A method of titanium metal modification with antibacterial properties and promoting osteoblast growth

A technology of osteoblasts and titanium metal, applied in the field of surface modification of biomedical materials, can solve the problems of antibiotic treatment, removal of implants, high infection rate, etc., achieve good biocompatibility, prevent coating from falling off, preparation method simple effect

Active Publication Date: 2015-12-30
陕西德健众普生物科技有限公司
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the infection rate of this type of surgery is high, which may lead to serious consequences such as heavy antibiotic treatment, removal of implants and even death

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method of titanium metal modification with antibacterial properties and promoting osteoblast growth
  • A method of titanium metal modification with antibacterial properties and promoting osteoblast growth
  • A method of titanium metal modification with antibacterial properties and promoting osteoblast growth

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Step 1, titanium metal pretreatment, ultrasonically treat titanium metal in 20ml 1mol / L acetone solution for 3 times, each time for 45 minutes, then put it into 30ml of nitric acid solution with a volume fraction of 40% and soak for 25 minutes, at a pressure of 0.3MPa , at a temperature of 80°C, and dried for 10 minutes to obtain pretreated titanium metal;

[0030] Step 2, coating preparation, soak the pretreated titanium metal in 50ml of 1mg / mL dopamine aqueous solution for 24 hours to obtain the coated titanium metal;

[0031] Step 3, the introduction of osteoblasts, get 2.5g of chitosan whose terminal group is carboxyl molecular weight and be dissolved in 50ml distilled water containing 0.5mmol acetic acid to obtain chitosan solution; get 0.2g epichlorohydrin and dissolve in 10ml ethanol to obtain epichlorohydrin solution; get 0.01g silver nitrate and dissolve it in 1ml distilled water to obtain silver nitrate solution, mix the three kinds of solutions to obtain a mi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a modification method of titanium metal having antibacterial property and capable of promoting the growth of osteoblast. The modification method comprises the following steps: pretreating titanium metal, preparing a mixed liquid which can be adhered on the surface of the titanium metal and contains a certain crosslinking space structure, wherein the mixed liquid contains silver nitrate with an antibacterial function; then adding osteoblast and the pretreated titanium metal, and performing vacuum drying to obtain titanium metal the coating of which is coated by osteoblast; and finally immersing into a pancreatin solution for 15-45 seconds, performing ultrasonic elution and vacuum drying to obtain modified medical titanium metal capable of promoting the growth of osteoblast. The method is simple, and mild in preparation conditions, no harmful substances are generated during preparation, the modified titanium metal can effective recognize osteoblast, promote the fast growth of the osteoblast on the surface of the titanium metal, and effectively inhibit the growth of bacteria; and after being implanted into a human body as an implant, the modified titanium metal is beneficial to fixed growth of osteoblast on the surface of the titanium metal.

Description

technical field [0001] The invention relates to the field of surface modification of biomedical materials, in particular to a method for modifying titanium metal which has antibacterial properties and promotes the growth of osteoblasts. Background technique [0002] With the development of medical technology, medical titanium metal is widely used as implant materials such as dental implants and bone implants in the treatment of dentition defects, bone loss and other diseases, and has played an important role in saving human lives. However, the infection rate of this type of operation is high, which may lead to serious consequences such as heavy antibiotic treatment, removal of implants and even death. There are two main reasons for the high incidence of implant-associated infection: the accumulation of bacterial plaque on the implant surface and the low resistance of the implant osseointegration interface. Therefore, there is a need to improve the antibacterial properties o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): A61L27/54A61L27/38A61L27/06
Inventor 李培源苏炜霍丽妮陈睿
Owner 陕西德健众普生物科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap