Processing technology of melt-blown non-woven fabric

A melt-blown non-woven fabric and processing technology, which is applied in the direction of non-woven fabrics, textiles and papermaking, and the melting of filament raw materials, can solve the problems of reducing heating effect, reducing shift effect, and uneven heating, etc. Improve the effect, improve the processing effect, improve the effect of stable shape

Inactive Publication Date: 2021-06-22
金艺炜
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Non-woven fabric is a kind of fabric formed without spinning and weaving. It is formed by orienting or randomly arranging short textile fibers or filaments to form a web structure, which is then reinforced by mechanical, thermal bonding or chemical methods. In the existing production process, the raw materials need to be heated and stirred, but when heated and stirred, they are heated from the bottom, which leads to uneven heating and reduces the heating effect; on the other hand, because the stirring will not bottom, so when stirring the molten mixture, the reduction effect will be reduced

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Processing technology of melt-blown non-woven fabric
  • Processing technology of melt-blown non-woven fabric
  • Processing technology of melt-blown non-woven fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Such as Figure 1-11 Shown, a kind of processing technology of meltblown nonwoven fabric, 1. may further comprise the steps:

[0033] a. Grinding: first, put the selected polypropylene raw material into the crushing device for crushing treatment. After the polypropylene crushing is completed, put the raw material into the grinder for secondary grinding. The grinding time is 40 minutes. The fineness of the raw material after grinding The degree of chemical transformation is 90 mesh;

[0034] b. Stirring: Put the ground raw materials in a into the stirring device, heat to 25°C and add deionized water into the stirring device, then stir and mix the ground raw materials, and pour them into the mixer during the stirring process of the raw materials Heating the toughening agent and continuing to stir, the stirring time was 60 minutes;

[0035] c. Spinning treatment: inject the molten mixture prepared in b into the melt-blown processing machine for spinning;

[0036] d. Pro...

Embodiment 2

[0042] A kind of processing technology of melt-blown non-woven fabric, comprises the following steps:

[0043] a. Pulverization: firstly, put the selected polypropylene raw material into a pulverization device for pulverization. After the polypropylene pulverization is completed, put the raw material into a grinder for secondary grinding. The grinding time is 60 minutes. The fineness of the raw material after grinding The degree of chemicalization is 100 mesh;

[0044] b. Stirring: Put the ground raw materials in a into the stirring device, heat to 30°C and add deionized water into the stirring device, then stir and mix the ground raw materials, and pour them into the blender during the stirring process of the raw materials Heating the toughening agent and continuing to stir, the stirring time was 80 minutes;

[0045] c. Spinning treatment: inject the molten mixture prepared in b into the melt-blown processing machine for spinning;

[0046] d. Processing: Process the fiber f...

Embodiment 3

[0048] A kind of processing technology of melt-blown non-woven fabric, comprises the following steps:

[0049] a. Pulverization: firstly, put the selected polypropylene raw material into a pulverization device for pulverization. After the polypropylene pulverization is completed, put the raw material into a grinder for secondary grinding. The grinding time is 50 minutes. The fineness of the raw material after grinding The chemical degree is 95 mesh;

[0050] b. Stirring: Put the ground raw materials in a into the stirring device, heat to 27°C and add deionized water into the stirring device, then stir and mix the ground raw materials, and pour them into the mixer during the stirring process of the raw materials Heating the toughening agent and continuing to stir, the stirring time was 70 minutes;

[0051] c. Spinning treatment: inject the molten mixture prepared in b into the melt-blown processing machine for spinning;

[0052] d. Processing: Process the fiber filaments prep...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a processing technology of a melt-blown non-woven fabric. The processing technology comprises the following steps: a, crushing, specifically, crushing a polypropylene raw material; b, stirring, specifically, putting the raw materials into a stirrer, adding a thermal toughening agent, and stirring; c, carrying out spinning treatment, specifically, carrying out spinning treatment on a molten mixture; and d, processing, specifically, processing fiber yarns prepared in the step c to obtain a melt-blown fiber layer, wherein the stirrer in the step b comprises a main body, a heating device, a motor, a stirring roller, a stirring device, a feeding hole and a discharging hole. The raw materials are uniformly heated through the heating device, and the raw materials are prevented from sticking into the main body during melting to affect the stirring effect; the uniformity of the bottom of the mixture is improved through a stirring plate, and the stirring effect is further improved, so that the product quality is improved; and the stirring device realizes heating and mixing of the thermal toughening agent, so that the thermal toughening agent is directly mixed in the mixture in the stirring process, the stirring effect is improved, and the product quality is further improved.

Description

technical field [0001] The invention belongs to the technical field of non-woven fabrics, and in particular relates to a processing technology of melt-blown non-woven fabrics. Background technique [0002] Non-woven fabric is a kind of fabric formed without spinning and weaving. It is formed by orienting or randomly arranging short textile fibers or filaments to form a web structure, which is then reinforced by mechanical, thermal bonding or chemical methods. In the existing production process, the raw materials need to be heated and stirred, but when heated and stirred, they are heated from the bottom, which leads to uneven heating and reduces the heating effect; on the other hand, because the stirring will not The bottom of the tank, so the reduction effect will be reduced when the molten mixture is stirred. Contents of the invention [0003] In order to overcome the deficiencies of the prior art, the present invention provides a process for improving the uniform stirri...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D04H1/56D04H1/4291D01D1/00D01D1/04B01F7/18B01F15/06
CPCD04H1/56D04H1/4291D01D1/00D01D1/04B01F27/191B01F27/90B01F35/93B01F2035/99
Inventor 金艺炜
Owner 金艺炜
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap