Ceramic coating material with 3D effect and coating method of ceramic coating material

A 3D effect, ceramic coating technology, used in magnetic coatings, coatings, household appliances, etc., can solve the problems of high temperature resistance, low hardness of silicone coating, single surface of tableware, etc., to achieve strong non-stick and wear resistance , The effect of small particle size distribution and high specific surface area

Inactive Publication Date: 2013-02-06
SHANGHAI EXCILON NEW MATERIALS
View PDF11 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The hard oxide layer has poor functionality, insufficient protection for the substrate, is not easy to clean, and is not strong in decoration; fluorocarbon coating, silicone coating has low hardness, poor scratch resistance, high temperature resistance, open flame resistance, and is easy to decompose and release There are toxic gases, which are harmful to human health, and most of them are solvent-based coatings, which cause great environmental pollution.
The surface of the existing tableware is single and rigid

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ceramic coating material with 3D effect and coating method of ceramic coating material
  • Ceramic coating material with 3D effect and coating method of ceramic coating material
  • Ceramic coating material with 3D effect and coating method of ceramic coating material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0059] A kind of coating method of the ceramic paint with 3D effect, its specific steps are:

[0060] One: Pattern design:

[0061] (1) Design graphics on the template or stretched sheet, and draw the positioning points with a pencil;

[0062] (2) The strong magnets are arranged in the same phase and pasted on the positioning point of the bottom plate with 502 glue;

[0063] (3) Correct the pattern arrangement distance of the magnetic blocks;

[0064] The pattern can be the company's trademark, or an animal pattern, or a personalized font, which can be changed according to actual needs.

[0065] 2. Proportion of ceramic coating: see Table 1-3;

[0066] three coating

[0067] (1) Substrate blasting and cleaning;

[0068] (2) The base material is preheated at 45-47°C;

[0069] (3) Spray primer with a film thickness of 20-23 μm;

[0070] (4) Place a magnetic block mold with a pattern on the base material, spray the magnetic paint, after the film thickness is 2-3 μm, immedi...

Embodiment 2

[0074] A kind of coating method of the ceramic paint with 3D effect, its specific steps are:

[0075] One: Pattern design:

[0076] (1) Design graphics on the template or stretched sheet, and draw the positioning points with a pencil;

[0077] (2) The strong magnets are arranged in the same phase and pasted on the positioning point of the bottom plate with 502 glue;

[0078] (3) Correct the pattern arrangement distance of the magnetic blocks;

[0079] The pattern can be the company's trademark, or an animal pattern, or a personalized font, which can be changed according to actual needs.

[0080] 2. Proportion of ceramic coating: see Table 1-3;

[0081] three coating

[0082] (1) Substrate blasting and cleaning;

[0083] (2) The base material is preheated at 46-48°C;

[0084] (3) Spray primer with a film thickness of 22-25 μm;

[0085] (4) Place a magnetic block mold with a pattern on the base material, spray the magnetic paint, after the film thickness is 2-3 μm, immediat...

Embodiment 3

[0089] A kind of coating method of the ceramic paint with 3D effect, its specific steps are:

[0090] One: Pattern design:

[0091] (1) Design graphics on the template or stretched sheet, and draw the positioning points with a pencil;

[0092] (2) The strong magnets are arranged in the same phase and pasted on the positioning point of the bottom plate with 502 glue;

[0093] (3) Correct the pattern arrangement distance of the magnetic blocks;

[0094] The pattern can be the company's trademark, or an animal pattern, or a personalized font, which can be changed according to actual needs.

[0095] 2. Proportion of ceramic coating: see Table 1-3;

[0096] three coating

[0097] (1) Substrate blasting and cleaning;

[0098] (2) The base material is preheated at 47-48°C;

[0099] (3) Spray primer with a film thickness of 24-26 μm;

[0100] (4) Place a magnetic block mold with a pattern on the base material, spray the magnetic paint, after the film thickness is 2-3 μm, immedi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to a ceramic coating material with 3D effect and a coating method of the ceramic coating material. The coating method specifically comprises the following steps of: 1, designing patterns; 2, proportioning ceramic coating material; and 3, preparing: (1) carrying out shot blasting and cleaning on base material; (2) preheating the base material to 45-50DEG C; (3) spraying priming paint, wherein the thickness of a film is 25-30mu m; (4) putting a magnetic block module with the patterns on the base material, spraying the magnetic powder coating material, wherein the thickness of the film is 2-3mu m, and immediately spraying finish paint, wherein the thickness of the film is 3-5mu m, directly putting the magnetic block module on a clamp before a bottom layer is sprayed so that the rotation speed of the clamp can be slightly slower than the conventional rotation speed, and the arrangement rule of the magnetic powder can not be influenced; (5) withdrawing the module after the finish paint is sprayed, and curing under low temperate, wherein the curing temperature is 80-100DEG C, and the curing time is 8-10minutes; and (6) cutting under high temperature, wherein the curing temperature is 240-280DEG C, and the curing time is 10-20minutes. The ceramic coating material with 3D effect has the advantages that simple to use is simple, low in cost is low, and better in decorative effect is good, patterns are controllable, 3D effect is vivid, and meets the requirement of market; and the coating layer is higher in non-stick property and abrasion resistance.

Description

【Technical field】 [0001] The invention relates to the technical field of high-performance coatings, in particular to a ceramic coating with 3D effects and a coating method thereof. 【Background technique】 [0002] Modern cooking utensils that integrate functionality and decoration are not only used as a convenient tool, but also can become a beautiful scenery in life. The outer surface of existing cooking utensils is mainly based on hard oxide layer, fluorocarbon coating, and organic silicon coating. The hard oxide layer has poor functionality, insufficient protection for the substrate, is not easy to clean, and is not strong in decoration; fluorocarbon coating, silicone coating has low hardness, poor scratch resistance, high temperature resistance, open flame resistance, and is easy to decompose and release There are toxic gases, which are harmful to human health, and most of them are solvent-based paints, which pollute the environment greatly. The surface of existing tabl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D1/00C09D5/23
CPCC04B41/52C04B41/009C04B41/89C04B2111/00422C04B2111/00965H01F41/16C04B33/00C04B2111/00491C04B41/4539C04B41/5025C04B41/4922C04B41/5089
Inventor 李力锋吴勇张磊陈科生
Owner SHANGHAI EXCILON NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap