Low-smoke-density PC/ABS (Poly Carbonate/Acrylonitrile Butadiene Styrene) plastic for automobile interior and preparation method thereof

A technology for automobile interior parts and smoke density, which is applied in the field of low smoke density PC/ABS alloy for automobile interior parts and its preparation, and can solve the problems of poor flame retardant performance of the alloy and the like

Active Publication Date: 2012-07-25
扬州诚森塑胶有限公司
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] However, the current PC / ABS alloy has poor flame retardancy

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-smoke-density PC/ABS (Poly Carbonate/Acrylonitrile Butadiene Styrene) plastic for automobile interior and preparation method thereof
  • Low-smoke-density PC/ABS (Poly Carbonate/Acrylonitrile Butadiene Styrene) plastic for automobile interior and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] According to the data corresponding to Example 1 in Table 1, four kinds of flame retardants such as decabromodiphenylethane, tris (2-chloropropyl) phosphate, melamine cyanurate and magnesium hydroxide are weighed, stirred and mixed evenly, and can be prepared Composite flame retardants.

[0031] Table 1: Composite flame retardant formula table Unit: kg

[0032] Example 1

Embodiment 2

[0034] According to the data corresponding to Example 2 in Table 1, four kinds of flame retardants such as decabromodiphenylethane, tris (2-chloropropyl) phosphate, melamine cyanurate and magnesium hydroxide are weighed, stirred and mixed evenly, and can be prepared Composite flame retardants.

Embodiment 3

[0036] According to the data corresponding to Example 3 in Table 1, four kinds of flame retardants such as decabromodiphenylethane, tris (2-chloropropyl) phosphate, melamine cyanurate and magnesium hydroxide are weighed, stirred and mixed evenly, and can be prepared Composite flame retardants.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses low-smoke-density PC / ABS (Poly Carbonate / Acrylonitrile Butadiene Styrene) plastic for an automobile interior and a preparation method thereof. The low-smoke-density PC / ABS plastic for the automobile interior comprises the following components in parts by weight: 50 parts of ABS resin, 40-60 parts of PC resin, 0.5-1.5 parts of polyfluortetraethylene, 5-10 parts of zinc borate, 1-3 parts of molybdenum trioxide, 2-6 parts of ammonium octamolybdate and 2-4 parts of zinc molybdate. The low-smoke-density PC / ABS plastic has excellent flame retardancy, particularly has lower smoke density, is used for suppressing smoke efficiently, and has excellent comprehensive performance. The low-smoke-density PC / ABS plastic for the automobile interior disclosed by the invention is particularly suitable for being molded into various automobile interiors by injecting.

Description

technical field [0001] The invention relates to a plastic material and a preparation method thereof, in particular to a low-smoke density PC / ABS alloy for automotive interior parts and a preparation method thereof. Background technique [0002] ABS resin (acrylonitrile-styrene-butadiene copolymer, ABS is the acronym for Acrylonitrile Butadiene Styrene) is a thermoplastic polymer material structure with high strength, good toughness and easy processing. [0003] ABS resin is a graft copolymer of three monomers of acrylonitrile, 1,3-butadiene and styrene. Its molecular formula can be written as (C 8 h 8 ·C 4 h 6 ·C 3 h 3 N) x , but in fact it is often a mixture of butadiene-containing graft copolymer and acrylonitrile-styrene copolymer, in which acrylonitrile accounts for 15-35%, butadiene accounts for 5-30%, and styrene accounts for 40- 60%, the most common ratio of emulsion method ABS is A:B:S=22:17:61, while the ratio of B in bulk method ABS is often lower, about 13...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L55/02C08L69/00C08L27/18C08K13/02C08K3/38C08K3/22C08K3/24C08K5/03C08K5/523C08K5/3492
Inventor 赵海应张荣福印玲
Owner 扬州诚森塑胶有限公司
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com