An acupuncture and 3D technology is applied in the field of the preparation of acupuncture 3D sound-absorbing bodies, which can solve the problems of incapable of environmental decoration, cleaning, complicated production process of sound-absorbing bodies, poor low-frequency sound-absorbing effect, etc., and achieves increased appearance effect and sound-absorbing performance. Improved, easy-to-install effect

Active Publication Date: 2015-10-28
JIANGSU BURGEREE NEW TECH MATERIALS
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Among them, the plate-shaped structure is the simplest and the most widely used; it has a good effect on high-frequency sound absorption, but the low-frequency sound absorption effect is not good; the function is single, and it cannot decorate the environment except for the incomplete sound absorption effect. , cleaning and other functions; in terms of construction, a large number of keels are needed as a support, which affects the sound absorption effect to varying degrees; the production process of the sound-absorbing body is complicated and requires multiple processes to complete

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of acupuncture 3D sound-absorbing body

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A method for preparing an acupuncture 3D sound-absorbing body, comprising the steps of:

[0033] (a) Weighing the first polyester staple fiber and the second polyester staple fiber at a mass ratio of 1:1;

[0034] (b) The weighed fiber enters the cotton rolling equipment for opening and mixing;

[0035] (c) The fiber processed by the rolling equipment is sent into the cotton mixing machine through the compression device, and the fiber is further mixed evenly;

[0036] (d) The fiber treated in step (c) enters the carding equipment, and forms a fiber web after opening;

[0037] (e) The fiber web enters the stacking equipment for stacking;

[0038] (f) After the piled fiber web is needled for the first time, a fiber cotton with a thickness of 25 mm is formed;

[0039] The needling density of the first needling is 1.6 needles / cm 2 ;

[0040] (g) Place a density of 200kg / m on the fiber cotton 3 cotton felt, and then perform the second needle punching to form needle pun...

Embodiment 2

[0049] A method for preparing an acupuncture 3D sound-absorbing body, comprising the steps of:

[0050] (a) weighing the first polyester staple fiber and the polyamide fiber at a mass ratio of 1:2;

[0051] (b) The weighed fiber enters the cotton rolling equipment for opening and mixing;

[0052] (c) The fiber processed by the rolling equipment is sent into the cotton mixing machine through the compression device, and the fiber is further mixed evenly;

[0053] (d) The fiber treated in step (c) enters the carding equipment, and forms a fiber web after opening;

[0054] (e) The fiber web enters the stacking equipment for stacking;

[0055] (f) After the piled fiber web is needled for the first time, a fiber cotton with a thickness of 30mm is formed;

[0056] The needling density of the first needling is 1.4 needles / cm 2 ;

[0057] (g) Place a density of 300kg / m on the fiber cotton 3 cotton felt, and then perform the second needle punching to form needle punched cotton fel...

Embodiment 3

[0066] A method for preparing an acupuncture 3D sound-absorbing body, comprising the steps of:

[0067] (a) weighing the first polyester staple fiber and the second polyester staple fiber at a mass ratio of 1:3;

[0068] (b) The weighed fiber enters the cotton rolling equipment for opening and mixing;

[0069] (c) The fiber processed by the rolling equipment is sent into the cotton mixing machine through the compression device, and the fiber is further mixed evenly;

[0070] (d) The fiber treated in step (c) enters the carding equipment, and forms a fiber web after opening;

[0071] (e) The fiber web enters the stacking equipment for stacking;

[0072] (f) The stacked fiber web is needled for the first time to form a fiber cotton with a thickness of 20mm;

[0073] The needling density of the first needling is 1.3 needles / cm 2 ;

[0074] (g) Place a density of 240kg / m on the fiber cotton 3 cotton felt, and then perform the second needle punching to form needle punched cot...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
melting pointaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to the preparation method of an acupuncturing 3D sound-absorbing body. The preparation method comprises the following steps:(a) weighting the first polyester staple fiber and fiber A respectively; (b) then entering into the cotton rolling equipment to carry out opening and mixing;(c) the fiber after processed by the cotton rolling equipment entering into a cotton mixing machine for further uniform mixing;(d) entering into the combing equipment and forming a fiber network after opening; (e) the fiber network entering into a stacking device for stacking;(f) forming cellucotton after first acupuncturing of the stacked fiber network; (g) placing a cotton blanket on the cellucotton, then carrying out the second acupuncturing to form into a acupuncturing cotton blanket;(h) cutting the acupuncturing cotton blanket into acupuncturing cotton blanket blocks by the cutting equipment; (i) enabling the acupuncturing cotton blanket blocks to enter into the heat setting equipment for heat setting; and(j) squeezing the acupuncturing cotton blanket blocks by a mould, so as to obtain the acupuncturing 3D sound-absorbing body. The 3D sound-absorbing body provided by the invention has the effects of sound absorption, noise reduction and decoration.

Description

technical field [0001] The invention relates to the field of building materials, in particular to a method for preparing an acupuncture 3D sound-absorbing body. Background technique [0002] When the existing sound-absorbing body is prepared, it is inevitable to use a binder, thereby introducing harmful substances. The patent application with the application number 200910071340.2 discloses "a fiberboard with self-absorbing formaldehyde function and its manufacturing method". The scheme uses wood fiber, aldehyde adhesive and activated carbon as the main raw materials; Activated carbon is spread on the wood fiber, and the fiber board can be made by hot pressing. Because this kind of fiberboard adopts aldehyde adhesive in the preparation process, and the aldehyde adhesive itself will release harmful gas, which is not environmentally friendly; moreover, the adsorption effect of this kind of fiberboard is not very ideal. [0003] At present, the sound-absorbing bodies on the ma...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D04H1/4382D04H1/46D06C7/02E04B1/84
Inventor 左百川相增辉
Owner JIANGSU BURGEREE NEW TECH MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products