Heat-resistant lubricating grease and preparation method thereof

A lubricating grease and heat-resistant technology, applied in the field of lubricating oil, can solve the problems of reducing the service life of the base lubricating grease, large friction coefficient, etc., and achieve the effects of good high temperature resistance, good anti-friction performance, and improved anti-ageing ability

Inactive Publication Date: 2022-04-22
湖北润滑之道科技有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the deficiencies of the prior art, the present invention provides a heat-resistant lubricating grease and its preparation method, which solves the problem that the friction coefficient of the existing synthetic-based lubricating grease will be large due to the friction of the workpiece rotation when the friction is used, thereby reducing the Solved the problem of the service life of the base grease

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Heat-resistant lubricating grease and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] The embodiment of the present invention provides a technical solution: a heat-resistant lubricating grease, which is composed of the following components and components: 75% of polyalphaolefin synthetic oil, 75% of high alkali value synthetic petroleum calcium sulfonate, and 10% of conversion agent acetic acid , 12-hydroxystearic acid 20%, boric acid 10%, calcium hydroxide 10%, sebacic acid 5%, water 50%, phenolic antioxidant 5%, thiadiazole derivatives 5% and high relative molecular weight 1% by mass liquid phenol.

[0029] The preparation method of above-mentioned a kind of heat-resistant lubricating grease specifically comprises the following steps:

[0030] S1. Transformation process: Use a balance to weigh the base oil and high-alkali synthetic petroleum calcium sulfonate of sufficient quality, add the weighed base oil and high-alkali synthetic petroleum calcium sulfonate to the beaker in turn, and fix the beaker on the In the oil bath, install the stirrer, start ...

Embodiment 2

[0039] The embodiment of the present invention provides a technical solution: a heat-resistant lubricating grease, which is composed of the following components and components: 80% of polyalphaolefin synthetic oil, 80% of high alkali value synthetic petroleum calcium sulfonate, and 15% of conversion agent acetic acid , 12-hydroxystearic acid 25%, boric acid 15%, calcium hydroxide 12, sebacic acid 8%, water 50%, phenolic antioxidant 5%, thiadiazole derivatives 5% and high molecular weight liquid Phenol 3%.

[0040] The preparation method of above-mentioned a kind of heat-resistant lubricating grease specifically comprises the following steps:

[0041] S1. Transformation process: Use a balance to weigh the base oil and high-alkali synthetic petroleum calcium sulfonate of sufficient quality, add the weighed base oil and high-alkali synthetic petroleum calcium sulfonate to the beaker in turn, and fix the beaker on the In the oil bath, install the stirrer, start the stirrer, adjus...

Embodiment 3

[0050] The embodiment of the present invention provides a technical solution: a heat-resistant lubricating grease, which is composed of the following components and components: 90% of polyalphaolefin synthetic oil, 90% of high alkali value synthetic petroleum calcium sulfonate, and 20% of conversion agent acetic acid , 30% of 12-hydroxystearic acid, 20% of boric acid, 15% of calcium hydroxide, 10% of sebacic acid, 50% of water, 5% of phenolic antioxidant, 5% of thiadiazole derivatives and high relative molecular weight Liquid Phenol 5%.

[0051] The preparation method of above-mentioned a kind of heat-resistant lubricating grease specifically comprises the following steps:

[0052] S1. Transformation process: Use a balance to weigh the base oil and high-alkali synthetic petroleum calcium sulfonate of sufficient quality, add the weighed base oil and high-alkali synthetic petroleum calcium sulfonate to the beaker in turn, and fix the beaker on the In the oil bath, install the s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses heat-resistant lubricating grease and a preparation method thereof. The heat-resistant lubricating grease is prepared from poly-alpha-olefin synthetic oil, high-base-number synthetic petroleum calcium sulfonate, a transforming agent acetic acid, 12-hydroxystearic acid, boric acid, calcium hydroxide, sebacic acid, water, a phenolic antioxidant, a thiadiazole derivative, high-relative-molecular-mass liquid phenol and a regulator. And finally, adding the liquid phenol with high relative molecular mass into the prepared base lubricating grease to obtain a finished product. According to the heat-resistant lubricating grease and the preparation method thereof, the smaller the adding amount of the high-relative molecular mass liquid phenol is, the minimum lubricating friction factor is achieved, the best antifriction performance is achieved and is reduced by about 9% compared with that of traditional lubricating grease, the anti-aging capacity of the lubricating grease is improved, and the problem that when existing synthetic base lubricating grease is used for friction, the service life of the lubricating grease is prolonged is solved. The friction coefficient is large due to friction of rotation of a workpiece, so that the service life of the base grease is shortened.

Description

technical field [0001] The invention relates to the technical field of lubricating oil, in particular to a heat-resistant lubricating grease and a preparation method thereof. Background technique [0002] Lubricating oil is a technology-intensive product, which is a mixture of complex hydrocarbons, and its real performance is the combined effect of complex physical or chemical changes. The basic properties of lubricating oil include general physical and chemical properties, special physical and chemical properties and simulated bench tests. [0003] The existing synthetic lubricating grease wall traditional lubricating grease has good performance, and all of them are high temperature resistant. However, when the existing synthetic base lubricating grease is used for friction, the friction coefficient will be large due to the friction of the workpiece rotation, thereby reducing the base lubrication. Grease service life. Contents of the invention [0004] (1) Solved techni...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C10M173/02C10M177/00C10N30/06C10N30/10C10N30/08C10N50/10
CPCC10M173/02C10M177/00C10M2205/02C10M2219/046C10M2207/122C10M2207/128C10M2201/087C10M2201/062C10M2207/127C10M2207/023C10M2219/106C10M2201/02C10N2030/06C10N2030/10C10N2030/08C10N2050/10C10N2010/04
Inventor 李兆阳
Owner 湖北润滑之道科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap