A kind of rubber asphalt, self-hardening technology, applied in the field of coatings, can solve the problems of low cloud point, self-hardening rubber asphalt coatings can not meet the construction process requirements, strict selection of components and so on

Inactive Publication Date: 2011-06-29
BEIJING ORIENTAL YUHONG WATERPROOF TECH CO LTD +1
View PDF5 Cites 25 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, high solid content no-bake rubber asphalt products are very strict in the selection of components. If the components, especially the emulsifier, are not properly selected, problems such as lo...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Self-hardening rubber asphalt paint
  • Self-hardening rubber asphalt paint
  • Self-hardening rubber asphalt paint

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] The emulsified asphalt raw materials in the invented product are proportioned according to the following (Table 1) (weight ratio, the same below):

[0042] Table 1 Emulsified asphalt formula table (100 parts of emulsified asphalt)

[0043]

[0044] The manufacturing process of emulsified asphalt is as follows:

[0045] A. Dehydrate the asphalt at 110°C-130°C for 1 hour to 2 hours, then gently heat it to 130°C-160°C, and use it after measurement;

[0046] B. Heat the tap water to 45℃-65℃, and use it after measurement;

[0047] C. Add the emulsifier and stabilizer to the standby hot water, stir evenly to make an emulsified aqueous solution, and control the temperature to 45°C-65°C for standby;

[0048] D. Turn on the emulsifier system, pour the emulsified aqueous solution that meets the temperature requirements into the emulsification, and immediately pour the hot asphalt that meets the temperature requirements, and the preparation of the emulsified asphalt that meets the requiremen...

Embodiment 2

[0055] Mix the emulsified asphalt raw materials according to the following (Table 3) (weight ratio, the same below):

[0056] Table 3 Emulsified asphalt formula table (100 parts of emulsified asphalt)

[0057]

[0058] The emulsified asphalt manufacturing process of Example 2 is as Example 1

[0059] Then mix the raw materials in the coating according to the following (table 4) ratio (weight ratio, the same below):

[0060] Table 4 Self-hardening rubber asphalt paint (100 parts paint)

[0061]

[0062] The manufacturing process of the self-hardening rubber asphalt coating of Example 2 is as in Example 1.

Embodiment 3

[0064] The emulsified asphalt raw materials are proportioned according to the following (Table 5) (weight ratio, the same below):

[0065] Table 5 Emulsified asphalt formula table (100 parts of emulsified asphalt)

[0066]

[0067] The emulsified asphalt manufacturing process of Example 3 is as Example 1

[0068] Then mix the raw materials in the coating according to the following (table 6) ratio (weight ratio, the same below):

[0069] Table 6 Self-hardening rubber asphalt paint (100 parts paint)

[0070] Emulsified asphalt

[0071] The manufacturing process of the self-hardening rubber asphalt coating of Example 3 is as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides self-hardening rubber asphalt paint which comprises the following components by weight percent: 50%-65% of asphalt, 3%-6% of cationic emulsifier, 3%-6% of nonionic emulsifier, 25%-35% of modified latex, 1%-3% of stabilizer and 5%-10% of filler. The invention further provides a preparation method of the self-hardening rubber asphalt paint, the rubber asphalt paint is modified through normal-temperature self-crosslinking emulsion, has the prominent characteristics of normal temperature spray coating, manual scrape-coating, instant shaping, perfect joint, high elastic force, zero joints and the like, and can fundamentally solve the technical difficulty of leakages at side angles, gaps and junction of irregular structures and the like, thereby thoroughly updating the traditional construction process and the method of waterproof material.

Description

Technical field [0001] The invention relates to a coating, especially a self-hardening rubber asphalt coating used in the field of waterproof and anticorrosion. Background technique [0002] In recent years, the country has strengthened investment in infrastructure and has been emphasizing environmental protection, energy saving and emission reduction. The high solid content self-hardening rubber asphalt coating is a world-class multi-purpose environmentally friendly waterproof product with room temperature spraying, instant performance, and perfect adhesion. The outstanding characteristics of joint, high elasticity, and no joints fundamentally solve the technical problems such as the leakage of corners, gaps, and irregular structure joints, and completely update the construction technology and methods of traditional waterproof materials. Hard rubber asphalt coatings will surely lead the new trend of technology upgrading in the field of waterproofing. [0003] However, high solid ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D195/00C09D111/02C09D113/02C09D109/08C09D125/14C09D107/02C09D109/04C09D123/22C09D109/10C09D123/08C09D131/04C09D123/16C09D123/28C09D123/34C09D7/12
Inventor 田凤兰段文锋栾斌常英
Owner BEIJING ORIENTAL YUHONG WATERPROOF TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka