Rubber cladding layer for cylinder and preparation method thereof

A rubber coating, roller technology, applied in transportation and packaging, conveyor objects, rollers, etc., can solve the problem of unsolved rollers, etc., and achieve the effect of high promotion and application value

Inactive Publication Date: 2012-04-11
ANHUI SHENGYUN RUBBER
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Although the above technologies can solve certain problems and improve the drum in terms of anti-corrosion, anti-rust, wear resistance, impact resistance, aging resistance, and tear resistance, the

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rubber cladding layer for cylinder and preparation method thereof
  • Rubber cladding layer for cylinder and preparation method thereof
  • Rubber cladding layer for cylinder and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

experiment example 1～6

[0029] The rubber coating layer material of the rollers in Experimental Examples 1 to 6 is rubber compound mainly composed of SBR, including SBR, vulcanizing agent, accelerator, active agent, reinforcing agent, plasticizer softener, anti-aging agent and Special compounding agent; the concrete components and consumption of experimental example 1~6 are as shown in table 1.

[0030] Components and consumption (kg) of table 1 embodiment 1~6

[0031]

[0032]

[0033] like figure 1 As shown, using the above-mentioned rubber coating layer material to prepare the roller rubber coating layer includes the following steps:

[0034] A. When using styrene-butadiene rubber as the main material to prepare the rubber compound for the acid and alkali-resistant rubber coating layer of the roller, firstly pretreat the material, and then plasticize the styrene-butadiene rubber on the open mill at 16 o'clock, and the roller temperature is 20-40 °C , Roll distance 1mm, thin pass method, af...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a rubber cladding layer for cylinder and preparation method thereof, wherein the outer side of the roller core of the cylinder is covered with a rubber cladding layer; the rubber cladding layer comprises the following components based on parts by weight: 100 parts of styrene butadiene rubber, 3-5 parts of vulcanizer, 0.45-1.5 parts of accelerator, 6-10 parts of activator, 30-70 parts of reinforcing agent, 10-30 parts of plasticized softener, 3-5 parts of antiager and 20-40 parts of special compounding ingredient. The preparation method comprises preparation of rubber, processing on the roller core, shaping and vulcanizing. In comparison with the existing technology, the acid-base proof rubber cladding layer is prepared by new formula materials and can keep the original physical performance after a long time stay in the acid-base bath lotion such that the cylinder of a conveyor can be used in acid-base and chemicals environment for a long time.

Description

technical field [0001] The invention relates to the technical field of conveyors, in particular to a rubber coating layer of a roller and a preparation method thereof. Background technique [0002] The rubber coating layer of the existing ordinary rollers cannot work in chemicals such as acid, alkali, and salt solution. When the rubber coating layer of ordinary rollers is in contact with acid, alkali, and salt solution, it will cause corrosion, cause rubber swelling, and produce rubber molecules. Fracture, depolymerization, and decomposition and dissolution of compounding agents lead to a significant decrease in its mechanical strength and physical properties, and the rubber layer gradually becomes sticky, oxidized, hardened, embrittled, cracked, etc., and cracks occur due to the attack of ozone. So that the corrosion completely loses the ability to work. [0003] With the continuous development of industrial production, the use of rollers is required to be more and more wi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L9/06C08K13/02B65G39/02B29B7/00B29C35/02
Inventor 詹莹青钟普查梅松桂
Owner ANHUI SHENGYUN RUBBER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap