Combustible glue used for destroying unexploded ordnance and preparation method and application thereof

A technology of unexploded ammunition and shellac, which is applied in the field of combustible glue and its preparation, can solve the problems of reduced safety, achieve the effects of slow burning speed, uniform combustion and release of heat, and prevent rapid collapse

Inactive Publication Date: 2016-07-27
PEOPLES LIBERATION ARMY ORDNANCE ENG COLLEGE
View PDF4 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] One of the purposes of the present invention is to provide a combustible glue for destroying unexploded ammunition, so as to solve the problem that additional explosive equivalents are required to detonate and destroy unexploded ammunition, resulting in reduced safety.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Combustible glue used for destroying unexploded ordnance and preparation method and application thereof
  • Combustible glue used for destroying unexploded ordnance and preparation method and application thereof
  • Combustible glue used for destroying unexploded ordnance and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0050] Weigh 21g of Al powder, Fe 3 o 4 Powder 45g, mix the two evenly to get Al / Fe 3 o 4 Mixed powder; weigh 6.5g of shellac, add it to 156mL absolute ethanol, and prepare a shellac absolute ethanol solution with a mass concentration of 5%; weigh Al / Fe 3 o 4 Mix 66g of powder, add it to 132mL of the above-mentioned shellac absolute ethanol solution, and stir until it is uniform to obtain a mixed solution; add 0.66g of glass fiber powder to the above-mentioned mixed solution, and after stirring evenly, add 0.66g of expandable graphite to fully Stir until evenly to obtain combustible glue.

Embodiment 2

[0052] Weigh 8g of Al powder, Fe 3 o 4 Powder 15g, mix the two evenly to get Al / Fe 3 o 4 Mix the powder; weigh 5g of shellac, add it to 100mL of absolute ethanol, and prepare a shellac absolute ethanol solution with a mass concentration of about 6%; weigh Al / Fe 3 o 4 Mix 23g of powder, add it to 69mL of the above-mentioned shellac absolute ethanol solution, stir until it is evenly mixed; Stir until evenly to obtain combustible glue.

Embodiment 3

[0054] Weigh 7g of Al powder, Fe 3 o 4 Powder 15g, mix the two evenly to get Al / Fe 3 o 4 Mixed powder; weigh 5g of shellac, add it to 120mL absolute ethanol, and prepare a shellac absolute ethanol solution with a mass concentration of 5%; weigh Al / Fe 3 o 4 Mix 22g of powder, add it to 44mL of the above-mentioned shellac absolute ethanol solution, stir until it is evenly mixed; Stir until evenly to obtain combustible glue.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides combustible glue used for destroying unexploded ordnance and a preparation method and application thereof. The combustible glue is prepared through the following steps that Al powder and Fe3O4 powder are evenly mixed to obtain Al/ Fe3O4 mixed powder; lac is dissolved in absolute ethyl alcohol to obtain a lac absolute ethyl alcohol solution with the mass concentration being 5%-6%; the Al/ Fe3O4 mixed powder is added into the lac absolute ethyl alcohol solution, and the Al/ Fe3O4 mixed powder and the absolute ethyl alcohol solution are stirred to be evenly mixed; glass fiber powder is added and stirred to be evenly mixed; and expandable graphite is added and stirred to be evenly mixed to obtain the combustible glue. The mass ratio of the Al powder to the Fe3O4 powder is 7-8 to 15. The massic volume ratio of the Al/ Fe3O4 mixed powder to the lac absolute ethyl alcohol solution is 1g to 2-3 mL. The adding amount of the glass fiber powder is 1%-3% of the Al/ Fe3O4 mixed powder by mass. The adding amount of the expandable graphite is 1%-3% of the Al/ Fe3O4 mixed powder by mass. The combustible glue is low in combustion speed, large in combustion heat output and long in combustion duration, and can heat explosives in the unexploded ordnance once being ignited, and it can be ensured that the explosives in the unexploded ordnance are reliably detonated.

Description

technical field [0001] The invention relates to a combustible glue and its preparation method and application, in particular to a combustible glue for destroying unexploded ammunition and its preparation method and application. Background technique [0002] Unexploded ordnance is a problem often encountered in military operations, training, and experiments. The appearance of unexploded ordnance seriously threatens the safety of surrounding personnel, facilities and equipment, and interferes with the normal development of military operations and military training. Measures need to be taken to eliminate it as soon as possible. The existing method of destroying unexploded ordnance is mainly to detonate and destroy. Explosion needs to be bundled in advance, and the detonator is detected. It is necessary for the detonator to touch the unexploded ordnance and place the detonation explosive. The work is cumbersome and dangerous, labor-intensive and low in efficiency. . In addition...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): F42D5/04
CPCF42D5/04
Inventor 甄建伟闫军刘国庆丁玉奎高兴勇张玉令王国栋李金明张倩陈玉丹
Owner PEOPLES LIBERATION ARMY ORDNANCE ENG COLLEGE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap