Paper pulp and high-bulk energy-saving environment-friendly card prepared from same

A pulp and copper card technology, applied in the direction of synthetic cellulose/non-cellulose material pulp/paper, papermaking, paper coating, etc., can solve the problems of poor stability of pulp quality, pulp yellow, unfavorable high-quality stability requirements, etc., to achieve Avoid excessive input into production, reduce energy consumption for refining, and stabilize quality

Active Publication Date: 2012-07-04
GOLD HUASHENG PAPER SUZHOU IND PARK
View PDF8 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0012] The disadvantage of the above scheme is that the pulp is relatively yellow and the quality stability of the pulp is poor. It is only

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Paper pulp and high-bulk energy-saving environment-friendly card prepared from same
  • Paper pulp and high-bulk energy-saving environment-friendly card prepared from same
  • Paper pulp and high-bulk energy-saving environment-friendly card prepared from same

Examples

Experimental program
Comparison scheme
Effect test

Example

[0048] Example 1 and comparative examples 1A, 1B: copper card

[0049] 1. See Table 1 for raw materials and dosage: NBKP is bleached softwood kraft pulp (Canada freeness control 430±20ml), LBKP is bleached hardwood kraft pulp (Canada freeness control 400±20ml), and BCTMP is chemical heat Refiner mechanical pulp (Canada freeness control 250ml), APMP is alkaline hydrogen peroxide mechanical pulp (Canada freeness control 250ml).

[0050] 2. Preparation method:

[0051] 1) Preparation of base paper: Dilute the pulp with water to a slurry with a mass concentration of 5%, centrifuge it for 5 times, then refine the pulp, add chemicals and fillers, mix well, spray the mixture onto the forming wire, then dehydrate and dry , Apply sizing material on the surface, then dry, curl into paper, and make base paper. The dust point of the base paper is required to be ≤5ppm;

[0052] 2) Paint coating: According to the formula, the primer and top coating are applied thinly and evenly on the base paper b...

Example

[0058] Example 2 and Comparative Examples 2A, 2B: copper card

[0059] 1. The raw materials and dosage are shown in Table 2: The Canadian freeness of NBKP is controlled at 430±20ml, the Canadian freeness of LBKP is controlled at 400±20ml, the Canadian freeness of BCTMP is 350ml, and the Canadian freeness of APMP is 350ml.

[0060] 2. Preparation method:

[0061] 1) Preparation of base paper: Dilute the pulp with water to a slurry with a mass concentration of 10%, centrifuge for 4 times, then refining, add chemicals and fillers, mix well, spray the mixture onto the forming wire, then dehydrate and dry , Apply sizing material on the surface, then dry, curl into paper, and make base paper. The dust point of the base paper is required to be ≤5ppm;

[0062] 2) Paint coating: According to the formula, the primer and top coating are applied thinly and evenly on the base paper by the coater, then dried, rolled into a roll on the reel, and then sent to the super calender It is calendered and ...

Example

[0068] Example 3 and Comparative Examples 3A, 3B: copper card

[0069] 1. The raw materials are shown in Table 3: The Canadian freeness of NBKP is controlled at 430±20ml, the Canadian freeness of LBKP is controlled at 400±20ml, the Canadian freeness of BCTMP is 250ml, and the Canadian freeness of APMP is 250ml.

[0070] 2. Preparation method:

[0071] 1) Preparation of base paper: Dilute the pulp with water to a slurry with a mass concentration of 30%, remove iron wires and stones through 3 centrifugation, then refine the pulp, add chemicals and fillers, mix well, and spray the mixture onto the forming wire , Then dehydrate, dry, apply sizing material on the surface, then dry, curl into paper, and make base paper. The dust point of the base paper is required to be ≤5ppm;

[0072] 2) Paint coating: According to the formula, the primer and top coating are applied thinly and evenly on the base paper by the coater, then dried, rolled into a roll on the reel, and then sent to the super cal...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses paper pulp and a high-bulk energy-saving environment-friendly card prepared from the same. The paper pulp is prepared from the following components in percentage by weight: 1 to 10 percent of bleached sulfate softwood pulp, 30 to 70 percent of bleached sulfate hardwood pulp, 20 to 50 percent of chemithermomechanical pulp, and 10 to 30 percent of alkaline peroxide mechanical pulp. The invention also provides the copperplate card prepared from the paper pulp and other components. The paper made with the paper pulp is high in bulk, the gram weight of the paper is effectively controlled to be in a certain range, the paper pulp is prevented from being put into production excessively, and the defibrination energy consumption of a paper machine is reduced correspondingly, so that the effects of environment friendliness and energy saving are effectively achieved.

Description

technical field [0001] The invention relates to papermaking technology, in particular to a paper pulp and a high-bulk energy-saving and environment-friendly copper plate card prepared therefrom. Background technique [0002] Art Board is a high-grade printing cardboard made of base paper coated with white paint, and the weight is above 200gsm (inclusive). It is mainly used for printing the cover of high-grade books and periodicals, color pictures, various exquisite commodity advertisements, samples, commodity packaging, trademarks, etc. Art Board was once translated as art card (literal translation) in my country in the 1930s. Because when this kind of paper was used to print exquisite famous paintings in Europe, the printing plates corroded by copper plates were used for printing. Therefore, according to the convention of naming by purpose, the art paper used for copperplate printing is called copperplate (printing) card. In the printing industry in mainland China, colle...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D21H13/00D21H19/64D21H19/40D21H19/54
Inventor 陈汉彬李娟马开元施立才
Owner GOLD HUASHENG PAPER SUZHOU IND PARK
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka