Low cost antibending ceramic roller rod and preparing method thereof

A low-cost technology for ceramic rollers, which can be used in the production of ceramic materials, clay products, and other household appliances. It can solve problems such as bending and deformation, and achieve the effects of improving density, reducing emissions, and optimizing formulas and processes.

Active Publication Date: 2016-04-13
JIN GANG NEW MATERIALS +1
View PDF4 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The technical problem to be solved by the present invention is to provide a low-cost anti-bending ceramic roller, recycle the waste ceramic roller, and solve the problem that the corundum-mullite ceramic roller is easy to break in the quenching zone or the area with a large temperature difference. To solve the problem of bending and deformation, improve the brick running situation of ceramic tiles in roller kiln

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low cost antibending ceramic roller rod and preparing method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0091] Accordingly, such as figure 1 As shown, the present invention also provides a method for preparing a low-cost anti-bending ceramic roller, including:

[0092] S101. Mix the aggregate and matrix material separately according to the formula.

[0093] The raw materials of the ceramic roller include aggregate, matrix material and resin, wherein the main raw material formula of the aggregate in parts by weight is: 30-60 parts of ceramic roller waste;

[0094] The main raw material formula of the base material in parts by weight is:

[0095] 15-40 parts of cordierite

[0096] Alumina 2~15 parts

[0097] Yttrium oxide 0.1~8 parts

[0098] 15~35 parts of clay;

[0099] The above-mentioned cordierite, ceramic roller waste, aluminum oxide, yttrium oxide, and clay total 100 parts by weight, based on this, plus:

[0100] Water-soluble resin, its weight part is 0.1~2 parts.

[0101] Preferably, the weight ratio of the aggregate to the matrix material is 35-50:50-65.

[0102] As a better embodiment ...

Embodiment 1

[0139] (1) Formula:

[0140] 30 pieces of ceramic roller waste

[0141] 30 parts of cordierite

[0142] 10 parts of alumina

[0143] Yttrium oxide 5 parts

[0144] 25 parts of clay;

[0145] 1 part of water-soluble resin.

[0146] Among them, the ceramic roller waste includes: 10 parts of ceramic roller waste with a particle size of 55 mesh, 15 parts of ceramic roller waste with a particle size of 75 mesh, and 5 parts of ceramic roller waste with a particle size of 95 mesh.

[0147] (2) Preparation method:

[0148] (1) Mix 30 parts of ceramic roller waste to obtain aggregate; mix 30 parts of cordierite, 10 parts of alumina, 5 parts of yttrium oxide, and 25 parts of clay to obtain matrix material;

[0149] (2) Ball mill the matrix material and 28 parts of water in a ball mill for 1.5 hours; put the aggregate into the ball milled matrix material, and perform a second ball milling for 0.5 hours to obtain a slurry; Screening and iron removal treatment;

[0150] (3) The slurry is made into a mud ...

Embodiment 2

[0156] (1) Formula:

[0157] 35 pieces of ceramic roller waste

[0158] 25 parts of cordierite

[0159] 8 parts of alumina

[0160] 2 parts of yttrium oxide

[0161] 30 parts of clay;

[0162] 0.2 parts of water-soluble resin.

[0163] Among them, the ceramic roller waste includes: 12 parts of ceramic roller waste with a particle size of 60 mesh, 18 parts of ceramic roller waste with a particle size of 80 mesh, and 5 parts of ceramic roller waste with a particle size of 100 mesh.

[0164] (2) Preparation method:

[0165] (1) Mix 35 parts of ceramic roller waste to obtain aggregate; mix 25 parts of cordierite, 8 parts of alumina, 2 parts of yttrium oxide, and 30 parts of clay to obtain matrix material;

[0166] (2) Ball mill the matrix material and 30 parts of water in a ball mill for 2 hours; put the aggregate into the ball milled matrix material, and perform the second ball milling for 0.6 hours to obtain a slurry; Screening and iron removal treatment;

[0167] (3) The slurry is made into a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a low cost antibending ceramic roller rod, comprising aggregate, a matrix material and resin, wherein the aggregate has a main raw material formula of 30-60 parts of ceramic roller rod waste material in parts by weight, the matrix material has a main raw material formula of 15-40 parts of cordierite, 2-15 pars of aluminium oxide, 0.1-8 parts of yttrium oxide and 15-35 parts of clay in parts by weight; the resin selects water soluble resin in 0.1-2 parts by weight. Correspondingly, the invention further discloses a preparing method of the low cost antibending ceramic roller rod. By adopting the low cost antibending ceramic roller rod and the preparing method thereof, the ceramic roller rod waste material is reused, the problem that a corundum-mullite ceramic roller rod easily generates bending and deforming in a quenching belt or a large temperature difference region, and the condition of sliding of a tile in a roller kiln is improved.

Description

Technical field [0001] The invention relates to the technical field of processing and manufacturing ceramic rollers, in particular to a low-cost anti-bending ceramic roller and a preparation method thereof. Background technique [0002] Roller kilns are widely used in the production of construction, daily-use and sanitary ceramics. Ceramic rollers, as a key component of roller kilns and rolling kilns, play the role of carrying ceramic products and completing the sintering process, directly affecting The development of the ceramic industry. [0003] At present, corundum-mullite ceramic rollers are the most widely used, but in the actual production process, a large amount of corundum-mullite roller waste is often produced. The domestic secondary utilization rate of waste is very low, so the roller waste is generally It is regarded as a non-degradable industrial solid waste pollutant, but also a waste of mineral resources. The widely used corundum-mullite ceramic rollers are mainly ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/132C04B35/10C04B35/622C04B35/634
CPCC04B33/132C04B35/10C04B35/622C04B35/63452C04B35/63476C04B2235/3217C04B2235/3225C04B2235/3481C04B2235/349C04B2235/5436C04B2235/5445C04B2235/96C04B2235/9607Y02P40/60
Inventor 杨华亮方仁德王玉梅郭鹏莉李剑蔺锡柱
Owner JIN GANG NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap