Electrical grade sheet electro-magnetism performance measurement method

A technology of electrical steel plate, measurement method, applied in the detection field

Inactive Publication Date: 2008-07-02
ANGANG STEEL CO LTD
View PDF0 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a method for measuring the electromagnetic properties of electrical steel sheets. Through the EBSD test results of the sample, the electromagnetic properties of the material can be deduced by using the correlation correction coefficient, so as to solve the problem that the electromagnetic properties of the sample cannot be measured due to the limitation of the sample size and quantity. measurement problem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Electrical grade sheet electro-magnetism performance measurement method
  • Electrical grade sheet electro-magnetism performance measurement method
  • Electrical grade sheet electro-magnetism performance measurement method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0011] A kind of measuring method of the electromagnetic property of electrical steel plate of the present invention is:

[0012] 1. Use the EBSD system to measure the Euler angle of each point orientation on the cross-section of the sample, and ensure that the orientation information of each point on the entire thickness of the steel plate is measured.

[0013] 2. For the measurement of the magnetic properties of non-oriented silicon steel, by calculating the angle between the (100) crystal plane and the rolling surface of the grains at each point, the orientation points with the same angle are combined into the same orientation, and the proportion of each orientation is calculated X i ; For the measurement of the magnetism of grain-oriented silicon steel, first calculate the angle between the crystal direction of each grain and the rolling direction, and merge the orientation points with the same angle into the same orientation, and calculate the proportion of each orientati...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method of measuring electromagnetic performance of electric steel plates, which is characterized in that the method measures three Euler angles of each sample point orientation in an EBSD system and occupied proportion X of each identical or similar orientation, combining with conjectured coefficient of thickness fH, composition fc and influential factor (e) of misorientation on performance, applies these factors to modify the measuring on the basis of pure iron performance B, which is applicable for small quantity of samples that cannot be measured by Epstein frame, manifesting performance of each micro area of the sample and enabling good effect for the process improvement of the material with the same composition. In addition, the invention provides statistical calculation of crystal orientation of each orientation (100) in the measuring of non-oriented silicon steel, completely reflecting the general magnetic property of steel plates.

Description

technical field [0001] The invention relates to the detection field, in particular to a method for measuring the electromagnetic properties of electrical steel sheets. Background technique [0002] The Epstein square circle method is used to measure the magnetic properties of electrical steel. The surface quality of the steel plate will have a certain impact on the performance test. The measurement of electromagnetic properties by this method can only reflect the overall performance of electrical steel macroscopically, and has a certain impact on the number and specifications of samples. Require. For non-oriented silicon steel, this method only measures the horizontal and vertical electromagnetic properties of the steel plate, while non-oriented silicon steel is applied in a rotating magnetic field, and requires good performance in all directions on the rolling surface. Therefore, this method cannot reflect the actual level of non-oriented silicon steel. For example, the h...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): G01R31/00G01R33/12
Inventor 张智义高振宇李文权李斌罗理王开宇张仁波于爽
Owner ANGANG STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap