Electrostatic flocking fabric made of alginate fiber and preparation method of electrostatic flocking fabric

A technology of seaweed fiber and electrostatic flocking, applied in chemical instruments and methods, cellulose plastic material layered products, devices for coating liquid on the surface, etc., can solve problems such as environmental pollution and poor environmental protection performance, and achieve cost reduction , Good flame retardancy, good high temperature resistance

Active Publication Date: 2013-11-27
山东领潮新材料有限公司
View PDF5 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Most of the flocking fibers currently used are chemical fiber materials, and natural fibers are rarely used as flocking materials. The environmental protection performance is poor, and it is easy to cause environmental pollution during the manufacturing process and later use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] An electrostatic flocking fabric of seaweed fiber, comprising a fluff layer, an adhesive layer and a base cloth layer, the fluff layer is seaweed fiber, the base cloth is aramid plain weave woven fabric, and the middle adhesive layer is silicone modified permanent epoxy glue. in:

[0025] The fluff layer is a blended fiber of seaweed fiber and one or more of viscose, cotton and chemical fiber.

[0026] The base fabric is an aramid plain weave fabric with a fabric density of 108×58 and a yarn fineness of 16tex.

[0027] The flame retardant performance of the seaweed fiber electrostatic flocking fabric meets the requirements of Class A in GB 8965 flame retardant clothing - flame retardant protection.

[0028] The above-mentioned manufacturing method of seaweed fiber electrostatic flocking fabric comprises the following steps:

[0029] a. The seaweed fiber tow is cut to make seaweed fiber fluff with a length of 1.0 mm and a fineness of 1.5 denier, and then conducting co...

Embodiment 2

[0035] An electrostatic flocking fabric of seaweed fiber, comprising a fluff layer, an adhesive layer and a base cloth layer, the fluff layer is seaweed fiber, the base cloth is aramid plain weave woven fabric, and the middle adhesive layer is silicone modified permanent epoxy glue. in:

[0036] The fluff layer is a blended fiber of seaweed fiber and one or more of viscose, cotton and chemical fiber.

[0037] The base fabric is an aramid plain weave fabric with a fabric density of 108×58 and a yarn fineness of 16tex.

[0038] The flame retardant performance of the seaweed fiber electrostatic flocking fabric meets the requirements of Class A in GB 8965 flame retardant clothing - flame retardant protection.

[0039] The above-mentioned manufacturing method of seaweed fiber electrostatic flocking fabric comprises the following steps:

[0040] a, the seaweed fiber tow is cut to make seaweed fiber fluff with a length of 1.2 mm and a fineness of 1.5 denier, and then conduct cond...

Embodiment 3

[0047] An electrostatic flocking fabric of seaweed fiber, comprising a fluff layer, an adhesive layer and a base cloth layer, the fluff layer is seaweed fiber, the base cloth is aramid plain weave woven fabric, and the middle adhesive layer is silicone modified permanent epoxy glue. in:

[0048] The fluff layer is a blended fiber of seaweed fiber and one or more of viscose, cotton and chemical fiber.

[0049] The base fabric is an aramid plain weave fabric with a fabric density of 108×58 and a yarn fineness of 16tex.

[0050] The flame retardant performance of the seaweed fiber electrostatic flocking fabric meets the requirements of Class A in GB 8965 flame retardant clothing - flame retardant protection.

[0051] The above-mentioned manufacturing method of seaweed fiber electrostatic flocking fabric comprises the following steps:

[0052] a. Cutting the seaweed fiber tow to make seaweed fiber fluff with a length of 1.0 mm and a fineness of 1.5 denier, and then conduct ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
lengthaaaaaaaaaa
lengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses electrostatic flocking fabric made of alginate fiber. The electrostatic flocking fabric comprises a flock layer, an adhesive layer and a base cloth layer, and is characterized in that the flock layer is the alginate fiber; the base cloth layer is aramid plain woven cloth; the middle adhesive layer is an organic silicon modified epoxy resin adhesive. The invention also discloses a preparation method of the electrostatic flocking fabric made of the alginate fiber. The preparation method is characterized by comprising the following steps of cutting alginate fiber strands into alginate fiber flock, and performing electric conduction and coloring treatment; pre-coating and mainly coating adhesives on flocking base cloth, wherein the total thickness of the adhesives is 0.2 to 0.25mm; performing flocking in an electrostatic flocking room to obtain flocked cloth; and performing baking to firmly composite the flock with the base cloth so as to obtain the electrostatic flocking fabric. The electrostatic flocking fabric has good flame resistance and is applicable to army combat uniforms, warship and submarine combat uniforms, bedding equipment, airman training combat uniforms, second artillery training combat uniforms and the like.

Description

technical field [0001] The invention relates to an electrostatic flocking fabric and a manufacturing method thereof, in particular to a special military seaweed fiber electrostatic flocking fabric and a manufacturing method thereof. . Background technique [0002] Most of the flocking fibers currently used are chemical fiber materials, and natural fibers are rarely used as flocking materials, which have poor environmental performance and are prone to environmental pollution during the manufacturing process and later use. Seaweed fiber has excellent characteristics of far infrared rays, negative ions, antibacterial, deodorant, and flame retardant, and has excellent high water absorption, easy removal, gel blocking, biocompatibility, degradable absorption, and environmental protection properties. The most excellent new fiber is used for special military natural flame retardant, anti-radiation, and far infrared. It is an excellent choice for special military use. Therefore, it...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B32B5/02B32B23/02B32B7/12B05D1/14
Inventor 赵丽
Owner 山东领潮新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap