Holography positioning alumite high speed thermoprint back glue and preparation method

An anodized aluminum, high-speed technology, applied in the direction of adhesives, temperature recording methods, adhesive types, etc., can solve the problems of hot stamping transfer integrity and edge tidiness that are difficult to reach high-end customers, achieve excellent adhesion performance, increase crosslinking Effect, bright and fast-drying effect of paint film

Active Publication Date: 2010-06-23
湖北省葛店开发区晨光实业有限公司 +1
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For example, the back glue of hot stamping paper cannot be hot stamped with ink and plastic, the back glue of hot stamped plastic cannot be hot stamped with UV ink or frosted ink, and products with a surface tension less than 38 dynes cannot be hot stamped at high speed. The neatness of the edges is also difficult to meet the requirements of high-end customers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0028] The present invention will be further described below in conjunction with embodiment:

[0029] raw material:

[0030] 50 kg of phenolic resin, 25 kg of EVA resin, 40 kg of acrylic resin, 30 kg of PU resin, 6 kg of chlorinated polyolefin, 117 kg of ethyl acetate, 80 kg of toluene, 18 kg of methyl ethyl ketone, 2 kg of isobutanol, polyether Modified dimethyl siloxane 0.5 kg, fumed silica 2.5 kg.

[0031] preparation:

[0032] ①Put 50 kg of phenolic resin 2402 (solid) and 50 kg of ethyl acetate into a stirring container, heat to 50°C for stirring and dispersing, stirring at a speed of 30 rpm, and stirring time of 60 minutes until the phenolic resin is completely dissolved to make 50 % phenolic resin solution, sealed in a container for subsequent use;

[0033] ②Put 25 kg of vinyl acetate EVA resin (solid), 37 kg of ethyl acetate and 38 kg of toluene into the mixing container, heat to 50°C for stirring and dispersing, the stirring speed is 30 rpm, and the stirring time is...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
softening pointaaaaaaaaaa
softening pointaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-speed hot stamping gum used for holographic positioning electrochemical aluminium and the preparation method. The gum prepared through the formulation and the method of the invention can achieve good adhesive effect under the appropriate temperature and pressure, and the appropriate release coating is added, thus the holographic image information of the holographic electrochemical aluminium can be stripped and cemented on the surface of the scalded object at the high speed. The fragileness of the gum is moderate, therefore, the trimming performance of the holographic image is good in the hot stamping process, the gum is particularly applied to high-speed hot stamping on the surface of the sheet paper and the printing ink with which the density and the hardness are big, the surface energy is low, the surface wettability is poor, and the general coating liquor is difficult to be transferred and cemented on.

Description

technical field [0001] The invention relates to a hot stamping adhesive and a preparation method thereof, in particular to a high-speed hot stamping adhesive for holographic positioning anodized aluminum and a preparation method thereof. Background technique [0002] In the process of high-speed automatic hot stamping, the anodized aluminum holographic image information layer is peeled off from the carrier film (PET) by heating and pressing, and is completely bonded to the surface of various materials through the adhesive coating, such as cigarette packs and wine packs. , plastic, cloth, leather and other surfaces. However, at present, most of the products in my country's anodized aluminum industry are medium and low-end products, which are difficult to meet the requirements of high-speed automatic hot stamping, especially for products whose surface is difficult to hot stamp, such as grinding oil ink, UU ink and other ink surfaces, PP, PE, ABS Such as plastic surfaces, soft ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J123/28C09J123/08B41M5/26C09J161/08C09J175/04C09J133/04
Inventor 刘长根涂文芳王群
Owner 湖北省葛店开发区晨光实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com