A thermotropic flame-retardant anti-melt droplet aromatic liquid crystal copolyester and preparation method thereof

An aromatic and copolyester technology, applied in the direction of liquid crystal materials, chemical instruments and methods, etc., can solve the problems of increased production costs, expensive liquid crystal polyarylate monomers, etc., and achieve simple preparation process, excellent flame retardancy and anti-dripping Performance, the effect of reducing loss of life and property

Active Publication Date: 2021-08-17
上海航永光电新材料有限公司
View PDF14 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

On the other hand, if the main chain of liquid crystal polyarylate is a rigid linear structure, it needs to be melted at a higher temperature (above 300°C) before it can be formed, and the monomer of liquid crystal polyarylate is relatively expensive, which will further increase the production capacity. cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A thermotropic flame-retardant anti-melt droplet aromatic liquid crystal copolyester and preparation method thereof
  • A thermotropic flame-retardant anti-melt droplet aromatic liquid crystal copolyester and preparation method thereof
  • A thermotropic flame-retardant anti-melt droplet aromatic liquid crystal copolyester and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] The thermotropic flame retardant and droplet resistant aromatic liquid crystal copolyester of this embodiment has the following chemical structural formula:

[0047]

[0048] Wherein, n=2~20, m=90~100;

[0049]Add 4,4'-dihydroxybiphenyl, terephthalic acid, 2,6-naphthalene dicarboxylic acid, terephthalic acid, and Hydroxybenzoic acid, PET particles, N-(3-carboxyphenyl)-4-phenylethynylphthalimide and N-(3-hydroxyphenyl)-4-phenylethynylphthalimide Imide; 150 ml of acetic anhydride was added, with 0.1 wt % potassium acetate as catalyst; the flask was equipped with a sealed glass paddle stirrer, a nitrogen inlet tube and an insulated distillation head. Nitrogen flow was introduced, and the reaction mixture was acetylated at 120°C for 30 minutes in a quicksand bath, and then the temperature was raised to 340°C at a rate of 1.5°C / min for 1 hour of transesterification. At this point, the reaction system was slowly evacuated to a vacuum degree of 1 mbar and the temperature ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
thermal decomposition temperatureaaaaaaaaaa
Login to View More

Abstract

The invention discloses a thermotropic flame-retardant and anti-droplet aromatic liquid crystal copolyester and a preparation method thereof. The end-blocking group is phenylacetylene or norbornene acetylene group, and the mesogenic group is composed of all aromatic diphenol monomers, all aromatic diacid monomers, and carboxyl-terminated A and hydroxyl-terminated B at the same time. It is composed of AB type fully aromatic monomers. The aromatic liquid crystal copolyester of the present invention has lower melting processing temperature and flame retardant and anti-dripping properties, and can effectively reduce the loss of life and property caused by fire, so it has broad application prospects in the fields of civil textiles and high-temperature protective materials. In addition, the molecular weight is controllable during the polymerization process, the preparation process is more convenient, efficient, and environmentally friendly, and no harmful gas will be generated during combustion.

Description

technical field [0001] The invention relates to the field of polymer materials, in particular to a thermotropic flame-retardant and droplet-resistant aromatic liquid crystal copolyester and a preparation method thereof. Background technique [0002] As a widely used high polymer material, semi-aromatic polyester has been widely used in civil and industrial fields due to its high strength, high modulus, and low water absorption characteristics. Polyester fiber, also known as polyester, occupies most of the chemical fiber industry. The types of polyesters that have been marketed include PET, PBT, PTT and so on. Because the polymer will undergo reactions such as oxidation and degradation at high temperatures, once it is burned, it is easy to form a fire, which will seriously affect the safety of people's lives and properties. Therefore, it is of great significance to improve the flame retardancy of polyester materials. [0003] The more mature polyester flame retardant modif...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G63/685C09K19/38
CPCC08G63/6856C09K19/3809
Inventor 陈导刘萍
Owner 上海航永光电新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More