Preparation method of imitated-metal enameled steel sheet

A technology of imitating metal and imitating metal powder, which is applied in the field of preparation of metal-imitating enamel steel plates, can solve the problems of unsuitable application and unsatisfactory appearance of enamel steel plates, and achieve excellent chemical stability, good mechanical properties, and easy cleaning and decontamination. Effect

Active Publication Date: 2013-07-24
ZHEJIANG KAIER NEW MATERIALS
View PDF6 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the appearance of traditional enamel steel plates is not beautiful enough, so it is not suitable for some special occasions

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of imitated-metal enameled steel sheet

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A method for preparing a metal-like enamel steel plate is characterized in that it comprises the following steps:

[0024] (1) Add suspending agent, water, sodium fluoroborate, urea, and potassium fluorosilicate to the transparent base glaze for ball milling to obtain glaze slurry, control the thickness of the glaze slurry at 0.2g / 100ml / 150 mesh, and the density of the glaze slurry at 165g / 100ml;

[0025] (2) Add imitation metal powder into the glaze slurry and mix evenly to obtain imitation metal enamel glaze;

[0026] The above-mentioned imitation metal enamel oil is sprayed on the biscuit with a spray gun to obtain an imitation metal enamel steel plate;

[0027] Place the above-mentioned imitation metal enamel steel plate at a temperature of 100°C and dry it for 20 minutes;

[0028] (3) Put the dried metal-like enamel steel plate into the firing furnace, and fire it at 800°C for 4 minutes.

[0029] The preparation method of the metal-like enamel steel plate, the ...

Embodiment 2

[0034] A method for preparing a metal-like enamel steel plate is characterized in that it comprises the following steps:

[0035] (1) Add suspending agent, water, sodium fluoroborate, urea, and potassium fluorosilicate to the transparent base glaze for ball milling to obtain glaze slurry, control the thickness of the glaze slurry at 0.3g / 100ml / 150 mesh, and the density of the glaze slurry at 170g / ml;

[0036] (2) Add imitation metal powder into the glaze slurry and mix evenly to obtain imitation metal enamel glaze;

[0037] The above-mentioned imitation metal enamel oil is sprayed on the biscuit with a spray gun to obtain an imitation metal enamel steel plate;

[0038] Place the above-mentioned imitation metal enamel steel plate at a temperature of 250°C and dry it for 60 minutes;

[0039] (3) Put the dried metal-like enamel steel plate into the firing furnace, and fire it at 860°C for 4.5 minutes.

[0040] In the preparation method of the metal-like enamel steel plate, th...

Embodiment 3

[0045] A method for preparing a metal-like enamel steel plate is characterized in that it comprises the following steps:

[0046] (1) Add suspending agent, water, sodium fluoroborate, urea, and potassium fluorosilicate to the transparent base glaze for ball milling to obtain glaze slurry, control the thickness of the glaze slurry at 0.25g / 100ml / 150 mesh, and the density of the glaze slurry at 168g / 100ml;

[0047] (2) Add imitation metal powder into the glaze slurry and mix evenly to obtain imitation metal enamel glaze;

[0048] The above-mentioned imitation metal enamel oil is sprayed on the biscuit with a spray gun to obtain an imitation metal enamel steel plate;

[0049] Place the above-mentioned imitation metal enamel steel plate at a temperature of 200°C, and dry it for 40 minutes;

[0050] (3) Put the dried metal-like enamel steel plate into the firing furnace, and fire it at 820°C for 5 minutes.

[0051] In the preparation method of the metal-like enamel steel plate,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a preparation method of an imitated-metal enameled steel sheet. The prepared enameled steel sheet has the advantages of good mechanical properties, good heat resistance, excellent chemical stability, clean and gorgeous appearance, and easy cleaning and decontamination. The enameled steel sheet is suitable to be used in decorative enamel of building interior and exterior wall decorations and decorative enamel of public places such as tunnels and subways. The enameled steel sheet has good imitated metal effect. A production process of the enameled steel sheet comprises the steps that: a suspending agent, water, sodium fluoroborate, urea, and potassium fluorosilicate are added into a transparent base glaze; ball milling is carried out, such that a glaze slurry is obtained; imitated-metal powder is added into the glaze slurry, and the mixture is well mixed, such that an imitated-metal enamel glaze is obtained; the imitated-metal enamel glaze is sprayed on a biscuit by using a spray gun; and the material is fired under a temperature of 800-860 DEG C, such that the imitated-metal enameled steel sheet is obtained.

Description

technical field [0001] The invention relates to a method for preparing a metal-like enamel steel plate. The prepared metal-like enamel steel plate has good mechanical properties, good heat resistance, excellent chemical stability, clean and gorgeous appearance, and is easy to clean and decontaminate. It is suitable for decoration of interior and exterior walls of buildings and decoration enamel of public places such as tunnels and subways. Background technique [0002] Enamel-coated products are also called post-coated products, which are products that provide functions such as corrosion resistance, chemical resistance, and weathering resistance by forming an enamel layer on the surface of a steel plate substrate, and improve the life of the steel plate. Compared with pre-coated products, enamel-coated products have disadvantages such as high manufacturing cost, but they have excellent quality in terms of hardness, weather resistance, washability, heat resistance and non-com...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C23D5/02C03C8/16
Inventor 顾金芳邢翰学江峰方淑玲杨理想王永刘鹤
Owner ZHEJIANG KAIER NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap