Medical far infrared hot compress patch for soft tissue repairing and preparation method thereof

A far-infrared and soft-tissue technology, applied to heating appliances for therapeutic treatment, phototherapy, contraceptives, etc., can solve problems such as uneven heating temperature, poor treatment effect of diseases, and short heating time, so as to achieve uniform heating and ensure uniformity Sexuality and persistence, the effect of increasing oxygen content

Inactive Publication Date: 2015-08-26
广西达庆生物科技有限公司
View PDF10 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the heating patch in the prior art has the problems of unbalanced heating temperature, too short heating time, and poor efficacy in treating diseases.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Medical far infrared hot compress patch for soft tissue repairing and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0067] A medical far-infrared hot compress for soft tissue repair, comprising a non-woven cloth bag, a heating layer arranged on the non-woven cloth bag and a pressure-sensitive adhesive tape for fixing the non-woven cloth bag, the heating layer is composed of the following raw materials in weight percentage:

[0068] Reduced iron powder 35%

[0069] Aluminum powder 0.1%

[0070] Far infrared ceramic powder 5%

[0071] Activated carbon 10%

[0072] Polymer absorbent resin 0.5%

[0073] Sodium chloride 1%

[0074] Purified water balance.

[0075] The reduced iron powder is a mixture of nano-scale reduced iron powder and micron-scale reduced iron powder with a weight ratio of 1:5, the particle diameter of the nano-scale reduced iron powder is 50 nanometers, and the particle size of the micron-scale reduced iron powder is 200 microns in diameter.

[0076] The aluminum powder is a mixture of nano-sized aluminum powder and micron-sized aluminum powder with a weight ratio of 1...

Embodiment 2

[0084] A medical far-infrared hot compress for soft tissue repair, comprising a non-woven cloth bag, a heating layer arranged on the non-woven cloth bag and a pressure-sensitive adhesive tape for fixing the non-woven cloth bag, the heating layer is composed of the following raw materials in weight percentage:

[0085] Reduced iron powder 35%

[0086] Aluminum powder 2%

[0087] Far infrared ceramic powder 12%

[0088] Activated carbon 13%

[0089] Polymer absorbent resin 1%

[0090] Sodium chloride 3%

[0091] Purified water balance.

[0092] The reduced iron powder is a mixture of nano-scale reduced iron powder and micron-scale reduced iron powder with a weight ratio of 1:6, the particle diameter of the nano-scale reduced iron powder is 180 nanometers, and the particle size of the micron-scale reduced iron powder is The diameter is 260 microns.

[0093] The aluminum powder is a mixture of nano-sized aluminum powder and micron-sized aluminum powder with a weight ratio of...

Embodiment 3

[0102] A medical far-infrared hot compress for soft tissue repair, comprising a non-woven cloth bag, a heating layer arranged on the non-woven cloth bag and a pressure-sensitive adhesive tape for fixing the non-woven cloth bag, the heating layer is composed of the following raw materials in weight percentage: The heat generating layer is composed of the following raw materials in weight percentage:

[0103] Reduced iron powder 40%

[0104] Aluminum powder 1%

[0105] Far infrared ceramic powder 10%

[0106] Activated carbon 13%

[0107] Polymer absorbent resin 1%

[0108]Sodium chloride 3%

[0109] Purified water balance.

[0110] The reduced iron powder is a mixture of nano-scale reduced iron powder and micron-scale reduced iron powder with a weight ratio of 1:9, the particle diameter of the nano-scale reduced iron powder is 150 nanometers, and the particle size of the micron-scale reduced iron powder is 340 microns in diameter.

[0111] The aluminum powder is a mixtur...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to medical compress patches, in particular to a medical far infrared hot compress patch for soft tissue repairing and a preparation method thereof. The medical far infrared hot compress patch comprises a non-woven fabric bag, a heating layer arranged at the non-woven fabric bag, and a pressure sensitive adhesive tape used for fixing the non-woven fabric bag; the heating layer is composed of 35-45% of reduced iron powder, 0.1-5% of aluminum powder, 5-15% of far infrared ceramic powder, 10-16% of active carbon, 0.5-2% of polymer water-absorbent resin, 1-6% of sodium chloride and rest of purified water by weight. By means of a thermal therapy and infrared therapy combination mode, the medical far infrared hot compress patch for the soft tissue repairing has physical therapy and therapy effects for the inflammation and indisposition due to rheumatic arthritis, cervical spondylosis, lumbar muscle degeneration, lumbar disc herniation, scapulohumeral periarthritis, soft tissue injury, hyperosteogeny, ischialgia, pain from rheumatism, knee injury, chronic prostatitis, chronic mastitis, hyperplasia of mammary glands, chronic gastroenteritis, chronic gynaecology inflammation, cold in uterus, stomach cold, pain from rheumatism and the like.

Description

technical field [0001] The invention relates to the technical field of medical application, in particular to a medical far-infrared thermal application for soft tissue repair and a preparation method thereof. Background technique [0002] Hot compresses, also known as heating stickers, have been introduced to China from Japan in the 1990s. After more than 20 years of development, heating stickers have been widely used in China. The reaction principle of heating stickers is to use primary batteries to speed up the oxidation reaction. Convert chemical energy into thermal energy. The heating patch is generally composed of a raw material layer, a gelatin layer and a non-woven bag. The raw material layer is placed in a non-woven bag, and the non-woven bag is made of a microporous air-permeable film. It must also have an airtight outer pocket. When in use, the outer bag is removed, and the inner bag, that is, the non-woven bag, is exposed to the air, and the oxygen in the air e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61F7/03A61N5/06
Inventor 梁奕福
Owner 广西达庆生物科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com