Acroleic acid mixed powder coating
A powder coating and hybrid technology, applied in powder coatings, epoxy resin coatings, coatings, etc., can solve problems that affect anti-yellowing and anti-loss properties, are highly toxic, and do not meet environmental protection, and achieve improved anti-yellowing Denaturation and tarnish resistance, low cost, effect of improving outdoor durability
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0010] The following examples further illustrate the present invention.
[0011] Accurately weigh the materials according to the composition of the embodiment in Table 1, and place them in a high-speed mixer to mix for 10-12 minutes; after the materials are mixed, they are extruded with an extruder at a temperature of 100-115°C; the extruded materials are pulverized with a crusher to average Powder particles with a particle size of 35-45 microns; the powder particles are sieved with a 140-mesh screen and packaged as finished products.
[0012] The formula of acrylic hybrid powder coating is shown in Table 1:
[0013] Table 1 Formula of acrylic hybrid powder coating (parts by weight)
[0014]
[0015] The acrylic hybrid powder coating obtained according to the above examples is sprayed with an electrostatic spray gun of 50-70 μm, and cured in an electric oven at 190°C for 25 minutes. Perform performance inspection on the coating. Its main coating film properties are:
...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap