Metal material and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of metal materials and formulations, applied in the field of materials, can solve the problems that the properties of metal materials cannot meet the actual needs, etc., and achieve the effect of enhancing toughness, improving tensile strength and hardness, and tight texture
Inactive Publication Date: 2016-09-28
WUXI JIABANG ELECTRIC POWER PIPE FACTORY
View PDF3 Cites 3 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
However, the performance of the metal material can not meet the actual needs
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0034] A metal material comprises the following components by weight percentage:
[0037] The preparation method of the metal material is as follows: according to the formula, each component is put into a melting furnace for heating and melting, after melting, pouring is performed at 1570-1600°C, and after cooling to 920-950°C, put it into an incubator and cool to room temperature , and finally tempered at 400 ° C ~ 430 ° C.
Embodiment 2
[0039] A metal material comprises the following components by weight percentage:
[0040] C2.6%, B0.8%, Mn1.2%, Cr23%, Sn2.3%, Al1.5%, Ti0.8%, Bi1.0%, Ce1.5%, Cu1.0%, the rest is Fe .
[0041] The preparation method of the metal material is the same as in Example 1.
Embodiment 3
[0043] C2.1%, B0.5%, Mn0.8%, Cr16%, Sn1.7%, Al1.0%, Ti0.6%, Bi0.5%, Ce1.3%, Cu0.7%, the rest is Fe .
[0044] The preparation method of the metal material is the same as in Example 1.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Login to View More
Abstract
The invention provides a metal material and a preparation method thereof. The metal material comprises the following components by weight percentage: C1.6-2.6%, B0.2-0.8%, Mn0.3-1.2%, Cr12- 23%, Sn0.8‑2.3%, Al0.7‑1.5%, Ti0.1‑0.8%, Bi0.4‑1.0%, Ce1.0‑1.5%, Cu0.2‑1.0%, and the rest is Fe. The metal material has excellent mechanical properties, wear resistance, corrosion resistance, cold resistance, heat resistance and fluidity, its hardness can reach HV670, its strength can reach 635MPa, and it has excellent toughness, plasticity, stiffness and resistance In addition, the metal material has a tight texture and good quality, and can be widely used in the field of metal materials.
Description
technical field [0001] The invention belongs to the technical field of materials, and in particular relates to a metal material and a preparation method thereof. Background technique [0002] Alloy metal materials are more widely used in the current metal materials, and the general metal materials are basically composed of C, B, Fe and other elements. These metal materials can meet general industrial needs, but in some fields that require high performance of metal materials, conventional metal materials are far from meeting the needs. my country's rare earth resources are at the forefront of the world. Due to their unique properties, infiltration of rare earth elements into steel can improve the performance of steel. Therefore, the current research on rare earth elements in the metallurgical industry has begun to be more in-depth. However, rare earth elements are generally expensive, and their addition amount and combination with those components are still a target for furt...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More 
Login to View More