Preparation method, product and use of modified vinylene chloride plastics

A polyvinyl chloride and polyvinyl chloride resin technology, applied in plastic/resin/wax insulators, organic insulators, conductors, etc., can solve the problems of poor toughness and poor temperature resistance, and achieve good compatibility and wear resistance. High and good thermal stability

Inactive Publication Date: 2011-08-03
LINOYA ELECTRONIC TECHNOLOGY CO LTD
View PDF10 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The blending and melting of PVC and various additives makes the blend have both polyester plasticizer and hydrogenated nitrile rubber temperature resistance, and solves the performance defects of poor toughness and poor temperature resistance of current PVC materials. By adding flame retardant And antioxidants and other additives to improve its flame retardant performance and anti-aging performance, especially the technical difficulties in the application of wire coating materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method, product and use of modified vinylene chloride plastics
  • Preparation method, product and use of modified vinylene chloride plastics

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] The present embodiment provides a kind of preparation method of modified polyvinyl chloride plastic, it comprises the following steps:

[0046] (1) Weighing raw materials: Weigh 60g of polyvinyl chloride resin powder, 27g of plasticizer, 5.7g of hydrogenated nitrile rubber, 4.3g of stabilizer (paraffin-calcium stearate), flame retardant (polyethylene wax and polytetrafluoroethylene Vinyl fluoride) 1.3g, lubricant (Sb 2 o 3 , Mg(OH) 2 )1.7g;

[0047] (2) Ingredients mixing: Add polyvinyl chloride resin powder into the mixer, start the mixer to preheat, then add plasticizer and stabilizer, continue to heat up, mix, heat up to 85-90°C, and put in hydrogenated nitrile For rubber, stabilizer, flame retardant, lubricant, heat up to 100-135°C, set the speed of the mixer to 1300r / min, and carry out high-speed mixing to obtain the mixture;

[0048] (3) Extrusion molding: Put the mixed material described in step (2) into the hopper of the twin-screw extruder, inject it by the...

Embodiment 2

[0050] Embodiment 2 and implementation 3 provide modified polyvinyl chloride plastics, and its preparation process steps are basically the same as in Example 1, the difference being that the raw material component distribution ratio is shown in Table 1:

[0051] The raw material ratio of each embodiment of table 1

[0052] components

Example 1

Example 2

Example 3

PVC resin powder

60

57

62

plasticizer

27

28

25

Hydrogenated nitrile rubber

5.7

5.7

5.7

stabilizer

4.3

4.3

4.3

Flame Retardants and Lubricants

3

3

3

[0053] The modified polyvinyl chloride plastic obtained in the above embodiments of the present invention has the characteristics of high wear resistance and scratch resistance, high flame retardancy, anti-ultraviolet radiation, good thermal stability, soft hand feeling, and anti-sticking. After testing, its performance is shown in the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
melting pointaaaaaaaaaa
Login to view more

Abstract

The invention provides a preparation method of modified vinylene chloride plastics, which comprises the following steps: (1) weighing raw materials; (2) mixing prepared materials, namely adding polrvinyl chloride resin powder into a mixing mill, preheating, adding a plasticizer and a stabilizer, mixing to 85 to 90 DEG C, adding other aids, heating to 100 to 135 DEG C, and mixing at a high speed of 1,300r / min to obtain a mixed material; (3) performing extrusion forming, namely placing the mixed material in a double-screw extruder, initially melting, and plasticizing to obtain a completely plasticized material; and (4) granulating, air cooling, sieving, cooling and discharging products. In the method, the process is simple, the conditions are easy to control, and large-scale production is easy. In addition, the invention also provides modified vinylene chloride plastics, which have the characteristics of high wear resistance, high scraping resistance, high flame retardance, high ultraviolet resistance, soft handfeel, adhesion prevention, and the like, and can be used as coating materials for wires and cables.

Description

technical field [0001] The invention relates to the technical field of polymer material modification, in particular to a preparation method of a PVC modified material, the PVC modified material and its application to electric wires and cables. Background technique [0002] Engineering plastics have excellent performance and are also in line with the trend of energy conservation and environmental protection. In recent years, engineering plastics have been widely used in electronics, automobiles, construction, office equipment, machinery, aviation and other industries. It has become an international trend to replace steel with plastic. Engineering plastics has become the fastest growing field in the plastics industry in the world today. Its development not only supports the national pillar industries and modern high-tech industries, but also promotes the transformation of traditional industries and the adjustment of product structure. After 10 years of development, China's eng...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L15/00C08L67/00C08K5/12C08K3/22B29C47/92H01B3/44H01B7/295B29C48/92
CPCB29C48/0022B29C48/04B29C48/875B29C48/92B29C2948/92704B29C2948/92895
Inventor 李国峰
Owner LINOYA ELECTRONIC TECHNOLOGY CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap