A technology of damp heat aging and photovoltaic modules, applied in the field of photovoltaics, can solve the problems of unfavorable updating of new materials or new processes, prolonging the speed of rejecting unsuitable solutions, and large amount of materials used, so as to optimize battery technology and aging resistance, save Electrical connection and auxiliary material packaging, the effect of increasing the corrosion rate

Pending Publication Date: 2022-04-29
ZHEJIANG JINKO SOLAR CO LTD +1
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, conventional photovoltaic module products are used for damp heat testing, the amount of materials used is large, and the test cost is high; and the test time is long (1000h-2000h), the entire verification cycle is as long as 4-5 months

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Humidity-heat aging test method for photovoltaic module
  • Humidity-heat aging test method for photovoltaic module
  • Humidity-heat aging test method for photovoltaic module

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0030] Reference will now be made to the accompanying drawings to describe in detail various exemplary embodiments of the present invention. It should be noted that, unless otherwise specified, the relative arrangement of the components and steps described in these embodiments, numerical expressions and numerical values do not limit the scope of the present invention.

[0031] The following description of at least one exemplary embodiment is in fact merely illustrative and in no way is intended as any restriction on the present invention and its application or use.

[0032] Techniques, methods and equipment known to those of ordinary skill in the relevant art may not be discussed in detail, but where appropriate, the techniques, methods and equipment should be considered part of the specification.

[0033]In all the examples shown and discussed here, any concrete value should be interpreted as merely exemplary and not as a limitation. Thus, other examples of exemplary embodiments...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a damp-heat aging test method for a photovoltaic module, which comprises the following steps: preparing a sample: providing a bare battery piece, and welding a welding strip on the front surface of the bare battery piece to obtain the sample; the sample testing step comprises the steps that initial testing is carried out on the sample to obtain an initial testing result, and the initial testing comprises power testing, PL testing and EL testing; putting the sample subjected to the initial test into a damp-heat aging oven for testing, and setting the testing conditions of the damp-heat aging oven as follows: the testing temperature is 85 +/-1 DEG C, the relative humidity is 85 +/-1%, and the testing time is 24 hours; and a sample result analysis step: performing post-detection on the sample to obtain a post-test result, the post-detection comprising power test, PL test and EL test, and calculating an attenuation value according to the initial test result and the post-test result. The method is closer to the state of a bare battery piece in an actual photovoltaic module product, the corrosion speed of the sample is increased, the experiment process is accelerated, and a large number of test resources are saved.

Description

technical field [0001] The invention relates to the technical field of photovoltaics, and more particularly, to a method for testing the damp heat aging of photovoltaic modules. Background technique [0002] At present, when photovoltaic manufacturing enterprises update new materials or improve and upgrade products, in order to verify the process reliability of materials or new products, they need to do a series of reliability tests to ensure that the life of photovoltaic modules reaches more than 25 years. Among them, the damp heat test (DH) is an important aging test, and its test conditions are temperature 85°C and humidity 85%. Through the damp heat test, the damp heat aging resistance performance of each component of the photovoltaic module product and the package is systematically evaluated and analyzed, and then Improve it to improve the overall performance of the product. [0003] At present, conventional photovoltaic module products are used for damp heat testing, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H02S50/10
CPCH02S50/10Y02E10/50
Inventor 闫灯周宫欣欣郭志球古文俊
Owner ZHEJIANG JINKO SOLAR CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap