Strippable nail-protecting glue for weekly use, and preparation method thereof

An armor and methyl technology, which is applied in the field of peelable armor glue and its preparation, can solve the problems of injury, skin burn, undisclosed health ring protection nail glue, etc., and achieves easy peeling or tearing, Excellent abrasion resistance and fullness, improving the effect of susceptibility to breakage

Active Publication Date: 2016-08-03
LES FINS NETWORK TECH
View PDF10 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the nail polish is very irritating, and it also has a certain burning sensation and injury when it touches the skin.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Strippable nail-protecting glue for weekly use, and preparation method thereof
  • Strippable nail-protecting glue for weekly use, and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0108] The peelable armor glue of Zhouzhuo contains the following components by weight: 11,14-diox-2,9-diazaheptadecane-16-enoic acid-4,4,6,16-tetramethyl 40 parts of -10,15-dioxo-2-[(2-methyl-1-oxo-2-propenyl)oxo] ethyl ester;

[0109] 0.01 part of compound of formula I;

[0110] 28 parts of acrylic oligomer;

[0111] 2.8 parts of 1-hydroxycyclohexyl phenyl ketone;

[0112] (2,4,6-trimethylbenzoyl) 2.6 parts of bisphenyl phosphine oxide;

[0113] 10 parts of hydroxyethyl methacrylate.

[0114] After mixing the above ingredients, stir and mix evenly at high speed to make a peelable and tearable armor glue that is thrown around.

Embodiment 2

[0116] The peelable armor glue of Zhouzhuo contains the following components by weight: 11,14-diox-2,9-diazaheptadecane-16-enoic acid-4,4,6,16-tetramethyl 35 parts of -10,15-dioxo-2-[(2-methyl-1-oxo-2-propenyl)oxo] ethyl ester;

[0117] 0.02 parts of compound of formula I;

[0118] 23 parts of acrylic oligomer;

[0119] 2.2 parts of 1-hydroxycyclohexyl phenyl ketone;

[0120] 2.2 parts of (2,4,6-trimethylbenzoyl) bisphenyl phosphine oxide;

[0121] 14 parts of hydroxyethyl methacrylate.

[0122] After mixing the above ingredients, stir and mix evenly at high speed to make a peelable and tearable armor glue that can be thrown around.

Embodiment 3

[0124] The peelable armor glue of Zhouzhuo contains the following components by weight: 11,14-diox-2,9-diazaheptadecane-16-enoic acid-4,4,6,16-tetramethyl 50 parts of -10,15-dioxo-2-[(2-methyl-1-oxo-2-propenyl)oxo] ethyl ester;

[0125] 0.03 parts of the compound of formula I;

[0126] 30 parts of acrylic oligomer;

[0127] 3.2 parts of 1-hydroxycyclohexyl phenyl ketone;

[0128] (2,4,6-trimethylbenzoyl) bisphenyl phosphine oxide 3.2 parts;

[0129] 9 parts of hydroxyethyl methacrylate.

[0130] After mixing the above ingredients, stir and mix evenly at high speed to make a peelable and tearable armor glue that can be thrown around.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Molecular weightaaaaaaaaaa
Molecular weightaaaaaaaaaa
Molecular weightaaaaaaaaaa
Login to view more

Abstract

The invention relates to a strippable nail-protecting glue for weekly use. The strippable nail-protecting glue comprises, by weight, 35 to 50 parts of 11,14-diox-2,9-diazaheptadecane-16-gadoleic acid-4,4,6,16-tetramethyl-10,15-dioxo-2-[(2-methyl-1-oxo-2-allyl)oxo]ethyl ester, 0.01 to 0.05 part of a compound as shown in a formula I, 23 to 30 parts of acrylate oligomer, 2.2 to 3.2 parts of 1-hydroxycyclohexyl phenyl ketone, 2.2 to 3.2 parts of phenylbis(2,4,6-trimethylbenzoyl)phosphine oxide, 9 to 14 parts of hydroxylethyl methacrylate. The nail-protecting glue provided by the invention can be cured to form a film only through LED light curing for 1 to 2 min, and has a full color and good luster and durability, and the lasting time of the glue reaches one to two weeks; a polish removing solution and wrapping with tinfoil are not needed in removing the nail-protecting glue, and the nail-protecting glue is not removed via a nail-beautifying pusher or abraded via a filling strip; and in removal of the nail-protecting glue, the glue can be integrally and easily stripped, so the glue has nail nursing effect and exerts strengthening and protection effect on fragile nails.

Description

Technical field [0001] The present invention relates to the field of cosmetic synthesis and production, and in particular to a peelable armor glue that can be thrown around and a preparation method thereof. Background technique [0002] Nail glue is a very popular beauty product among women of all ages. Beauty lovers apply it on the nails to make the nails colorful and shiny. At present, there are many brands of armor glue on the market, good and bad. [0003] CN102908266A (2013-2-6) discloses an environmentally friendly nail polish and a preparation method thereof. The environmentally friendly nail polish includes an emulsion, a film-forming agent, an aqueous environmentally friendly color paste and deionized water; wherein the emulsion prepared The body includes butyl acrylate, styrene, methacrylic acid and vinyl hydroxy silicone oil; the initiator is azobisisobutyronitrile. Although the patent claims that its nail polish is environmentally friendly nail polish, it is not the c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): A61K8/891A61K8/81A61K8/86A61K8/49A61K8/73A61K8/55A61K8/37A61Q3/02
Inventor 赵明
Owner LES FINS NETWORK TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap