Filling material and ground-repairing method

A technology of filling materials and mass parts, which is applied in the direction of infrastructure repair, soil conditioning materials, chemical instruments and methods, etc., can solve the problems of large quantity and rising cost, so as to slow down the hardening speed, reduce the total cost, and reduce failures The effect that occurs

Inactive Publication Date: 2014-07-09
JFE STEEL CORP
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0011] Compared with the prior art, the technology of Patent Document 1 can obtain lightweight foam filling material at a low cost, but at 1 m 3 The average amount of medium cement is about 100kg, and the amount is large, so there is a problem of cost increase

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Filling material and ground-repairing method
  • Filling material and ground-repairing method
  • Filling material and ground-repairing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0078] Next, the effects of the present invention will be described using examples and comparative examples, but this example is only an example for explaining the present invention and does not limit the present invention.

[0079]

[0080] Filling materials were produced in the formulation shown in Table 1.

[0081] In addition, with regard to the mixed granulated slag, the throughput of 1mm particle diameter is 50% or more, and the maximum particle diameter is 9.5mm, which has figure 2 The cumulative particle size curve is shown. In addition, blast furnace type B was used for the blast furnace cement.

[0082]

[0083]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

Provided are a filling material, which can be manufactured at low cost and has excellent flowability / pumpability and appropriate strength as well as a ground-repairing method using the filling material. The filling material is characterized by comprising 2-10 parts by mass of cement, 30-100 parts by mass of water and 3-10 parts by mass of bentonite with respect to 100 parts by mass of iron and steel slag and in the gas bubble content being in the range of 10-40 volume%.

Description

technical field [0001] The present invention relates to a filling material that can be produced at low cost and has excellent fluidity, pressurized conveyability, and appropriate strength, and a foundation repair method using the filling material. Background technique [0002] Due to the consolidation subsidence of the foundation or the liquefaction accompanying the earthquake, the subsidence of the surface foundation and the subsidence of the road are caused, and a cavity (also called a void) appears between the foundation of the building and the foundation, resulting in the indoor concrete floor. There are problems such as cracks or collapse. [0003] As a method of solving the above-mentioned problems, use of fillers such as micro sand air mortar (micro sand air mortar) can be mentioned. However, regarding the filling material, it is desired to improve the following points: because cement (cement) hardens quickly, it is difficult to carry out pressurized transportation w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09K17/02C04B7/02C04B7/19C04B14/10C04B28/08C09K17/08C09K17/10C09K17/44E02D3/12E02D37/00C04B111/70C09K103/00
CPCC04B28/02C04B2111/00146C04B2111/00663C04B2111/00732C09K17/10E02D3/12Y02W30/91C04B14/104C04B18/142C04B18/144C04B38/0074
Inventor 林正宏林堂靖史中西克佳吉武英树筱原雅树
Owner JFE STEEL CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap