Corrosion inhibitor for steel wire and preparation method thereof

A technology of anti-rust agent and steel wire, which is applied in the direction of anti-corrosion coating, coating, polyether coating, etc., can solve the problems of high cost, corrosion of steel wire, serious environmental pollution, etc., achieve good stability and maintain the original color effect

Active Publication Date: 2014-01-01
WUJIANG JUNDA ELEVATOR PARTS
View PDF5 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Most of the existing steel wire antirust agents are solvent-based, which have high cost, serious e...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Corrosion inhibitor for steel wire and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] A kind of antirust agent for steel wire, comprising by weight components: 20 parts of polyvinyl alcohol, 100030 parts of polyethylene glycol, 2 parts of ammonium benzoate, 3 parts of trisodium phosphate, 1 part of thiourea, and 2 parts of sodium thiosulfate , 1 part of triethanolamine, 1 part of undecanedibasic acid, 1 part of benzotriazole, 3 parts of citric acid, 1 part of sodium molybdate, 3 parts of tetrapropylammonium acetate, and 100 parts of water.

[0011] Add polyvinyl alcohol and polyethylene glycol into water, heat while stirring to dissolve completely, then add other components, keep stirring at 40°C, and cool to room temperature after complete dissolution.

Embodiment 2

[0013] A kind of antirust agent for steel wire, comprising by weight components: 30 parts of polyvinyl alcohol, 200040 parts of polyethylene glycol, 3 parts of ammonium benzoate, 3 parts of trisodium phosphate, 2 parts of thiourea, 3 parts of sodium thiosulfate , 2 parts of triethanolamine, 2 parts of undecanedibasic acid, 1 part of benzotriazole, 4 parts of citric acid, 1 part of sodium molybdate, 4 parts of tetrapropylammonium acetate, and 150 parts of water.

[0014] Add polyvinyl alcohol and polyethylene glycol into water, heat while stirring to dissolve completely, then add other components, keep stirring at 40°C, and cool to room temperature after complete dissolution.

Embodiment 3

[0016] A kind of antirust agent for steel wire, comprising by weight components: 38 parts of polyvinyl alcohol, 200050 parts of polyethylene glycol, 5 parts of ammonium benzoate, 4 parts of trisodium phosphate, 3 parts of thiourea, and 5 parts of sodium thiosulfate , 3 parts of triethanolamine, 4 parts of undecanedibasic acid, 3 parts of benzotriazole, 6 parts of citric acid, 2 parts of sodium molybdate, 5 parts of tetrapropylammonium acetate, and 200 parts of water.

[0017] Add polyvinyl alcohol and polyethylene glycol into water, heat while stirring to dissolve completely, then add other components, keep stirring at 40°C, and cool to room temperature after complete dissolution.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a corrosion inhibitor for a steel wire. The corrosion inhibitor comprises the following components in parts by weight: 20-50 parts of polyvinyl alcohol, 30-70 parts of polyethylene glycol, 2-7 parts of ammonium benzoate, 3-6 parts of trisodium phosphate, 1-5 parts of thiocarbamide, 2-8 parts of sodium thiosulfate, 1-5 parts of triethanolamine, 1-6 parts of undecanedioic acid, 1-4 parts of benzotriazole, 3-9 parts of citric acid, 1-4 parts of sodium molybdate, 3-7 parts of tetrapropyl ammonium acetate and 100-300 parts of water. The preparation method disclosed by the invention comprises the following steps: adding polyvinyl alcohol and polyethylene glycol to water, and heating while stirring, so as to completely dissolve polyvinyl alcohol and polyethylene glycol; then adding other components, and stirring at 40-60 DEG C in a heat-preservation manner; cooling to room temperature after completely dissolving. The corrosion inhibitor for the steel wire disclosed by the invention has the characteristics of being long in anti-rust time, good in anti-corrosion performance, low in cost, environment-friendly and the like.

Description

technical field [0001] The invention belongs to the technical field of metal surface treatment, and in particular relates to a steel wire antirust agent and a preparation method thereof. Background technique [0002] Steel wire is widely used in bridges, automobiles, electronics, power transmission and other industries. When preparing steel wire products, cleaning and antirust treatment of the material before processing is an important process in the production process. For high-tech products, the cleaning of steel wire materials And anti-rust treatment is the key process. The cleanliness and anti-rust treatment of steel wire materials are related to the performance, quality, service life and reliability of the product. Anti-rust treatment is very sensitive, and tiny pollution and rust spots will have a serious impact on product performance, quality, service life and reliability. Therefore, improving the cleanliness and antirust treatment effect of steel wire materials has...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D171/08C09D129/04C09D7/12C09D5/08C23F11/173
Inventor 平利中
Owner WUJIANG JUNDA ELEVATOR PARTS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap