Abstract

The invention discloses an imitated silk fabric reactive printing method which comprises the following steps: pretreatment of fabrics: imitated silk fabric cloth is put into a pretreating agent to be pretreated; sizing: the pretreated imitated silk fabric cloth undergoes sizing by a sizing machine; heat shaping; making of print files; jet-printing: jet-printing is carried out by a digital ink-jet printing machine; and streaming drying is carried out to obtain a finished product. By the method for reactive ink-jet printing of imitated silk fabric cloth, printing effect and colour fastness are both improved greatly, and there is no need to specially process ink. The machine is not easy to damage, and hand feeling of the product is also improved obviously.

Description

Technical field

[0001] The present invention involves a textile printing and dyeing technology field, which specifically involves a method of simulating silk active printing. Background technique

[0002] Digital inkjet printing is a printed technology developed rapidly in recent years. It is the driver of ink containing pigments under the driver of compressed air. It is sprayed from the nozzle to the fabric.The performance, after appropriate post -treatment, makes the fabric have a certain color and brightness.Pre -processing fabrics to reduce the degree of seepage of ink on the fabric is very important. The seepage process of ink on the fabric can be divided into two parts. One is the seepage of inkjet printing, and the other is the generated during the printed printed..

[0003] At present, digital printing varieties include cotton, hair, chemical fiber and other types of fabrics, and there are fewer fabrics involving silk. This is because the surface of the fabric is relative...

Examples

Embodiment 1

[0037] A method for imitation silk active printing, the steps are as follows:

[0038] (1) Fabric pretreatment: Put the imitation silk cloth into the pretreatment agent for pretreatment

[0039] Pretreatment agent is made up of the raw material of following parts by weight:

[0040] Trehalose 1 part

[0041] Collagen 1.5 parts

[0042] 50 parts of water

[0043] (2) Sizing: The pretreated imitation silk cloth is sizing on a sizing machine, and the sizing is composed of the following raw materials in parts by weight:

[0044] Phosphate grafted starch 0.5 parts

[0045] 4 parts sodium alginate

[0046] Nano titanium dioxide 1 part

[0047] Baking soda 3 parts

[0048] Yuan Mingfen 2 parts

[0049] 4 parts urea

[0050] Triethylene glycol 1 part

[0051] 40 parts of water

[0052] Mix the above components and put them into a beater, beat until the slurry is uniform, and then let it stand for 2 hours;

[0053] (3) Heating and shaping: Two hot blankets are pressed and h...

Embodiment 2

[0058] A method for imitation silk active printing, the steps are as follows:

[0059] (1) Fabric pretreatment: Put the imitation silk cloth into the pretreatment agent for pretreatment

[0060] Pretreatment agent is made up of the raw material of following parts by weight:

[0061] Trehalose 2 parts

[0062] Collagen 1 part

[0063] 60 parts of water

[0064] (2) Sizing: The pretreated imitation silk cloth is sizing on a sizing machine, and the sizing is composed of the following raw materials in parts by weight:

[0065] Phosphate grafted starch 1.5 parts

[0066] 3 parts sodium alginate

[0067] Nano titanium dioxide 1.5 parts

[0068] Baking soda 2 parts

[0069] Yuan Mingfen 3 parts

[0070] 3 parts urea

[0071] Triethylene glycol 1 part

[0072] 50 parts of water;

[0073] Mix the above components and put them into a beater, beat until the slurry is uniform, and then let it stand for 2 hours;

[0074] (3) Heating and shaping: Two hot blankets are pressed and...

Embodiment 3

[0079] A method for imitation silk active printing, the steps are as follows:

[0080] (1) Fabric pretreatment: Put the imitation silk cloth into the pretreatment agent for pretreatment

[0081] Pretreatment agent is made up of the raw material of following parts by weight:

[0082] Trehalose 1 part

[0083] Collagen 1.4 parts

[0084] 55 parts of water

[0085] (2) Sizing: The pretreated imitation silk cloth is sizing on a sizing machine, and the sizing is composed of the following raw materials in parts by weight:

[0086] Phosphate grafted starch 0.7 part

[0087] 4 parts sodium alginate

[0088] Nano titanium dioxide 1.1 parts

[0089] Baking soda 3 parts

[0090] Yuan Mingfen 2 parts

[0091] 4 parts urea

[0092] Triethylene glycol 1 part

[0093] 42 parts of water

[0094] Mix the above components and put them into a beater, beat until the slurry is uniform, and then let it stand for 2 hours;

[0095] (3) Heating and shaping: Two hot blankets are pressed and...

Technical field

[0001] The present invention involves a textile printing and dyeing technology field, which specifically involves a method of simulating silk active printing. Background technique

[0002] Digital inkjet printing is a printed technology developed rapidly in recent years. It is the driver of ink containing pigments under the driver of compressed air. It is sprayed from the nozzle to the fabric.The performance, after appropriate post -treatment, makes the fabric have a certain color and brightness.Pre -processing fabrics to reduce the degree of seepage of ink on the fabric is very important. The seepage process of ink on the fabric can be divided into two parts. One is the seepage of inkjet printing, and the other is the generated during the printed printed..

[0003] At present, digital printing varieties include cotton, hair, chemical fiber and other types of fabrics, and there are fewer fabrics involving silk. This is because the surface of the fabric is relative...

Examples

Embodiment 1

[0037] A method for imitation silk active printing, the steps are as follows:

[0038] (1) Fabric pretreatment: Put the imitation silk cloth into the pretreatment agent for pretreatment

[0039] Pretreatment agent is made up of the raw material of following parts by weight:

[0040] Trehalose 1 part

[0041] Collagen 1.5 parts

[0042] 50 parts of water

[0043] (2) Sizing: The pretreated imitation silk cloth is sizing on a sizing machine, and the sizing is composed of the following raw materials in parts by weight:

[0044] Phosphate grafted starch 0.5 parts

[0045] 4 parts sodium alginate

[0046] Nano titanium dioxide 1 part

[0047] Baking soda 3 parts

[0048] Yuan Mingfen 2 parts

[0049] 4 parts urea

[0050] Triethylene glycol 1 part

[0051] 40 parts of water

[0052] Mix the above components and put them into a beater, beat until the slurry is uniform, and then let it stand for 2 hours;

[0053] (3) Heating and shaping: Two hot blankets are pressed and h...

Embodiment 2

[0058] A method for imitation silk active printing, the steps are as follows:

[0059] (1) Fabric pretreatment: Put the imitation silk cloth into the pretreatment agent for pretreatment

[0060] Pretreatment agent is made up of the raw material of following parts by weight:

[0061] Trehalose 2 parts

[0062] Collagen 1 part

[0063] 60 parts of water

[0064] (2) Sizing: The pretreated imitation silk cloth is sizing on a sizing machine, and the sizing is composed of the following raw materials in parts by weight:

[0065] Phosphate grafted starch 1.5 parts

[0066] 3 parts sodium alginate

[0067] Nano titanium dioxide 1.5 parts

[0068] Baking soda 2 parts

[0069] Yuan Mingfen 3 parts

[0070] 3 parts urea

[0071] Triethylene glycol 1 part

[0072] 50 parts of water;

[0073] Mix the above components and put them into a beater, beat until the slurry is uniform, and then let it stand for 2 hours;

[0074] (3) Heating and shaping: Two hot blankets are pressed and...

Embodiment 3

[0079] A method for imitation silk active printing, the steps are as follows:

[0080] (1) Fabric pretreatment: Put the imitation silk cloth into the pretreatment agent for pretreatment

[0081] Pretreatment agent is made up of the raw material of following parts by weight:

[0082] Trehalose 1 part

[0083] Collagen 1.4 parts

[0084] 55 parts of water

[0085] (2) Sizing: The pretreated imitation silk cloth is sizing on a sizing machine, and the sizing is composed of the following raw materials in parts by weight:

[0086] Phosphate grafted starch 0.7 part

[0087] 4 parts sodium alginate

[0088] Nano titanium dioxide 1.1 parts

[0089] Baking soda 3 parts

[0090] Yuan Mingfen 2 parts

[0091] 4 parts urea

[0092] Triethylene glycol 1 part

[0093] 42 parts of water

[0094] Mix the above components and put them into a beater, beat until the slurry is uniform, and then let it stand for 2 hours;

[0095] (3) Heating and shaping: Two hot blankets are pressed and...