A method for optimizing paper structure and improving paper performance

A technology for improving structure and forming paper, which is applied in pulp beating method, pulp beating/refining method, papermaking, etc., to achieve the effect of improving paper performance and product quality

Active Publication Date: 2016-08-24
SHAANXI UNIV OF SCI & TECH
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, most of the current patents and literature reports focus on the use of various chemical additives or equipment improvement to improve paper performance, and there are few reports on improving paper performance by optimizing filler distribution.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for optimizing paper structure and improving paper performance
  • A method for optimizing paper structure and improving paper performance

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] The paper-forming filler content of present embodiment is 25%, comprises the following steps:

[0032] 1) Disintegration of pulp: fully disintegrate and dehydrate the chemical hardwood pulp to make a slurry with a final concentration of 10%;

[0033] 2) Refining: refining the prepared slurry, the refining concentration is 9%, and the final beating degree of the slurry after refining is 30°SR;

[0034] 3) Preparation of filler suspension: prepare calcium silicate filler suspension with a concentration of 10%, and fully stir and disperse;

[0035] 4) Papermaking of paper sheets: divide the slurry prepared in step 2) into three parts (upper, middle and lower layers), and dilute each part of the slurry to a concentration of 0.1%; The absolute dry mass ratio of the total amount of fibers in the slurry with a beating degree of 30°SR is 30:70, and the final paper-forming filler content meets the target paper-forming filler content of 25% by adding retention aids.

[0036] Ac...

Embodiment 2

[0041] The paper-forming filler content of present embodiment is 25%, comprises the following steps:

[0042] 1) Disintegration of pulp: fully disintegrate and dehydrate the chemical mechanical pulp to make a slurry with a final concentration of 12%;

[0043] 2) Refining: refining the prepared slurry, the refining concentration is 12%, and the final beating degree of the slurry after refining is 50°SR;

[0044] 3) Preparation of filler suspension: prepare a calcium carbonate filler suspension with a concentration of 15%, and fully stir and disperse;

[0045] 4) Papermaking of paper sheets: the prepared slurry in step 2) is divided into three parts (upper, middle and lower layers), and each part of the slurry is diluted to a concentration of 0.3%; The absolute dry mass ratio of the total amount of fibers in the slurry with a beating degree of 50°SR is 10:90, and the final paper-forming filler content meets the target paper-forming filler content of 25% by adding retention aid ...

Embodiment 3

[0048] The paper-forming filler content of present embodiment is 25%, comprises the following steps:

[0049] 1) Disintegration of pulp: fully disintegrate and dehydrate the chemical softwood pulp to make a slurry with a final concentration of 9%;

[0050] 2) Refining: refining the prepared slurry, the refining concentration is 9%, and the final beating degree of the slurry after refining is 28°SR;

[0051]3) Preparation of filler suspension: prepare calcium carbonate filler suspension with a concentration of 20%, and fully stir and disperse;

[0052] 4) Papermaking of paper sheets: the prepared slurry in step 2) is divided into three parts (upper, middle and lower layers), and each part of the slurry is diluted to a concentration of 0.3%; The absolute dry mass ratio of the total amount of fibers in the slurry with a beating degree of 50°SR is 40:60, and the final paper-forming filler content meets the target paper-forming filler content of 25% by adding retention aids.

[0...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for optimizing paper structure and improving paper-making performance, comprising: pulp disintegration, pulp refining, preparation of filler suspension and paper sheet making: during paper sheet making, three-layer paper sheets are laminated In the papermaking method, by adjusting the concentration factor Fc of the filler distribution in the paper, the purpose of improving the bulk, air permeability, physical strength and optical properties of the filled paper can be achieved when the filler content is fixed. By optimizing the filler distribution factor to improve paper performance, by adjusting the distribution of fillers in the paper structure, to maximize the advantages of fillers, so as to achieve the purpose of improving paper performance. The method of the invention is simple and easy to operate, and can regulate the performance of the target paper according to the needs. In a modern paper machine, by optimizing the concentration factor and adjusting the distribution of fillers, the purpose of improving paper performance can be achieved, thereby improving product quality.

Description

technical field [0001] The invention belongs to the technical field of papermaking, and in particular relates to a method for optimizing paper structure and improving paper-making performance. Background technique [0002] Adding fillers in the papermaking process can effectively improve the optical properties and printability of paper. On the other hand, since the cost of fillers is lower than that of fibers, the use of fillers is also beneficial to reduce production costs. For most paper mills, optimizing various properties of paper is mainly achieved by adding various chemical additives, such as strengthening agents, whitening agents, etc., to achieve the purpose of improving paper performance. Relevant studies have shown that changes in additive types, paper machine types, headbox and dehydration conditions have a greater impact on the distribution of fillers in paper sheets. This shows that the distribution of fillers in the paper can be regulated by various methods, s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D21D1/02D21D1/20D21H17/67D21H21/10
Inventor 宋顺喜张美云王建吴养育郝宁李琳
Owner SHAANXI UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap