A kind of self-service peelable armor glue and its application method

A technology of armor gel and armor, which is applied in manicure, medical formula, and cosmetic preparations, etc. It can solve the problems of long time required for manicure, insecure health, and insecure health, etc., to improve nail stratification , good durability and high economic cost

Active Publication Date: 2018-06-12
LES FINS NETWORK TECH
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the problems in the prior art that manicure needs to be done by a professional manicurist and the time required for manicure is long, the cost is high, and the health is not guaranteed. long-term, high cost, and insecure health; personal

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of self-service peelable armor glue and its application method
  • A kind of self-service peelable armor glue and its application method
  • A kind of self-service peelable armor glue and its application method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0074] The components of the armor gel and the parts by weight of each component are: trimethylhexyl dicarbamate diHEMA ester 45; formula I compound 0.01; polymer acrylate oligomer 25; 1-hydroxycyclohexyl benzophenone 2; Phenyl bis(2,4,6-trimethylbenzoyl)phosphine oxide 2; Hydroxyethyl methacrylate 20; Colorant 6. Wherein, the colorant includes one or more of CI 17200 red, CI 15850 red, CI77499 black, CI 77492 yellow, CI 77510 blue, CI 77742 purple, CI 77891 white, and CI 15985:1 yellow. The colorants selected in this embodiment include CI 15850 red and CI 77499 black, the component weight of CI 15850 red accounts for 3% of the total amount of nail polish, and the component weight of CI 77499 black accounts for 3% of the total amount of nail polish. After the above ingredients are mixed, stir at high speed and mix evenly to make armor glue.

[0075] Diamond armor gel, which comprises the following components by weight: 40 parts of polyacrylate-2-crosslinked polymer; 12 parts ...

Embodiment 2

[0082] The components of the armor gel and the parts by weight of each component are: trimethylhexyl dicarbamate diHEMA ester 47; formula I compound 0.02; polymer acrylate oligomer 28; 1-hydroxycyclohexyl benzophenone 3; Phenylbis(2,4,6-trimethylbenzoyl)phosphine oxide 3; hydroxyethyl methacrylate 14; colorant 5. Wherein, the colorant includes one or more of CI 17200 red, CI 15850 red, CI77499 black, CI 77492 yellow, CI 77510 blue, CI 77742 purple, CI 77891 white, and CI 15985:1 yellow. The colorants selected in this embodiment include CI 15850 red and CI 77499 black, the component weight of CI 15850 red accounts for 2.4% of the total amount of nail polish, and the component weight of CI 77499 black accounts for 2.6% of the total amount of nail polish. After the above ingredients are mixed, stir at high speed and mix evenly to make armor glue.

[0083] Diamond armor glue, which comprises the following components by weight: 45 parts of polyacrylate-2-crosslinked polymer; 12 pa...

Embodiment 3

[0090] The components of the armor gel and the parts by weight of each component are: trimethylhexyl dicarbamate diHEMA ester 46; formula I compound 0.03; polymer acrylate oligomer 27; 1-hydroxycyclohexyl benzophenone 3; Phenylbis(2,4,6-trimethylbenzoyl)phosphine oxide 3; hydroxyethyl methacrylate 14; colorant 7. Wherein, the colorant includes one or more of CI 17200 red, CI 15850 red, CI77499 black, CI 77492 yellow, CI 77510 blue, CI 77742 purple, CI 77891 white, and CI 15985:1 yellow. The colorants selected in this embodiment are CI 15850 red and CI 77499 black, the component weight of CI 15850 red accounts for 5.4% of the total amount of nail polish, and the component weight of CI 77499 black accounts for 1.6% of the total amount of nail polish. After the above ingredients are mixed, stir at high speed and mix evenly to make armor glue.

[0091] Diamond armor glue, which comprises the following components by weight: 50 parts of polyacrylate-2-crosslinked polymer; 10 parts ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a self-service strippable nail-protecting glue and a nail beautifying method. The self-service strippable nail-protecting glue comprises, by weight, 40 to 50 parts of trimethylhexyl dicarbamic acid dihydroxyethyl methacrylate, 0.01 to 0.05 part of a compound as shown in a formula I, 20 to 30 parts of polymer acrylate oligomer, 1 to 3 parts of 1-hydroxycyclohexyl phenyl ketone, 1 to 3 parts of phenylbis(2,4,6-trimethylbenzoyl)phosphine oxide, 10 to 20 parts of hydroxyethyl methacrylate and 1 to 7 parts of a coloring agent. The nail-protecting glue can be rapidly cured, has good glossiness and durability and can be integrally and easily removed. The nail-protecting glue has nail nursing effect, exerts strengthening and protection effect on fragile nails and can overall overcome the problems of layer and easy breakage of nails. The self-service nail beautifying method provided by the invention overcomes the problems of long nail-beautifying time and high cost of nail beautifying in a nail beautifying store and the problem that health is not guaranteed in the nail beautifying store; with the method, individual consumers can beautify their nails by themselves; and the method is easy, convenient, rapid and economical.

Description

technical field [0001] The present invention relates to a kind of technical field of cosmetics, more specifically, it relates to a kind of armor gel and the treatment method of manicure with armor gel. Background technique [0002] At present, nail art is a very popular art design, and it has become a way for modern women to add self-glamour. However, traditional manicure techniques are time-consuming, labor-intensive and relatively expensive. Professional manicures generally need to be obtained through the creative labor of professional manicurists, relying on the skills and aesthetics of manicurists. However, with the development of the times, many women who love beauty are more concerned about the speed and personality of manicure updates. The requirements for personalization are getting higher and higher, and they hope to complete the manicure work efficiently, quickly and according to their own personal style. However, it usually takes 120 minutes to make a manicure wi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A61K8/81A61K8/49A61K8/44A61K8/35A61K8/55A61K8/37A61K8/891A61Q3/02C08J3/24C08L33/12C08L71/02
Inventor 赵明
Owner LES FINS NETWORK TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com