Preparing method and apparatus of artificial crystal synthetic mica

A technology for synthesizing mica and artificial crystals, applied in electric heating devices, chemical instruments and methods, silicon compounds, etc., can solve the problems of low purity, low mica yield, and poor mica performance, and achieve the effect of strong light transmission performance

Inactive Publication Date: 2006-04-26
辽宁中科晶体产业有限公司
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There is also artificially synthesized mica in the prior art. Due to the inaccurate formula and the unreasonable production process, the operating conditions controlled in the preparation are not suitable, which makes the performance of the synthesized mica worse. There are impurities, and its crystal sheets are also small, which greatly reduce the comprehensive utilization value of synthetic mica
[0003] Traditional mica manufacturing equipment mostly uses DC two-phase power supply for power supply. Due to the low voltage of the two-phase power supply, the electrodes connected to the power supply have small arcing and generate less heat, resulting in low mica production and high cost; moreover, the flow through the electrodes The current is unstable, the power factor is low, and the impact on the power grid is large, which makes the traditional mica manufacturing equipment unsuitable for industrialized large-scale production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparing method and apparatus of artificial crystal synthetic mica
  • Preparing method and apparatus of artificial crystal synthetic mica
  • Preparing method and apparatus of artificial crystal synthetic mica

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0063] The artificial crystal synthetic mica provided by the invention comprises quartz sand, magnesia, aluminum oxide powder, potassium fluorosilicate and potassium carbonate in the basic composition of its preparation raw materials, and its content (weight percent) purity and particle size are:

[0064] Quartz sand (SiO 2 ) 40%~35% 97%~99% 40 mesh~100 mesh

[0065] Magnesia (MgO) 30% to 29% 92% to 99% 16 mesh to 30 mesh

[0066] Alumina powder (Al 2 o 3 ) 10%~13% 98%~99% 120 mesh~200 mesh

[0067] Potassium fluorosilicate (K 2 SiF 6 ) 16%~20% 98%~99% 120 mesh~200 mesh

[0068] Potassium carbonate (K 2 CO 3 ) 4% ~ 3% 96% ~ 99% 16 mesh ~ 40 mesh

[0069] The molecular formula of the artificial crystal synthetic mica synthesized by the above raw materials is: KMg 3 (AlSi 3 o 10 ) F 2 .

[0070] In the prepared KMg 3 (AlSi 3 o 10 ) F 2 In, SiO 2 The content of Al is 38-42%. 2 o 3 The content of K is between 10% and 14%. 2 The content of O is 9-14%, the cont...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method and device for artificial crystal synthetic mica. The method and device provided by the invention provide reliable guarantee for obtaining high-quality synthetic mica. In addition to being used as synthetic mica, each component in the raw material for preparing synthetic mica provided by the invention also has the function of removing impurities in the raw material, which lays a good foundation for forming synthetic mica and obtains high-quality synthetic mica.

Description

technical field [0001] The invention provides an artificially synthesized crystal, in particular a preparation method for artificially synthesized mica. The invention also relates to a preparation device for the artificial crystal synthetic mica. Background technique [0002] Mica is a crystalline substance with good insulation, corrosion resistance and high temperature resistance, and is widely used in various fields. The natural mica commonly used in the prior art has some deficiencies, mainly in terms of corrosion resistance and high temperature resistance, which gradually cannot meet the higher requirements in use. In terms of high temperature resistance, natural muscovite melts at 400-500°C, and phlogopite also melts at 600-800°C. There is also artificially synthesized mica in the prior art. Due to the inaccurate formula and the unreasonable production process, the operating conditions controlled in the preparation are not suitable, which makes the performance of the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01B33/26C01B33/42H05B7/00
Inventor 孙海英
Owner 辽宁中科晶体产业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products