Material for preparing porcelains

A ceramic wine bottle and component technology, which is applied in the production of ceramic materials, clay products, and other household appliances, etc., can solve the problems of low utilization rate of low-grade raw materials, waste of cultivated land area by clay, monotonous selection of raw materials, etc., and achieve impermeability Excellent, high molding efficiency, good fire resistance

Inactive Publication Date: 2011-09-07
内蒙古汇江陶瓷研究设计院 +2
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The existing ceramic production methods are relatively mature from the perspective of process technology, but in terms of raw material selection, traditional ceramic production uses feldspar, quartz, and clay as the main raw materials, and the selection of raw materials is relatively monotonous, and feldspar Excessive mining of mineral resources such as quartz and quartz will seriously damage the ecological environment, and the use of a large amount of clay will waste arable land
In addition, there are also defects in the selection of raw materials such as solid waste and low utilization rate of low-grade raw materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] Embodiment 1: a kind of material of making ceramic wine bottle, it is made up of the component of following weight fraction:

[0015] Desert Sand 40%

[0016] Clay 30%

[0017] Gangue 26%

[0018] Sodium metasilicate 4%

[0019] The sum of the percentages of the above components is 100%.

[0020] According to the formula of the above-mentioned materials for making ceramic wine bottles, the raw materials are weighed, crushed, ground, grouted, dried, fired at 1150°C, decals painted, and baked at 700°C to make packaged porcelain bottles .

Embodiment 2

[0021] Embodiment 2: a kind of material of making ceramic wine bottle, it is made up of the following components by weight:

[0022] Desert Sand 70%

[0023] Clay 15%

[0024] Calcined coal gangue 14.3%

[0025] Sodium tripolyphosphate 0.7%

[0026] The sum of the percentages of the above components is 100%.

[0027] According to the formula of the above-mentioned materials for making ceramic wine bottles, the raw materials are weighed, crushed, ground, grouted, dried, fired at 1170°C, decals painted, and baked at 750°C to make packaged porcelain bottles .

Embodiment 3

[0028] Embodiment 3: a kind of material of making ceramic wine bottle, it is made up of the component of following weight fraction:

[0029] Desert Sand 53%

[0030] Clay 23%

[0031] Gangue 22%

[0032] Sodium tripolyphosphate 2%

[0033] The sum of the percentages of the above components is 100%.

[0034] According to the formula of the above-mentioned materials for making ceramic wine bottles, the raw materials are weighed, crushed, ground, grouted, dried, fired at 1160°C, decals painted, and baked at 720°C to make packaged porcelain bottles .

[0035] There is no national standard or industry standard for packaging porcelain bottles, and the appearance and shape are determined through negotiation between the supplier and the buyer. Generally, it is required to have uniform appearance size, uniform capacity, and no leakage. The ceramic wine bottle products obtained in Examples 1-3 can all meet the requirements of uniform appearance size, uniform capacity, and no leakag...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a material for preparing ceramic winebottles. The material comprises the following components by weight percent: 40%-75% of desert sand, 15%-30% of clay, 12%-33% of coal gangue and 0.8%-4% of sodium metasilicate, wherein the sum of the weight percentages of the components is 100%. The invention has the following advantages: desert sand is used as a main raw material, a good low-cost method for treating desert is provided; compared with the traditional formula, the formula provide by the invention has the advantages that the product cost is greatly reduced; the product has gentle color, excellent impermeability and high strength; and the quality of the product meets the national standards of the related product.

Description

technical field [0001] The invention relates to a material for making ceramic wine bottles, in particular to a material for making porcelain with desert sand as the main component. Background technique [0002] China is one of the countries seriously endangered by land desertification. At present, my country's land desertification is still showing an increasing trend. Land desertification is not only a major ecological environment problem, but also a very serious social and economic sustainable development problem that our country is facing. my country's desert and desertification land area is about 1.607 million square kilometers, accounting for 16.7% of the country's land area. At present, the area of ​​desertified land in my country is expanding at a rate of 2,460 square kilometers per year, and there is a trend of accelerating expansion. If the existing desert sand can be developed and utilized on the basis of controlling desert expansion, the unity of ecological benef...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/132
CPCY02P40/60
Inventor 马东升杨卫江
Owner 内蒙古汇江陶瓷研究设计院
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap