Low-brittleness 750MPa-level automobile beam steel and manufacturing method thereof

An automobile frame, low brittleness technology, applied in the field of metallurgy, can solve the problems of low strength of steel and cannot meet the requirements of environmental protection regulations, etc., and achieve the effects of good formability, good low temperature toughness and high strength

Active Publication Date: 2014-06-11
武汉钢铁有限公司
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This type of steel has low strength and cannot meet the requirements of modern heavy-duty commercial vehicle manufacturers for high-strength steel thinning to meet increasingly stringent environmental protection regulations.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-brittleness 750MPa-level automobile beam steel and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0050] According to the specific chemical composition shown in Table 1, the low-brittleness 750MPa grade hot-rolled steel for automobile frame was prepared. The preparation process is as follows:

[0051] Top-bottom compound blowing is carried out on 90-ton and 250-ton converters in steelmaking plants, and hot metal desulfurization technology is adopted to make S in hot metal ≤ 0.005%; ferroalloy is added when 1 / 3 of the steel is tapped after the furnace, and 2 / 3 of the steel is tapped After the addition is complete, the alloying sequence is: Al-Fe → Ferro-Manganese → Ferro-Niobium → Ferro-Molybdenum. Use an aluminum adding machine to add aluminum wires for final deoxidation, add titanium during vacuum treatment, and fine-tune the composition so that the chemical composition in the steel meets According to the requirements of Table 1, the balance is Fe and unavoidable inclusions; then pour the molten steel with the composition shown in Table 1 into a slab with a cross-section ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses low-brittleness 750MPa-level automobile beam steel and a manufacturing method thereof. The low-brittleness 750MPa-level automobile beam steel comprises the following chemical components in percentage by mass: 0.04-0.06% of C, less than 0.1% of Si, 1.6-1.85% of Mn, less than 0.012% of P, less than 0.005% of S, 0.020-0.070% of Al, 0.04-0.06% of Nb, 0.08-0.1% of Ti, 0.08-0.14% of Mo, less than 0.005% of N and the balance of iron and unavoidable impurities. A hot continuous rolling process comprises the steps of heating a continuous cast slab to 1,250-1,300 DEG C within 200-300 minutes, and performing rough rolling; after the rough rolling, controlling the temperature at 1,040-1,140 DEG C, and performing finish rolling, wherein the finish rolling temperature is 780-880 DEG C. The low-brittleness 750MPa-level automobile beam steel disclosed by the invention has high strength, and the weight reducing effect can reach 10-25% in frame design; with good formability, the low-brittleness 750MPa-level automobile beam steel is suitable for the processes of stamping, rolling, bending and the like; with low-temperature toughness, the low-brittleness 750MPa-level automobile beam steel is suitable for the transportation in cold regions.

Description

technical field [0001] The invention belongs to the technical field of metallurgy and relates to a steel for automobile longitudinal beams, in particular to a low-brittleness 750MPa grade steel for automobile beams and a manufacturing method thereof. Background technique [0002] Reducing the weight of the vehicle body by increasing the strength of the steel plate, reducing consumption, saving energy, and reducing environmental pollution are important topics in the research of today's automobile industry. At home and abroad, at this stage, some microalloying elements are mostly used to strengthen the strength of steel. Girder steel, as a safe load-bearing part of passenger and freight vehicles, has high requirements on performance and formability. All domestic steel mills are carrying out research work in related fields. However, the alloying elements, dosage, and process used are different, and are related to the equipment, technology, and raw materials of each factory. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/14C21D8/02
Inventor 赵江涛刘斌刘永前周祖安周一中桂洲张扬徐浩杨海林
Owner 武汉钢铁有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap