An anti-oxidation oil-absorbing drawing board

An oil-absorbing and anti-oxidation technology, which is applied in textiles, papermaking, and fiber processing, can solve problems affecting the preservation and collection of art works, easy drying of pigments, and yellowing of materials, so as to improve three-dimensionality, balance surface tension, and improve The effect of hardness

Active Publication Date: 2017-11-17
沭阳凤凰画材有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Ordinary drawing board oil paints are easy to dry and float on the surface of the canvas. After a long time, the material will turn yellow, become brittle, and crack, which will affect the preservation and collection of art works

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] An anti-oxidation oil-absorbing drawing board is characterized in that the preparation process of the drawing board is as follows:

[0015] 1. Preparation of clear slurry: Add 30 parts of yellow gum, 5 parts of chlorinated paraffin, and 60 parts of water into the reaction kettle, stir, and the stirring speed is 1800 rpm, and then spray coating on the surface of the substrate;

[0016] 2. Production of flour paste: Add 70 parts of quartz sand, 70 parts of marble powder, 150 parts of deionized water, stir at a stirring speed of 3000 rpm, then add 70 parts of acrylic resin, 20 parts of adhesive, and 5 parts of surfactant 70 parts of white glue and 70 parts of white glue are stirred and mixed, and the stirring speed is 2000 rpm / min to obtain the coating for flow coating. Using the technology of flow coating, the surface tension and speed are controlled to achieve the effect of no pinholes and improve the three-dimensional effect and hardness;

[0017] 3. Coat the surface of...

Embodiment 2

[0019] An anti-oxidation oil-absorbing drawing board is characterized in that the preparation process of the drawing board is as follows:

[0020] 1. Preparation of clear slurry: Add 40 parts of yellow glue, 10 parts of chlorinated paraffin, and 80 parts of water into the reaction kettle, stir at a stirring speed of 2000 rpm, and spray coating on the surface of the substrate;

[0021] 2. Production of flour paste: add 80 parts of quartz sand, 80 parts of marble powder, 200 parts of deionized water, stir at a stirring speed of 3500 rpm, then add 80 parts of acrylic resin, 30 parts of adhesive, and 10 parts of surfactant 80 parts, 80 parts of white glue are stirred and mixed, and the stirring speed is 2500 rpm / min to obtain the flow coating coating. Using the flow coating technology, the surface tension and speed are controlled to achieve the effect of no pinholes and improve the three-dimensional effect and hardness;

[0022] 3. Coat the surface of the substrate with clear glue...

Embodiment 3

[0024] An anti-oxidation oil-absorbing drawing board is characterized in that the preparation process of the drawing board is as follows:

[0025] 1. Preparation of clear slurry: Add 35 parts of yellow gum, 8 parts of chlorinated paraffin, and 70 parts of water into the reaction kettle, stir at a stirring speed of 1900 rpm, and then spray coating on the surface of the substrate;

[0026] 2. Production of flour paste: add 75 parts of quartz sand, 75 parts of marble powder, 175 parts of deionized water, stir at a stirring speed of 3250 rpm, then add 75 parts of acrylic resin, 25 parts of adhesive, and 8 parts of surfactant 75 parts of white glue are stirred and mixed, and the stirring speed is 2250 rpm / min to obtain the coating coating. The coating technology is used to control the surface tension and speed, so as to achieve the effect of no pinholes and improve the three-dimensional effect and hardness;

[0027] 3. Coat the surface of the substrate with clear glue layer and top...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

An antioxidant ink-absorbing sketchpad is prepared according to the preparation procedures that firstly, 30-40 parts of yellow gum, 5-10 parts of chlorinated paraffin and 60-80 parts of water are added into a reaction kettle and stirred, the rotation speed of stirring is 1800-2000 r / min, and clean paste is obtained and sprayed to the surface of a base material; secondly, 70-80 parts of quartz sand, 70-80 parts of marble powder and 150-200 parts of deionzed water are mixed and stirred, the stirring speed is 3000-3500 r / min, 70-80 parts of acrylate, 70-80 parts of white glue, 20-30 parts of an adhering agent and 5-10 parts of a surfactant are added, stirred and mixed, the rotation speed of stirring is 2000-2500 r / min, surface paste is obtained, the base material obtained in the first step is coated with the surface paste through the shower coating technology, and then drying is performed. The antioxidant ink-absorbing sketchpad has oxidization resistance and will not become yellow or fade, and paintings can be preserved for a long time; surface tension of the sketchpad is balanced, the sketchpad has the dull polish effect and is high in ink absorbing performance, and drying of the paintings is fast.

Description

technical field [0001] The invention relates to the technical field of drawing boards, in particular to an anti-oxidation oil-absorbing drawing board and a preparation method thereof. Background technique [0002] Ordinary drawing board oil paints are easy to dry and float on the surface of the canvas. After a long time, the material will turn yellow, become brittle, and crack, which will affect the preservation and collection of art works. Contents of the invention [0003] To solve the above-mentioned problems in the prior art, the applicant provides an anti-oxidation and oil-absorbing drawing board. The invention has oxidation resistance, no yellowing and no fading, and the paintings can be preserved for a long time; the surface tension of the drawing board is balanced, has a frosting effect, strong oil absorption, and the paintings dry quickly. [0004] Technical scheme of the present invention is as follows: [0005] An anti-oxidation oil-absorbing drawing board, th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D06M15/693D06M15/01D06M11/79D06M11/76D06M13/224D06M15/333D06M13/252
CPCD06M11/76D06M11/79D06M13/2246D06M13/252D06M15/01D06M15/333D06M15/693
Inventor 陈卫宏陈祎
Owner 沭阳凤凰画材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap