A kind of heavy metal curing agent and curing method thereof

A technology of heavy metal and curing agent, applied in the field of environmental engineering, can solve the problems of unfavorable As fixation, easy leaching of Pb, no treatment method, etc., and achieves the effects of low manufacturing cost, wide source of raw materials, and reduced toxicity risk.

Active Publication Date: 2018-11-27
湖南瀚洋环保科技有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there is no effective treatment method for the compound pollution of Pb and As.
Because in the case of higher pH, it is conducive to the fixation of Pb, but not conducive to the fixation of As, conversely, in the case of lower pH, it is beneficial to the fixation of As and not conducive to the fixation of Pb; Pb is easy to leach at low pH

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] 1) Weigh 30% by weight of fly ash, 35% of lime, and 35% of peat. The peat is first calcined in a muffle furnace at a high temperature of 450°C for 4.5 hours, and then fully pulverized and mixed by a ball mill to obtain a heavy metal curing agent. ;

[0037] 2) Weigh 100g of Pb and As contaminated soil, add 10g of the above curing agent, stir evenly, add tap water with 40% (weight ratio) of the mixture, stir thoroughly for 10min, mix evenly, seal with film, and let stand for 15 days ;

[0038] 3) After 15 days, the cured body was leached by solid waste respectively. Toxic leaching method - acetic acid buffer solution method (HJ / T300-2007) to obtain the leachate, and the soil was measured by "Determination of Soil pH" (Agricultural Industry Standard NY / T 1377-2007) pH value.

[0039] After testing, the leaching concentration of Pb dropped from 34.1 mg / L before curing to 3.6mg / L after curing, which was lower than the detection value, and the leaching concentration of As ...

Embodiment 2

[0041] 1) Weigh 40% fly ash, 40% lime, and 20% peat. The peat is first calcined in a muffle furnace at a high temperature of 450°C for 4.5 hours, and then fully pulverized and mixed by a ball mill to obtain a heavy metal curing agent. ;

[0042] 2) Weigh 100g of Pb and As contaminated soil, add 10g of the above curing agent, stir evenly, add tap water with 40% (weight ratio) of the mixture, stir thoroughly for 10min, mix evenly, seal with film, and let stand for 15 days ;

[0043] 3) After 15 days, the cured body was leached by solid waste respectively. Toxic leaching method - acetic acid buffer solution method (HJ / T300-2007) to obtain the leachate, and the soil was measured by "Determination of Soil pH" (Agricultural Industry Standard NY / T 1377-2007) pH value.

[0044]After testing, the leaching concentration of Pb dropped from 34.8 mg / L before curing to 3.1 mg / L after curing, which was lower than the detection value, and the leaching concentration of As dropped from 21.5 m...

Embodiment 3

[0046] 1) Weigh 30% by weight of fly ash, 51% of lime, and 19% of peat. The peat is first calcined in a muffle furnace at a high temperature of 450°C for 4.5 hours, and then fully pulverized and mixed by a ball mill to obtain a heavy metal curing agent. ;

[0047] 2) Weigh 100g of Pb and As contaminated soil, add 10g of the above curing agent, stir evenly, add tap water with 40% (weight ratio) of the mixture, stir thoroughly for 10min, mix evenly, seal with film, and let stand for 15 days ;

[0048] 3) After 15 days, the cured body was leached by solid waste respectively. Toxic leaching method - acetic acid buffer solution method (HJ / T300-2007) to obtain the leachate, and the soil was measured by "Determination of Soil pH" (Agricultural Industry Standard NY / T 1377-2007) pH value.

[0049] After testing, the leaching concentration of Pb dropped from 33.6 mg / L before curing to 2.3 mg / L after curing, which was lower than the detection value, and the leaching concentration of As...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a curing agent and method for heavy metal and particularly discloses a curing agent for heavy metal in polluted soil. The curing agent is characterized by comprising the three components in percentage by weight: 30-40% of pulverized fuel ash, 35-51% of lime and 19-35% of peat. When the curing agent is used for treating the polluted soil, the curing method comprises the steps of sufficiently mixing the curing agent and heavy metal polluted soil according to the ratio of 1:10 (weight ratio); then, adding water accounting for 40% (weight ratio) of the mixture; and then, sufficiently stirring and mixing. The curing agent for heavy metal in polluted soil, disclosed by the invention, is prepared by taking natural minerals as raw materials, so that no secondary pollution is caused, the soil fertilizer efficiency can be effectively improved while the heavy metal is cured, and the technical problems that the pH value of the soil is remarkably changed and the soil is hardened in the existing chemical remediation method are solved.

Description

technical field [0001] The invention belongs to the technical field of environmental engineering, and in particular relates to a heavy metal curing agent and a usage method. Background technique [0002] Heavy metals generally refer to about 45 elements with a specific gravity above 5.0g / cm3. Big money in environmental pollution research [0003] The genus mainly refers to elements with significant biological toxicity such as Pb, Cd, Hg, Cr, and metalloid As, and also includes heavy metals such as Zn, Cu, Co, Ni, and Sn with certain toxicity. In recent years, the cadmium rice incidents that have occurred in China have aroused great concern from the party and the country. On February 18, 2011, the "Twelfth Five-Year Plan for Comprehensive Prevention and Control of Heavy Metal Pollution" was officially approved by the State Council and became the first approved "Twelfth Five-Year Plan". According to the requirements of the plan, the central government will invest in About 7...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09K17/40B09C1/08C09K101/00C09K103/00
CPCB09C1/08C09K17/40C09K2101/00
Inventor 孟涛
Owner 湖南瀚洋环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com