A kind of metallic glaze and its preparation method and application method

An application method and technology of metallic glaze, applied in the field of ceramic glaze, can solve the problems of difficult appearance of metallic luster, poor stability of metallic effect, poor metallic effect, etc., and achieve the effects of improving the superiority rate, showing stability and reducing crystallization conditions.

Active Publication Date: 2022-01-18
FOSHAN SANSHUI CREATE TIDE
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] One of the purposes of the present invention is to overcome the deficiencies of the prior art and provide a metallic glaze to solve the problems of the existing metallic glazes that the metallic luster is not easy to appear and the stability of the metallic effect is poor
[0006] The third object of the present invention is to provide a method for applying a metal glaze, that is, to apply the above-mentioned metal glaze or the metal glaze obtained by the above-mentioned method for preparing a metal glaze to prepare ceramic rock slabs, so as to solve the existing problems. The metal effect of the ceramic rock plate is not good, and the glaze has many defects, and it can present a three-dimensional effect on the ceramic rock plate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of metallic glaze and its preparation method and application method
  • A kind of metallic glaze and its preparation method and application method
  • A kind of metallic glaze and its preparation method and application method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] A kind of metallic glaze of the present embodiment, the weight percent of its each raw material is:

[0048] Albite 37%, quartz 15%, wollastonite 2%, calcined kaolin 9%, calcined zinc oxide 4%, calcined iron phosphate 19%, self-made high phosphorus frit powder 14%.

[0049] Among them, the weight percentage of each raw material in the self-made high phosphorus frit powder is: aluminum dihydrogen phosphate 40%, phosphate rock powder 15%, sodium carbonate 12%, calcined kaolin 9%, potassium carbonate 13%, alumina 11%.

[0050] The preparation method of this metallic glaze comprises the following steps:

[0051] Step S11, preparing self-made high-phosphorus frit powder: weighing according to the above formula of self-made high-phosphorus frit powder, mixing the weighed raw materials evenly in a mixer, and then melting in a high-temperature frit furnace, the melting process The heating rate in the medium is 10°C / min, the maximum temperature is 1000°C, and the holding time i...

Embodiment 2

[0057] A kind of metallic glaze of the present embodiment, the weight percent of its each raw material is:

[0058] Albite 35%, quartz 8%, wollastonite 4%, calcined kaolin 11%, calcined zinc oxide 4%, calcined iron phosphate 23%, self-made high phosphorus frit powder 15%.

[0059] Among them, the weight percentage of each raw material in the self-made high phosphorus frit powder is: aluminum dihydrogen phosphate 48%, phosphate rock powder 10%, sodium carbonate 11%, calcined kaolin 5%, potassium carbonate 12%, alumina 14%.

[0060] The preparation method of this metallic glaze comprises the following steps:

[0061] Step S11, preparing self-made high-phosphorus frit powder: weighing according to the above formula of self-made high-phosphorus frit powder, mixing the weighed raw materials evenly in a mixer, and then melting in a high-temperature frit furnace, the melting process The heating rate in the medium is 10°C / min, the maximum temperature is 1050°C, and the holding time i...

Embodiment 3

[0067] A kind of metallic glaze of the present embodiment, the weight percent of its each raw material is:

[0068] Albite 34%, quartz 10%, calcined kaolin 16%, calcined zinc oxide 4%, calcined iron phosphate 23%, homemade high phosphorus frit powder 13%.

[0069] Among them, the weight percentage of each raw material in the self-made high phosphorus frit powder is: aluminum dihydrogen phosphate 30%, phosphate rock powder 25%, sodium carbonate 15%, calcined kaolin 5%, potassium carbonate 15%, alumina 10%.

[0070] The preparation method of this metallic glaze comprises the following steps:

[0071] Step S11, preparing self-made high-phosphorus frit powder: weighing according to the above formula of self-made high-phosphorus frit powder, mixing the weighed raw materials evenly in a mixer, and then melting in a high-temperature frit furnace, the melting process The heating rate in the medium is 10°C / min, the highest temperature is 1060°C, and the holding time is 5h. After stopp...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of ceramic glazes, and relates to a metal glaze and a preparation method and an application method thereof; the weight percentages of each raw material in the metal glaze are: 30-37% albite, 8-15% quartz, 0-4 % wollastonite, 9-16% calcined kaolin, 4-6% calcined zinc oxide, 19-23% calcined iron phosphate, 13-20% self-made high phosphorus frit powder. On the basis of calcined iron phosphate, the metal glaze adds self-made high-phosphorus frit powder as a crystallization accelerator to make the metallic luster easier to appear, and the self-made high-phosphorus frit powder introduces P element in the form of frit, compared with High-phosphorus raw material system, the self-made high-phosphorus frit powder has a wider firing temperature range, making the metal effect more stable; by fine-tuning the ratio of the self-made high-phosphorus frit powder and silicon-aluminum glaze, that is It can realize the adjustment of metal effects of different colors. In addition, the metal glaze is combined with a roller printing process, which can make the glaze surface present a good three-dimensional effect.

Description

technical field [0001] The invention relates to the technical field of ceramic glazes, in particular to a metal glaze, a preparation method and an application method thereof. Background technique [0002] Decorative metal materials are highly sought after by consumers because of their gorgeous and precious decorative styles, but their high price and poor acid and alkali resistance limit their application scenarios. With the innovation of preparation technology of decorative materials, architectural ceramics with metallic effects are widely used because of their realistic metallic luster and excellent corrosion resistance. [0003] Among them, the metal glaze is a special crystal glaze. There are four methods of preparing metallic glazes in the ceramic industry: coating pyrolysis and imitation gold technology, thermal spraying, evaporation and sintering. The sintering method is the most common method for preparing metallic glazes. Usually, transition metal oxides (such as C...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C8/14C03C8/08C04B41/89
Inventor 肖元成王衔雯周军张天杰戴建斌黄文辉张丹肖永平
Owner FOSHAN SANSHUI CREATE TIDE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.