Sanitary ceramic glaze with colorful effect, preparation method thereof and sanitary ceramic

A technology for sanitary ceramics and glaze, applied in the field of sanitary ceramics, can solve the problems of difficulty in applying sanitary ceramics, low glaze hardness, easy scratching, etc., and achieve the effects of improving decorative function, reasonable formula and prolonging service life.

Pending Publication Date: 2020-11-13
景德镇乐华陶瓷洁具有限公司
View PDF11 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, crystal glaze generally has low glaze hardness and is easy

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Sanitary ceramic glaze with colorful effect, preparation method thereof and sanitary ceramic
  • Sanitary ceramic glaze with colorful effect, preparation method thereof and sanitary ceramic
  • Sanitary ceramic glaze with colorful effect, preparation method thereof and sanitary ceramic

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0059] Example 1

[0060] This embodiment provides a sanitary ceramic glaze with dazzling color effect, the formula of which is:

[0061] Quartz 27%, potash feldspar 23.5%, dolomite 0.5%, kaolin 3.5%, zinc oxide 4%, alumina 10.5%, zirconium silicate 11%, wollastonite 19.5%, methyl cellulose 0.5%.

[0062] Its chemical composition is:

[0063] SiO 2 51%, Al 2 O 3 8.9%, Fe 2 O 3 0.5%, TiO 2 0.3%, CaO 12.6%, MgO 0.3%, K 2 O3.7%, Na 2 O 0.9%, ZnO4.9%, ZrO 2 7.1%, LOI 9.8%.

Example Embodiment

[0064] Example 2

[0065] This embodiment provides a sanitary ceramic glaze with dazzling color effect, the formula of which is:

[0066] Quartz 25%, potash feldspar 27%, dolomite 0.5%, kaolin 3.5%, zinc oxide 3.5%, alumina 9.5%, zirconium silicate 10%, wollastonite 20.5%, methylcellulose 0.5%.

[0067] Its chemical composition is:

[0068] SiO 2 49.3%, Al 2 O 3 8.3%, Fe 2 O 3 0.6%, TiO 2 0.4%, CaO 15.7%, MgO 0.2%, K 2 O3.2%, Na 2 O 1.8%, ZnO 4.7%, ZrO 2 5.5%, LOI 10.3%.

Example Embodiment

[0069] Example 3

[0070] This embodiment provides a sanitary ceramic glaze with dazzling color effect, the formula of which is:

[0071] Quartz 25%, potash feldspar 23.5%, dolomite 0.6%, kaolin 3.8%, zinc oxide 3.6%, alumina 11%, zirconium silicate 9%, wollastonite 23%, methyl cellulose 0.5%.

[0072] Its chemical composition is:

[0073] SiO 2 46.4%, Al 2 O 3 9.5%, Fe 2 O 3 0.5%, TiO 2 0.1%, CaO 16.7%, MgO 0.5%, K 2 O3.8%, Na 2 O 1.1%, ZnO 4.5%, ZrO 2 5.2%, LOI 11.7%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Fluidityaaaaaaaaaa
Vickers hardnessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a sanitary ceramic glaze with a colorful effect. The sanitary ceramic glaze mainly comprises the following raw materials in percentage by weight: 16%-28% of quartz, 18%-27% ofpotassium feldspar, 0.4%-0.8% of dolomite, 3%-4% of kaolin, 3.2%-4.2% of zinc oxide, 9%-11% of aluminum oxide, 9.5%-11.5% of zirconium silicate and 15%-30% of wollastonite. Correspondingly, the invention further discloses a preparation method of the sanitary ceramic glaze with a colorful effect, and a sanitary ceramic. The Vickers hardness of the sanitary ceramic glaze surface can be effectively improved, and meanwhile, the glaze surface has a colorful flashing effect under the irradiation of lamplight and has an outstanding decorative function.

Description

technical field [0001] The invention relates to the technical field of sanitary ceramic glazes, in particular to a sanitary ceramic glaze with colorful effects, a preparation method thereof, and sanitary ceramics. Background technique [0002] The glazed surface of existing sanitary ceramics is mainly based on bright glazed surface, and the decorative effect is relatively poor. At the same time, the existing sanitary ceramic glazes have relatively low hardness, are easily scratched during use, and are difficult to clean after scratches and dirt are absorbed. [0003] On the other hand, in the field of glazes, a common glaze is crystalline glaze, which adds 15-20% crystallization agents to the glaze, and after high-temperature melting, these crystallization agents can form a supersaturated melt. During the cooling process, crystals with a particle size of more than 10 μm are precipitated to achieve the purpose of decoration. Common crystallization agents such as zinc oxide,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C03C8/00C03C1/04C04B33/13C04B41/86C04B33/34
CPCC03C8/00C03C1/04C04B33/131C04B41/86C04B41/5022C04B41/009C04B33/34C04B2235/3418C04B2235/3427C04B2235/963C04B41/4543
Inventor 仝元东汪志良唐小勇吴小兵许凡陈拥强
Owner 景德镇乐华陶瓷洁具有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap