads, the surface treatment liquid and hollow glass beads are weighed acc...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Volume resistanceaaaaaaaaaa
Shielding effectivenessaaaaaaaaaa
Volume resistivityaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the field of shielding materials, and relates to a shielding type plastic film and a composite belt prepared therefrom. The composite belt comprises a metal layer and a shielding type plastic film layer at least arranged on one side of the metal layer. The shielding type plastic film layer comprises the following components in parts by weight: 55-69 parts of EVA, 10-15 parts of PE-g-MAH, 8-12 parts of C5 petroleum resin, 13-18 parts of SBS, 10-15 parts of a self-made conductive filler, 3-5 parts of a lubricant, 0.5-1 part of an antioxidant and 0.3-0.5 part of an anti-copper agent. The shielding type plastic film layer has an excellent conductive shielding performance, the composite belt prepared by from the film has the adhesion of a conventional composite belt, when the composite belt longitudinally wraps or wraps a cable core, the overlapping positions can be bonded together in a hot mode, the composite belt can be bonded with a sheath, reliable damp-proof and protective effects are provided for the cable, and the two sides of the composite belt both have a shielding effect.

Description

technical field [0001] The invention belongs to the field of shielding materials, and relates to a shielding plastic film and a composite tape prepared therefrom. Background technique [0002] In order to meet the requirements of moisture-proof, shielding and protection of wires and cables, people will use metal-plastic composite tapes in wires and cables. Usually, the metal-plastic composite tape is made by covering the surface of the plastic film with a metal layer or covering the surface of the metal foil with a plastic film, which not only has a certain tensile strength, but also plays a shielding role. However, the plastic film is insulating and non-conductive. If an insulating plastic film is attached to one or both sides of the metal, the composite tape will form a winding current when wrapping the cable, which affects the electromagnetic shielding effect to a certain extent. . In order to solve the problem of the flow around the metal-plastic composite tape and imp...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/08C08L51/06C08L57/02C08L53/02C08K9/10C08K7/28C08K3/08C08J5/18H05K9/00B32B15/20B32B27/30B32B27/32B32B27/20B32B27/18B32B15/082B32B15/085B32B33/00
CPCC08J5/18H05K9/0098B32B15/20B32B27/306B32B27/32B32B27/20B32B27/18B32B15/082B32B15/085B32B33/00C08J2323/08C08J2451/06C08J2457/02C08J2453/02C08K9/10C08K7/28C08K2003/0806C08K2003/0856C08K2003/0862C08K2201/001B32B2307/202B32B2307/212
Inventor 虞家桢
Owner JIANGSU KEMAITE TECH DEV CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap