Method for manufacturing silicone modified double-sided double-color flexible decorative brick

A technology of flexible veneering and manufacturing methods, applied in chemical instruments and methods, floors, layered products, etc., can solve problems such as weather resistance, water vapor permeability constraints, easy aging and fading of color, and inconvenient construction operations, etc., to achieve Convenient typesetting process, high production efficiency, and excellent weather resistance

Inactive Publication Date: 2013-03-27
谈霄
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] 1. The flexible decorative brick with polymer cement sheet as the base, the substrate is made of polymer cement and non-woven fabric, the surface material is made of high molecular polymer as gel material and sand and gravel as aggregate ;Due to the different composition of the bottom and surface materials, the difference in surface tension between the two materials after forming will cause the brick body to bend and deform to one side. Warping, resulting in the brick joints are not dense, and the brick joints are easy to enter water, causing engineering hidden dangers
[0004] 2. The overall flexible facing brick is compounded with high molecular polymer as the gel material and sand and gravel as the aggregate. Although it overcomes the shortcomings of structural deformation, the mechanical strength of the brick body is poor due to the absence of reinforced tire base, and the manufacturing The process adopts the lining mold, so that there are a large number of irregular pores on the bottom of the brick body, which reduces the structural strength
[0005] 3. The overall flexible facing brick is compounded with high molecular polymer as the gel material and soil as the aggregate. The structure of this kind of flexible facing brick is not deformed, and the mechanical strength is also good. However, the natural soil is limited by the monotonous color. The color paste is artificially dyed, so this kind of flexible facing brick is used for exterior walls, and its color is easy to age and fade
[0006] 4. The above three types of flexible facing bricks are divided into front and back sides. During construction, it is necessary to find the opposite side to paste, especially when pasting two colors of bricks, it is necessary to match two colors of flexible facing bricks, which will bring new advantages to the construction operation. inconvenient
[0007] 5. The gel materials of the current flexible facing bricks are all made of acrylic or styrene-acrylic modified polymer emulsions, which are subject to certain restrictions in terms of weather resistance and water vapor permeability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for manufacturing silicone modified double-sided double-color flexible decorative brick

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] 1. Preparation materials:

[0032] 1. Add the polyurethane emulsion and deionized water into the liquid glue stirring tank according to the ratio of 1:1 by weight and stir evenly to make the liquid glue, and set aside;

[0033] 2. Take the following components by weight percentage: 40% of 40-80 mesh white sand, 30% of 80-120 mesh liver red sand, 10% of pure acrylic polymer emulsion, 10% of silicone resin latex, calcium stearate 2 %, antimony oxide 6%, UH4202%; add the above-mentioned components measured into the slurry preparation kettle, stir evenly to prepare silica gel modified polymer colored sand A-color slurry, and set aside;

[0034] 3. Take the following components by weight percentage: 45% of 40-80 mesh white sand, 25% of 80-120 mesh coffee red sand, 10% of pure acrylic polymer emulsion, 10% of silicone resin latex, calcium stearate 2 %, antimony oxide 6%, UH4202%; add the above-mentioned components measured into the slurry preparation kettle, stir evenly to p...

Embodiment 2

[0039] Concrete production step is the same as embodiment 1, and wherein glass fiber cloth is glass fiber non-woven fabric, and wherein standby material is prepared as follows:

[0040] 1. Add the polyurethane emulsion and deionized water into the liquid glue stirring tank according to the ratio of 1:1 by weight and stir evenly to make the liquid glue, and set aside;

[0041]2. Take the following components by weight percentage: 20 mesh-40 mesh Chinese black sand 4%, 80 mesh-200 mesh white sand 30%, 40 mesh-80 mesh golden sand 30%, styrene-acrylic polymer emulsion 12%, silicon 11.5% rubber, 2.5% zinc stearate, 7% magnesium hydroxide, TE9363%; add the above-mentioned components measured into the slurry preparation kettle, and stir evenly to prepare silica gel modified polymer colored sand A color paste material, spare;

[0042] 3. Take the following components by weight percentage: 20 mesh-40 mesh Chinese black sand 4%, 80 mesh-200 mesh white sand 50%, 40 mesh-80 mesh golden s...

Embodiment 3

[0044] Concrete production step is the same as embodiment 1, and wherein glass fiber cloth is glass fiber felt, and wherein standby material is prepared as follows:

[0045] 1. Add the polyurethane emulsion and deionized water into the liquid glue stirring tank according to the ratio of 1:1 by weight and stir evenly to make the liquid glue, and set aside;

[0046] 2. Take the following components by weight percentage: 30% of 80-120 mesh gray jade sand, 28% of 40-80 mesh gray jade sand, 14% of silicon-acrylic polymer emulsion, 13% of silica sol, hydrophobic organic silicon powder 3%, DMMP8%, T50004%; add the above-mentioned components that have been measured into the slurry preparation kettle, and stir evenly to prepare a silica gel-modified polymer colored sand A-color slurry, which is set aside;

[0047] 3. Take the following components by weight percentage: 80 mesh-120 mesh gray jade sand 30%, 40 mesh-80 mesh white sand 28%, silicon-acrylic polymer emulsion 14%, silica sol 1...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for manufacturing a silicone modified double-sided double-color flexible decorative brick. The double-sided double-color flexible decorative brick is composited by three layers, the middle layer is a glass fiber reinforced layer (2), and a silicone modified polymer color sand A paste layer (1) and a silicone modified polymer color sand B paste layer (3) are respectively coated on the upper surface and the lower surface of the glass fiber reinforced layer, wherein the thicknesses of the coating layers of the A paste and the B paste can be controlled according to design requirements, and the colors of the A paste and the B paste can be the same or different according to design requirements. The double-sided double-color flexible decorative brick produced by adopting the manufacturing method of the invention has the advantages of good flexibility, light weight per unit area, no radioactive contamination, realistic stone-like and pottery-like patterns on the appearance, high manufacturing efficiency, energy saving and environmental protection without high-temperature sintering, weather resistance, wear resistance, vapor permeability, fire resistance, convenience of use and like.

Description

technical field [0001] The invention relates to a facing material for building walls or floors and a manufacturing method thereof, in particular to a manufacturing method of silica gel-modified double-sided and double-color flexible facing bricks. Background technique [0002] It will be an inevitable trend to use non-sintered flexible facing bricks instead of high-temperature sintered, high-energy consumption, and high-carbon-emission ceramic facing bricks as facing materials for the interior and exterior walls of buildings or indoor floors. In recent years, the flexible facing materials that have been introduced to the market successively have come out continuously, which has enriched the application market of building exterior wall facing materials. However, currently several representative flexible facing bricks have unsatisfactory places in practical applications, and the common defects are: [0003] 1. The flexible decorative brick with polymer cement sheet as the bas...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B32B17/04B32B27/04B32B27/08E04F13/077E04F15/10
Inventor 谈霄
Owner 谈霄
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com