Ancient blue and white porcelain and production method thereof

A production method and technology for cultural porcelain, applied in the field of daily-use ceramics, can solve the problems of insufficiently bright and smooth glaze, low-grade ceramic products, and few varieties of product colors, and achieve the effects of simple and elegant color, rich and colorful colors, and smooth hand feel.

Active Publication Date: 2011-11-23
GUANGXI NANSHAN PORCELAIN
View PDF5 Cites 26 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, except for a few enterprises, the celadon products produced by most celadon manufacturers are not uniform in color, the color is not bright enough, the glaze is not bright enough, the product design and color are few, and the grade

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ancient blue and white porcelain and production method thereof
  • Ancient blue and white porcelain and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0022] In the following, the present invention will be described in detail by taking an ancient celadon culture porcelain bowl whose surface pattern is a sage figure of Confucianism as an example.

[0023] In the ancient celadon culture porcelain bowl, the raw material weight percentage composition of the green body ingredients is 95.5% of the green body base material and 4.5% of the color material.

[0024] In the ancient celadon culture porcelain bowl, the raw material weight percentage composition of the green body base material ingredients is: feldspar sand 48%, high white clay 23%, clay 9%, and kaolin 20%.

[0025] In the ancient celadon culture porcelain bowl, the raw material weight percentage composition of the color material ingredients is: cobalt black 6%, fruit green 7%, chrome green 9%, mineralizer 78%.

[0026] In the ancient celadon culture porcelain bowl, the raw material weight percentage composition of the enamel ingredients is: feldspar 37%, quartz 22%, talc 11%, lime...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to ancient blue and white porcelain and a production method thereof. The ancient blue and white porcelain comprises a blank body ingredient and a porcelain glaze ingredient. The production method comprises the following steps of: manufacturing a blank body, coloring matters, porcelain glaze, stained paper and applique decoration liquid; mixing a blank substrate with the coloring matters to obtain the blank body ingredient; adding an appropriate amount of water for performing ball milling; and performing iron sieving, clay squeezing, crude refining, ageing, refining, rolling molding, drying, blank trimming, line drawing, glaze applying, stained paper attaching, baking and drawing to obtain a finished product. Due to the adoption of the production method, the principle of color development from body glaze in the conventional celadon color tone is changed, part of color development pigment is added into the blank body substrate to obtain the blank body, stained paper with various historical character miracles or pictures and texts is attached to a glaze layer, the ancient blue and white porcelain obtained by one-step baking at high temperature has the advantages of stable blue tone, abundant colors, shining and smooth appearance, simple and elegant color and luster, high strength, high thermal stability, extremely small dissolved quantity of lead and cadmium, smoothness and light transmittance, safety and sanitation. The preparation method is scientific and reasonable and is suitable for mass production.

Description

Technical field [0001] The invention belongs to the technical field of daily ceramics, and relates to a ceramic product and a production method thereof, in particular to an ancient celadon cultural porcelain and a production method thereof. Background technique [0002] Celadon is one of the famous traditional porcelains in China. Celadon is famous for its delicate porcelain, bright and smooth lines, dignified and simple shapes, and pure and colorful colors. Celadon not only includes blue and green, but also has different shades in terms of quality. This is due to the thickness and difference of the glaze layer, which presents different tones after firing. Cyan comes from glaze green, so it is called "green glazeware". Celadon ware is a high-temperature color glaze variety with iron as the coloring agent. Its technological feature is to apply green glaze (iron as the coloring agent) on the body. Cyan glaze), fired in a reducing flame. The formation of celadon hue is mainly cau...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B35/18C04B35/622
Inventor 钟民东杨家森覃克灿龚镇飞
Owner GUANGXI NANSHAN PORCELAIN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products