Screen printing making technology

A technology of screen printing plate and metal screen, which is applied in the direction of screen printing machine, printing plate, printing plate preparation, etc., can solve the problems of tension stability, uniformity of screen thickness and uniformity of printing layer thickness , poor adhesion of the light-cured resin layer, etc., to increase the amount of dye transferred, reduce the wear of the printing plate, and improve the permeability

Inactive Publication Date: 2006-05-10
MURAKAMI CORP
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, metal fiber screens and metal sheet screens do not have good adhesion to the photocurable resin layer (resistance layer) as the image layer, and are easy to separate from the photocurable resin layer during printing, and the metal screen is tightened in addition. There are also problems with the stability of the tension, the uniformity of the thickness of the screen, and the uniformity of the thickness of the printing layer.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1 and comparative example 1

[0080] (1) Stretching step

[0081] Stretch a 325-mesh, 64.0μm-thick stainless steel fiber screen on an aluminum die-cast screen frame with a size of 320mm×320mm through a mechanical stretcher to prepare a stainless steel screen printing plate stretched on the aluminum screen frame . Two such plates were prepared.

[0082] (2) Sand blasting step

[0083] One of the two printing plates was blasted on its printing surface for 60 seconds with a blaster (model SC, blasting material No. 800 (alumina), manufactured by Fuji Manufacturing Co., Ltd.).

[0084] The other plate was not sandblasted.

[0085] As a result, it was found by surface roughness material equipment (profile measuring microscope VF-7500, manufactured by Keyence Corporation) that the stainless steel wire subjected to sandblasting roughening to generate many pits with a depth of about 3 μm (the percentage of pits was 60%) The mesh formed a satin pattern over the entire surface (Example 1).

[0086] On the other ...

example 2 and comparative example 2

[0101] (1) Stretching step

[0102] Stretch a 225-mesh polyester fiber screen with a thickness of 73 μm on an aluminum die-casting frame with a size of 320mm×320mm through a mechanical stretcher to prepare polyester filaments stretched on the aluminum frame screen printing version. Two such plates were prepared.

[0103] Then, a high-tensile stainless steel fiber mesh with an opening size of 360 mesh (filament diameter: 16 µm) was laminated and pasted on the central portion of the polyester mesh with an adhesive. The overlapping part of the polyester screen is removed, and the printing plate of the combined screen is stretched on the screen frame. Two such plates were prepared.

[0104] (2) Sand blasting step

[0105] One of the two printing plates was blasted on its printing surface for 30 seconds with a blaster (model SC, blasting material No. 1000 (alumina), manufactured by Fuji Manufacturing Co., Ltd.).

[0106] The other plate was not sandblasted.

[0107] As a resu...

example 3

[0121] Repeat the operation of Example 1, using polishing instead of sandblasting.

[0122] The results of the evaluation are shown in Table 5.

[0123] polishing

[0124] The tensioned wire mesh was slowly passed between two rotating non-woven fabric polishers "CP wheel7 AVF" manufactured by 3M Company to form a straight hair pattern containing a large number of dimples with a depth of 4 μm.

[0125] Evaluation results

[0126] coarsening

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
surface roughnessaaaaaaaaaa
depthaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

THRE IS PROVIDED A PLATE FOR SCREEN PRINTING, COMPRISING: A SCREEN STRETCHED OVER A FRAME; AND AN IMAGE LAYER, FORMED OF A PHOTO-CURED RESIN, PROVIDED ON THE SURFACE OF THE SCREEN, THE SCREEN COMPRISING A METALLIC SCREEN HAVING CONCAVES WITH A DEPTH OF 0.05 TO 20µm.THERE IS ALSO PROVIDED A PROCESS FOR PRODUCING A PLATE FOR SCREEN PRINTING, COMPRISING THE STEPS OF:FORMING A PHOTO-SENSITIVE RESIN LAYER ON THE SURFACE OF A METALLIC SCREEN STRETCHED OVER A FRAME; EXPOSING THE PHOTO-SENSITIVE RESION LAYER THROUGH A MASK TO FORM A LATENT IMAGE; AND DEVELOPING THE EXPOSED RESIN LAYER TO FORM AN IMAGE LAYER,THE SURFACE OF THE METALLIC SCREEN HAVING BEEN ROUGHENED BY BLOWING GRAINS HAVING A SIZE OF 100 TO 2,000 MESH AGAINST THE SURFACE OF THE METALLIC SCREEN AND / OR BY BUFFING.

Description

[0001] This application was filed on June 1, 2000 by Murakami Co., Ltd., the applicant. It is a divisional application of the application with the application number 00117934.9 and the title of the invention "screen printing plate and its manufacturing process". technical field [0002] The invention relates to a screen printing plate using a metal screen, and a process for making the printing plate. Specifically, the present invention relates to a screen printing plate, which can realize the tension stability and uniform screen thickness in the early stage of the screen by tightening the wire mesh, and can improve the adhesion between the resistance layer and the wire mesh during the plate making process. In the printing process, it can improve the permeability of the ink, increase the amount of dye transferred, reduce invalid printing and improve the positioning accuracy of the printed product, the uniformity of the thickness of the printing layer, and reduce the wear of the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B41C1/14B41F15/36B41F15/34B41N1/24G03F7/00G03F7/12
CPCB41C1/147B41N1/24G03F7/20
Inventor 宫坂四志男间濑惠二村上泰藏长尾文隆井上和夫
Owner MURAKAMI CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com