Thermoplastic polypropylene cable insulating material and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A cable insulation and polypropylene technology is applied in the field of thermoplastic polypropylene cable insulation material and its preparation.
Pending Publication Date: 2020-08-14
江苏瑞文新材料科技有限公司
View PDF3 Cites 2 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
Polypropylene material has a high melting point and excellent electrical insulation properties. However, polypropylene is brittle at room temperature, which makes it difficult to use as a cable insulation material (He Jinliang, Peng Lin, Zhou Yao. Research progress on environmentally friendly high-voltage DC cable insulation materials [J]. High Voltage Technology, 2017,043(002):337-343.)
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0023] (1) Add 25 parts of LDPE and 25 parts of LLDPE into the torque rheometer, raise the temperature to 120°C, stir at 40rpm for 30min, keep the temperature at 120°C during stirring, and obtain the mixed material;
[0024] (2) Raise the temperature of the torque rheometer to 150°C, add 50 parts of pp to the mixed material in step (1), stir at 40 rpm for 30 minutes, keep the temperature at 150°C during stirring, and obtain thermoplasticity after stirring Polypropylene cable insulation.
Embodiment 2
[0026] (1) Add 22 parts of LDPE and 22 parts of LLDPE into the torque rheometer, raise the temperature to 120°C, stir at 40rpm for 30min, keep the temperature at 120°C during stirring, and obtain the mixed material;
[0027] (2) Raise the temperature of the torque rheometer to 150°C, add 56 parts of pp to the mixed material in step (1), stir at 40 rpm for 30 minutes, keep the temperature at 150°C during stirring, and obtain thermoplasticity after stirring Polypropylene cable insulation.
Embodiment 3
[0029] (1) Add 20 parts of LDPE and 20 parts of LLDPE into the torque rheometer, raise the temperature to 120°C, stir at 40rpm for 30min, keep the temperature at 120°C during stirring, and obtain the mixed material;
[0030] (2) Raise the temperature of the torque rheometer to 150°C, add 60 parts of pp to the mixed material in step (1), stir at 40 rpm for 30 minutes, keep the temperature at 150°C during stirring, and obtain thermoplasticity after stirring Polypropylene cable insulation.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
density
aaaaa
aaaaa
melt flow index
aaaaa
aaaaa
density
aaaaa
aaaaa
Login to view more
Abstract
The invention relates to the technical field of insulating materials, in particular to a thermoplastic polypropylene cable insulating material and a preparation method thereof. The thermoplastic polypropylene material has high brittleness at room temperature so that the material is difficult to use as a cable insulating material; to solve this problem, the invention provides the thermoplastic polypropylene cable insulation material comprising, by weight, 50-60 parts of PP, 20-25 parts of LDPE and 20-25 parts of LLDPE. According to the invention, two polyethylene materials which are the LDPE and the LLDPE are added into a polypropylene matrix, so that the room-temperature brittleness of the polypropylene insulating material can be greatly improved, the application range of the polypropylenecable insulating material is greatly expanded, and the polypropylene cable insulating material has a good development prospect.
Description
technical field [0001] The invention relates to the technical field of insulating materials, in particular to a thermoplastic polypropylene cable insulating material and a preparation method thereof. Background technique [0002] At present, the most commonly used insulation material for DC plastic cables is cross-linked polyethylene. This material not only maintains the good electrical insulation properties of polyethylene, but also enhances the heat resistance of polyethylene. The cross-linking process also makes the ethylene molecules form a chain structure Transformed into a network structure, the mechanical properties of polyethylene at high temperatures have been greatly improved. However, the cross-linking process makes polyethylene change from a thermoplastic material to a thermosetting material, so it cannot be directly recycled after the cable life expires, and it does not have the characteristics of green environmental protection, and a large amount of waste XLPE ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.