Novel environment-friendly building brick and preparation method

A new type of technology for construction, applied in sustainable waste treatment, solid waste management, climate sustainability, etc., can solve problems such as occupation of land resources, hidden dangers of soil and groundwater safety, reduce combustion energy consumption, and achieve outstanding environmental protection effects , the effect of shortening the preparation time

Active Publication Date: 2014-03-26
山东环兴再生资源科技有限公司
View PDF3 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Slag is generally landfilled, which not only occupies land resources, but also brings potential safety hazards to soil and groundwater

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Novel environment-friendly building brick and preparation method
  • Novel environment-friendly building brick and preparation method
  • Novel environment-friendly building brick and preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0067] Environmentally friendly new building bricks, consisting of the following components by weight:

[0068] Portland cement: 3 parts

[0069] Gypsum: 5 parts

[0070] GCY Activator: 1 part

[0071] MSZ168-C additive: 10 parts

[0072] Coarse slag (5-15mm): 40 parts

[0073] Fine slag (2mm-4mm): 20 parts

[0074] Magnetized water: 3 parts

[0075] The method for environmental protection novel building brick, comprises the steps:

[0076] (1) Slag treatment

[0077] a. The slag discharged from the waste incineration power plant is washed by the hydrolysis tank to remove the soluble salt;

[0078] b. Crushing and screening to adjust the size distribution of slag particles;

[0079] c. Magnetic separation to remove iron;

[0080] d. Carry out buoyancy sorting to remove remaining non-ferrous metals;

[0081] e. Screen 3-15mm granules for later use, and 3mm and less granules and water roll milling, stirring, aging, and later use;

[0082] (2) Raw material ratio and mi...

Embodiment 2

[0090] Environmentally friendly new building bricks, consisting of the following components by weight:

[0091] Portland cement: 8 parts

[0092] Gypsum: 10 parts

[0093] GCY activator: 5 parts

[0094] MSZ168-C additive: 20 parts

[0095] Coarse slag (5-15mm): 50 parts

[0096] Fine slag (2mm-4mm): 30 parts

[0097] Magnetized water: 8 parts;

[0098] The method for environmental protection novel building brick, comprises the steps:

[0099] (1) Slag treatment

[0100] a. The slag discharged from the waste incineration power plant is washed by the hydrolysis tank to remove the soluble salt;

[0101] b. Crushing and screening to adjust the size distribution of slag particles;

[0102] c. Magnetic separation to remove iron;

[0103] d. Carry out buoyancy sorting to remove remaining non-ferrous metals;

[0104] e. Screen 3-15mm granules for later use, and 3mm and less granules and water roll milling, stirring, aging, and later use;

[0105] (2) Raw material ratio and...

Embodiment 3

[0113] Environmentally friendly new building bricks, consisting of the following components by weight:

[0114] Portland cement: 5 parts

[0115] Plaster: 7 parts

[0116] GCY activator: 2.5 parts

[0117] MSZ168-C additive: 15 parts

[0118] Coarse slag (5-15mm): 45 parts

[0119] Fine slag (2mm-4mm): 25 parts

[0120] Magnetized water: 5 parts;

[0121] The method for environmental protection novel building brick, comprises the steps:

[0122] (1) Slag treatment

[0123] a. The slag discharged from the waste incineration power plant is washed by the hydrolysis tank to remove the soluble salt;

[0124] b. Crushing and screening to adjust the size distribution of slag particles;

[0125] c. Magnetic separation to remove iron;

[0126] d. Carry out buoyancy sorting to remove remaining non-ferrous metals;

[0127] e. Screen 3-15mm particles for later use, 3mm and less than 3mm particles;

[0128] (2) Raw material ratio and mixing

[0129] a. Using a magnetizer to ma...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
water absorptionaaaaaaaaaa
Login to View More

Abstract

The invention relates to a novel environment-friendly building brick and a preparation method, and belongs to the technical field of waste disposal. The building brick comprises silicate cement, gypsum, a GCY activating agent, an MSZ168-C additive, coarse slag, fine slag and magnetized water. The preparation method comprises steps as follows: firstly, slag discharged by a slag waste incineration power plant is subjected to a series of pretreatment of hydrolytic tank washing, crushing screening, magnetic separation, flotation separation and screening of 3-15 cm particles, the slag and the MSZ168-C additive are added into an agitation tank by using a forced mixer according to a set proportion, the GCY activating agent is diluted in the magnetized water magnetized by a magnetizer, the mixture and cement are jointly added for agitation, and maintenance is performed after compression molding, so that a finished product is obtained. According to the novel environment-friendly building brick and the preparation method, the slag is prepared into a mold brick without firing, the preparation time is shortened, the burning energy consumption is reduced, emission of harmful gas in a burning process is avoided, and the environment protection effect is remarkable; and the manufactured brick is high in strength, light in weight and good in thermal insulation property, and the requirement for light mass, energy conservation and thermal insulation of wall materials of a modern building can be met.

Description

technical field [0001] The invention relates to a building brick, in particular to an environmentally friendly brick produced by using slag produced by burning garbage and a preparation method thereof, belonging to the technical field of waste treatment. Background technique [0002] As the basic construction continues to heat up, the demand for building bricks is also increasing. The existing brick-making technology is to use clay to burn bricks, and clay to burn bricks will cause a lot of damage to basic farmland. Therefore, using the principle of waste reuse, it has become a top priority to produce energy-saving and waste-friendly environmentally friendly bricks. [0003] A certain amount of slag will be produced after incineration of garbage in the domestic garbage incinerator, and the amount of slag produced by the grate furnace is about 20% of the weight of the garbage. Slag is generally landfilled, which not only occupies land resources, but also brings potential saf...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B18/10
CPCY02W30/91
Inventor 顾振清顾钊宇
Owner 山东环兴再生资源科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com