A kind of low dielectric constant microwave dielectric ceramic bain2zno5 and preparation method thereof

A technology of microwave dielectric ceramics and low dielectric constant, which is applied in the field of dielectric ceramic materials, can solve the problems of restricting the development of microwave dielectric ceramics and devices, the inability to meet practical application requirements, and excessive temperature coefficients, and meet the requirements of low-temperature co-firing Technology, large application value, small temperature coefficient effect

Inactive Publication Date: 2016-04-06
临泉县非凡装饰工程有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] Due to the three performance indicators of microwave dielectric ceramics (ε r with Q f and τ ? ) is a mutual restrictive relationship (see literature: The restrictive relationship between the dielectric properties of microwave dielectric ceramic materials, Zhu Jianhua, Liang Fei, Wang Xiaohong, Lu Wenzhong, Electronic Components and Materials, Issue 3, March 2005), satisfying three There are very few single-phase microwave dielectric ceramics with individual performance requirements, mainly because their resonant frequency temperature coefficient is usually too large or the quality factor is too low to meet the practical application requirements.
At present, most of the research on microwave dielectric ceramics is a summary of experience obtained through a large number of experiments, but there is no complete theory to explain the relationship between microstructure and dielectric properties. Predict the microwave dielectric properties such as its resonant frequency temperature coefficient and quality factor, explore and develop near-zero resonant frequency temperature coefficient (-10ppm / ℃≤τ ? ≤+10ppm / ℃) and a series of different dielectric constant microwave dielectric ceramics with higher quality factors are difficult problems that those skilled in the art have been eager to solve but have always been difficult to achieve, which largely limits the use of microwave dielectric ceramics and device development

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of low dielectric constant microwave dielectric ceramic bain2zno5 and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0018] Table 1 shows three specific examples of different sintering temperatures constituting the present invention and their microwave dielectric properties. The preparation method is as above, and the microwave dielectric performance is evaluated by the cylindrical dielectric resonator method.

[0019] The ceramic can be widely used in the manufacture of microwave devices such as various dielectric substrates, and can meet the technical needs of mobile communication and satellite communication systems.

[0020] Table 1:

[0021]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
quality factoraaaaaaaaaa
Login to View More

Abstract

The invention discloses temperature-stable type low-dielectric-constant microwave dielectric ceramic BaIn2ZnO5 and a preparation method thereof. The preparation method comprises the following steps: (1) weighing and blending original powder of BaCO3, In2O3 and ZnO of which the purity is 99.9% (percentage by weight) according to composition of BaIn2ZnO5; (2) performing wet ball-milling mixing on the raw materials obtained in the step (1) for 12 hours with distilled water as a ball milling medium, drying, and then pre-burning for 6 hours in a 1200 DEG C atmosphere; and (3) adding a bonding agent into the powder prepared in the step (2), pelleting, then performing press molding, and finally sintering for 4 hours in a 1250-1300 DEG C atmosphere, wherein the bonding agent is a polyvinyl alcohol solution with the mass concentration of 5%, and the added amount of polyvinyl alcohol accounts for 3% of the total mass of the powder. The ceramic prepared by the method disclosed by the invention is good in sintering property, the dielectric constant reaches 26.7-28.9, the quality factor Qf reaches 70000-95000 GHz, and the temperature coefficient of resonance frequency is small, so that the ceramic has great application values in industry.

Description

technical field [0001] The invention relates to a dielectric ceramic material, in particular to a dielectric ceramic material for manufacturing microwave components such as ceramic resonators and filters used in microwave frequencies and a preparation method thereof. Background technique [0002] Microwave dielectric ceramics refer to ceramics that are used as dielectric materials in circuits in the microwave frequency band (mainly UHF and SHF bands) and perform one or more functions. They are widely used as resonators, filters, and dielectric substrates in modern communications. Components such as chips and dielectric waveguide circuits are the key basic materials of modern communication technology. They have been used in portable mobile phones, car phones, cordless phones, TV satellite receivers and military radars. They are used in modern communication tools. It is playing an increasingly important role in the process of miniaturization and integration. [0003] Dielectr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/01C04B35/622
CPCC04B35/453C04B2235/3215C04B2235/3286
Inventor 罗昊李纯纯苏和平
Owner 临泉县非凡装饰工程有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products