Composite antibacterial far infrared medical stone porous ceramic ball and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of porous ceramic balls and compound antibacterial, which is applied in the field of compound antibacterial far-infrared medical stone porous ceramic balls, can solve the problem that the effect of far-infrared activated water is not obvious, achieves easy human health, long service life, and solves the problem of easy reunion. Effect
Inactive Publication Date: 2011-08-17
ZHEJIANG HAERS VACUUM CONTAINERS CO LTD
View PDF6 Cites 27 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0004] The water activation treatment in the prior art often uses natural tourmaline to introduce, so the effect of far-infrared activated water is not obvious. If the composite introduction of optimized high-temperature artificially synthesized far-infrared ceramic powder and natural tourmaline is used, the water activation treatment can be optimized.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0035] Porous ceramic balls are made of ceramic natural minerals composed of the following weights, high-temperature artificially synthesized silver-loaded analcime, and far-infrared materials, which are crushed, batched, pelletized, sintered, and washed by self-grinding water;
[0036] Lead-free and cadmium-free low-temperature solvent: silver-loaded analcite: nano-anatase TiO 2 : Artificial high-temperature synthetic far-infrared material: Natural tourmaline: Medical stone: Hole forming and normal temperature adhesive = 9kg: 9kg: 4.6kg: 9kg: 9kg: 43kg: 16.7kg;
[0037] Among them, lead-free and cadmium-free low-temperature solvents, nano-anatase TiO 2 , natural tourmaline, medical stone, pore forming and normal temperature adhesive (starch) are commercially available; silver-loaded analcite and artificial high-temperature synthetic far-infrared materials are products developed and produced by Zhejiang Hals Vacuum Vessel Co., Ltd.
[0038] The preparation method of the porou...
Embodiment 2
[0081] Porous ceramic balls are composed of ceramic natural minerals and high-temperature synthetic far-infrared materials, which are crushed, batched, pelletized, sintered, and self-grinding and washed with water;
[0082] Lead-free and cadmium-free low-temperature solvent: calcined analcime without introducing rare earth and silver elements: nano-anatase TiO 2 : Artificial high-temperature synthetic far-infrared material: natural tourmaline: medical stone: hole forming and normal temperature adhesive = 9kg: 9kg: 4.6kg: 9kg: 9kg: 43kg: 16.7kg;
[0083] Among them, lead-free and cadmium-free low-temperature solvents, nano-anatase TiO 2 , natural tourmaline, medical stone, analcime and pore-forming and room temperature adhesive (starch) are commercially available; artificial high-temperature synthetic far-infrared materials are products developed and produced by Zhejiang Hals Vacuum Vessel Co., Ltd.
[0084] The preparation method of the porous ceramic ball of the present inve...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
particle diameter
aaaaa
aaaaa
particle diameter
aaaaa
aaaaa
particle diameter
aaaaa
aaaaa
Login to view more
Abstract
The invention relates to a composite antibacterial far infrared medical stone porous ceramic ball. The surface of the porous ceramic ball is in the form of a closer porous sintered structure while the internal structure of the porous ceramic ball is three-dimensional communicated micropores which are uniformly distributed as a whole and are interlaced and connected with each other; the particle size of the porous ceramic ball is 10 microns to 5 millimeters; the volume density is 1.0-2.8 g / cm<3>; the porosity is 30-50%; the aperture size is 10-100 microns; and the compressive strength is 10-18 MPa. The porous ceramic ball is prepared from a ceramic natural mineral, a high temperature synthetic ceramic raw material and a pore-forming and binding material through the following processes of finely crushing, proportioning, pelletizing, sintering at low temperature, washing with water and drying, and the porous ceramic ball comprises the following components in parts by weight: 5-15 parts of lead-free and cadmium-free low temperature solvent, 5-15 parts of silver-loading analcite, 3-6 parts of nano-anatase TiO2 (Titanium Dioxide), 5-15 parts of high temperature synthetic far-infrared material, 5-15 parts of natural electric stone, 40-50 parts of medical stone and 10-20 parts of pore-forming and binding material. Because good whole sintering degree and a porous structure are remained and the surface of the porous ball is easy to grind, decontaminate and wash by adopting a self-created preparation process of uniformly dispersing the nano-TiO2 powder in the slurry without agglomeration, the porous ceramic ball has the advantages of strong regeneration capacity and long service life.
Description
technical field [0001] The invention relates to a composite antibacterial far-infrared medical stone porous ceramic ball, in particular, it is used as a functional adsorption and impregnation material in drinking water cups, water dispensers, and field water purifiers for purifying, antibacterial, and activating water. Applied porous ceramic ball and preparation method. Background technique [0002] In the water purification and mineralization treatment of the prior art, three types of materials are most commonly used: medical stone, activated carbon and ordinary porous ceramic balls. Commercially available medical stone products include medical stone "powder" with a fineness of 80-325 mesh and solid "medican stone balls" with a particle size of 0.1-9mm. The original medical stone powder has gradually withdrawn from the field of water purification and mineralization treatment, and has been replaced by solid medical stone balls. Activated carbon generally adopts granular ac...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more