Stainless steel material for blade of electric razor

An electric shaving, stainless steel technology, applied in the field of stainless steel materials, can solve the problems of corrosion resistance, wear resistance, inability to meet the strength, restrict the development of shavers, poor shaving sharpness, etc., and achieve better wear resistance. , The effect of improving tempering stability and improving strength requirements

Active Publication Date: 2014-03-12
SHANGHAI POVOS ELECTRIC WORKS
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For a long time, there is no special material suitable for razor blades in China. Domestic razor companies can only use martensitic stainless steel materials similar to SUS420J2 to make razor blades. Cracks are prone to appear in the middle, therefore, the use is limited
Moreover, its corrosion resistance, wear resistance, and strength cannot meet the quality requirements of high-speed moving razor knives, so the overall quality of domestic razors is not high, the shaving sharpness is poor, the sound quality is not good, and the service life is short. And other problems, seriously restricted the development of the shaver industry

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Stainless steel material for blade of electric razor
  • Stainless steel material for blade of electric razor
  • Stainless steel material for blade of electric razor

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0012] The present invention will be further elaborated below in conjunction with the accompanying drawings and specific embodiments. These examples should be understood as only for illustrating the present invention but not for limiting the protection scope of the present invention. After reading the contents of the present invention, those skilled in the art can make various changes or modifications to the present invention, and these equivalent changes and modifications also fall within the scope defined by the claims of the present invention.

[0013] The first preferred embodiment of the present invention uses conventional smelting methods or stainless steel SUS420J2 as the base material, melts it in an electric furnace, and uses electrolytic separation to remove material impurities to produce materials with the following alloy elements: C (carbon) 0.2%, Si (silicon) 1.00%, Mn (manganese) 1.50%, P (phosphorus) 0.04%, S (sulfur) 0.015%, Cr (chromium) 15%, Mo (molybdenum) 1...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
hardnessaaaaaaaaaa
hardnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a stainless steel material for a blade of an electric razor. Calculated in percentage by weight, the material comprises the following alloy element components: 0.15-0.2% of C (carbon), not more than 1.00% of Si (silicon), not more than 1.50% of Mn (manganese), not more than 0.04% of P (phosphorus), not more than 0.015% of S (sulfur), 13.50-15.50% of Cr (chromium), 0.80-1.30% of Mo (molybdenum), not more than 1.00% of Ni (nickel), 1.5-2.5% of Cu (copper) and the balance of Fe (iron). The hardness of the stainless steel material disclosed by the invention can achieve HV540-620 and be in line with the hardness requirement of the blade of the electric razor through three-stage heating quenching at the temperature of 400 DEG C, 850 DEG C and 1050 DEG C and tempering treatment at the temperature of 200 DEG C-400 DEG C. In addition, the material disclosed by the invention has the characteristics of high abrasion resistance, strong corrosion resistance, stable heat treatment property, excellent grinding processing performance and the like, the comprehensive performance of the material is better than that of a cutter material which is imported from abroad, and the material is suitable for production needs of large-batch domestic cutters and can get obvious economic benefits, so that the material is of an excellent new material for the blade of the electric razor.

Description

technical field [0001] The present invention relates to a stainless steel material for electric razor blades. Background technique [0002] The cutter head and knife net (collectively referred to as cutting tools) of the electric shaver are the core parts of the electric shaver. For a long time, there is no special material suitable for razor blades in China. Domestic razor companies can only use martensitic stainless steel materials similar to SUS420J2 to make razor blades. Cracks are prone to appear in the middle, so the use is limited. Moreover, its corrosion resistance, wear resistance, and strength cannot meet the quality requirements of high-speed moving razor knives, so the overall quality of domestic razors is not high, the shaving sharpness is poor, the sound quality is not good, and the service life is short. And other problems have seriously restricted the development of the shaver industry. Contents of the invention [0003] The technical problem to be solve...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/44C22C38/22C21D1/18
Inventor 刘伟明
Owner SHANGHAI POVOS ELECTRIC WORKS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com