A kind of preparation method of conductive silver paste based on silver-coated graphite conductive agent

A technology of conductive silver paste and conductive agent, which is used in conductive materials, conductive materials, cable/conductor manufacturing, etc., can solve the problems of difficult to guarantee the uniformity of conduction, difficult to control the thickness of the silver-plated layer, and difficult to cover uniformly with silver. The effect of improving electron conductivity, low density, and reducing the amount of silver used

Active Publication Date: 2020-12-15
ZHEJIANG UNIV
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, carbon materials are usually hydrophobic, and the affinity between silver and carbon is poor. It is difficult to achieve uniform coverage of silver on the surface of carbon particles by simple electroless plating, and it is difficult to control the thickness of the silver plating layer, and it is difficult to ensure the uniformity of conductivity.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Embodiment 1: preparation of sodium polysulfide solution

[0032] Dissolve 0.1 mol of anhydrous sodium sulfide in 200 ml of tetrahydrofuran to obtain a sodium sulfide solution, add 0.3 mol of sulfur, stir and react for 24 hours, and filter to obtain Na 2 S 4 solution.

Embodiment 2

[0033] Embodiment 2: Acetylene black adsorption sodium polysulfide

[0034]Dissolve 0.1 mol of anhydrous sodium sulfide in 200 ml of tetrahydrofuran to obtain a sodium sulfide solution, add 0.5 mol of sulfur, stir and react for 24 hours, and filter to obtain Na 2 S 6 solution.

[0035] Take the above Na 2 S 6 Solution 100mL, add 10g of commercially available acetylene black, ultrasonic treatment for 10min, ultrasonic frequency 40kHz, impregnation for 2h; make acetylene black saturated and adsorb sodium polysulfide, filter and dry to get Na 2 S 6 Modified acetylene black.

Embodiment 3

[0036] Example 3: Conductive carbon material super P adsorbs sodium polysulfide

[0037] Dissolve 0.1 mol of anhydrous sodium sulfide in 200 ml of tetrahydrofuran to obtain a sodium sulfide solution, add 0.7 mol of sulfur, stir and react for 24 hours, and filter to obtain Na 2 S 8 solution.

[0038] Take the above Na 2 S 8 Solution 100mL, add 20g commercial conductive carbon material super P, ultrasonic treatment 20min, ultrasonic frequency 40kHz, impregnation 6h; make conductive carbon material super P saturated adsorption sodium polysulfide, filter and dry to get Na 2 S 8 Modify super P.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a conductive material synthesis technology, and aims to provide a preparation method of conductive silver paste based on a silver-coated graphite conductive agent. The preparation method comprises the following steps: adding a carbon conductive agent into a sodium polysulfide solution, carrying out supersonic vibration and then, carrying out dipping, filtering and drying to obtain a sodium polysulfide modified carbon material; dispersing the sodium polysulfide modified carbon material in a silver ammonia solution, and stirring for reaction to obtain a silver sulfide loaded carbon material; adding NaCl to reduce silver sulfide into metal silver, and carrying out filtering, washing and drying to obtain a silver-loaded carbon material; adding pyrrole into a cyclodextrin solution, and carrying out ultrasonic treatment to obtain a pyrrole cyclodextrin inclusion compound solution; dropwise adding hydrogen peroxide, then adding the silver-loaded carbon material, and uniformly stirring, and heating to remove water to obtain the conductive silver paste. The silver-loaded carbon material obtained by the invention has the characteristics of low density and low silverconsumption, but maintaining the same conductivity. The use amount of silver can be effectively reduced, the cost is reduced, and the maximum exertion of the electrical conductivity and the thermal conductivity of the silver is facilitated by using the least silver.

Description

technical field [0001] The invention relates to a synthesis technology of conductive materials, more specifically, relates to a new type of conductive agent and a preparation method thereof which uses silver-coated nano-graphite to reduce the contact resistance between graphite conductors and reduce the cost of conductive silver paste. Background technique [0002] Printed circuit boards, solar cell panels, and anti-radiation coatings all require highly conductive materials as the main components of conductive paste. Silver powder has good corrosion resistance and high conductivity and is widely used, such as PET-based membrane switch and low-temperature silver paste for flexible circuit boards, paste for single-board ceramic capacitors, silver paste for varistors and thermistors, Silver paste for piezoelectric ceramics, silver electrode paste for carbon film potentiometer, etc. Silver powder is classified according to particle size, the average particle size <0.1μm (100...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01B1/02H01B1/04H01B1/12H01B13/00
CPCH01B1/02H01B1/04H01B1/127H01B13/00
Inventor 刘宾虹李洲鹏
Owner ZHEJIANG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products